Abstract
Ce- and/or Y-doped zirconia nanopowders having average particle sizes ranging 12–18 nm have been synthesized by a technique based on mechanochemical processing (MCP). Despite their small particle size, the powders had excellent compactibility with green densities exceeding 50% achieved under a moderate uniaxial pressure of 150 MPa. Nearly fully dense ceramics having grain sizes of around 100 nm were successfully produced from these powders by spark plasma sintering (SPS) at temperatures of 1,050–1,150 °C for 5 min under pressures of 50–80 MPa; these temperatures and pressures are considerably lower than those required for achieving near full density with conventional nanopowders. Hardness and fracture-toughness measurements showed that the ceramics prepared by SPS had superior mechanical properties to those prepared by conventional pressureless sintering. It is argued that the high sinterability of the MCP nanopowders is ascribed to their ability to form uniform powder compacts under relatively low pressure, and that that ability in turn originates in two features of the MCP powders: absence of hard agglomeration and pseudo-spherical particle morphology.
Similar content being viewed by others
References
Rhodes WH (1981) J Am Ceram Soc 64:19
Skandan G (1995) NanoStruct Mater 5:111
Sardic V, Winterer M, Hahn H (2000) J Am Ceram Soc 83:729
Gao L, Lia W, Wanga HZ, Zhoub JX, Chaob ZJ, Zaib QZ (2001) J Eur Ceram Soc 83:135
Bravo-Leon A, Morikawa Y, Kawahara M, Mayo MJ (2002) Acta Mater 50:4555
Mayo MJ, Suresh A, Porter WD (2003) Rev Adv Mater Sci 5:100
Muroi M, Trotter G (2006) Ceramic Trans 190:129 [Also in Proceedings of the 6th pacific rim conference on ceramic and glass technology, Maui, Hawaii, September 2005 (in CD-ROM).]
McCormick PG, Ding J, Miao W–F, Street R (2001) US Patent 6203768 B1
McCormick PG, Tsuzuki T (2003) US Patent 6503475
Ding J, Tsuzuki T, McCormick PG, Street R (1996) J Phys D—Appl Phys 29:2365
Ding J, Tsuzuki T, McCormick PG (1996) J Am Ceram Soc 79:2956
Dodd AC, Raviprasad K, McCormick PG (2001) Scripta Mater 44:689
Dodd AC, McCormick PG (2001) Acta Mater 49:4215
Dodd AC, McCormick PG (2002) J Eur Ceram Soc 22:1823
Tsuzuki T, McCormick PG (1997) Appl Phys A 65:607
Liu W, McCormick PG (1999) NanoStruct Mater 12:187
Muroi M, Street R, McCormick PG (2000) J Appl Phys 87:3424
Muroi M, Street R, McCormick PG, Amighian J (2001) Phys Rev B 63:184414
Yoshimura M, Ohji T, Sando M, Niihara K (1988) J Mater Sci Lett 17:1389
Li W, Gao L (2000) J Eur Ceram Soc 20:2441
Chen XJ, Khor KA, Chan SH, Yu LG (2003) Mater Sci Eng A341:43
Anselmi-Tamburini U, Garay JE, Munir ZA, Tacca A, Maglia F, Spinolo G (2004) J Mater Res 19:3255
Anselmi-Tamburini U, Garay JE, Munir ZA (2006) Scripta Mater 54:823
Graeve OA, Singh H, Clifton A (2005) In: Proceedings of the 6th pacific rim conference on ceramic and glass technology, Maui, Hawaii, September 2005 (in CD-ROM)
Amin KE (1991) Toughness, hardness, and wear. In: Schneider SJ (ed) Ceramics and glasses, engineering materials handbook, vol 4. ASM International, Materials Park, p 601
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Muroi, M., Trotter, G., McCormick, P.G. et al. Preparation of nano-grained zirconia ceramics by low-temperature, low-pressure spark plasma sintering. J Mater Sci 43, 6376–6384 (2008). https://doi.org/10.1007/s10853-008-2559-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-008-2559-4