Abstract
The objective of this paper is to prove the possibility to produce single side buffered substrates for coated conductors. We report for the first time the production of highly textured NiW/La2Zr2O7/CeO2 system by all-chemical solution deposition means using an in-house built drop-on-demand ink-jet printer. Lanthanum zirconate precursor ink was produced using lanthanum acetate and zirconium n-propoxide modified with propionic and acetic acid, respectively, and diluted with methanol. Cerium oxide precursor ink was prepared using cerium acetylacetonate dissolved in acetylacetone and diluted in methanol. Optimized ink jet control parameters (inter-droplet distance, nozzle opening time and pressure in the chamber) allowed the deposition of homogeneous highly textured films with a thickness of approximately 150–200 nm at speeds as high as 27 cm/min. La2Zr2O7 film showed in plane and out of plane misalignment of 6.6° and 7.4°, respectively, whereas values obtained for CeO2 were 7.8° and 8.1°, respectively. This study represents a step forward in the production of reel-to-reel coated conductors in an efficient and economic way.
Similar content being viewed by others
References
Kakihana M (1996) J Sol–Gel Sci Technol 6:7
Celik E, Okuyucu H, Mutlu I, Tomsic M, Schwartz J, Hascicek Y (2001) IEEE Trans Appl Supercond 11:3162
Mutlu I, Celik E, Ramazaoglu Y, Akin Y, Hascicek Y (2000) IEEE Trans Appl Supercond 10:1162
Knoth K, Huhne R, Oswald S, Schultz L, Holzapfel B (2005) Supercond Sci Technol 18:334
Sathyamurthy S (2004) J Mater Res 19:2117
Celik E, Akin Y, Sigmund W, Hascicek YS (2004) Mater Sci Eng B 106:182
Chen S, Sun Z, Shi K, Wang S, Meng J, Liu Q, Han Z (2004) Physica C 412–414:871
Morlens S, Ortega L, Rousseau A, Phok S, Deschanvre J, Chaudouet P, Odier P (2003) Mater Sci Eng B 104:185
Chen S, Wang S, Shi K, Liu Q, Han Z (2005) Physica C 419:7
Jackson T, Glowacki BA, Evetts J (1998) Physica C 296:215
Sohma M, Yamaguchi I, Tsukada K, Kondo W, Mizuta S, Manabe TT, Kumagai T (2004) Physica C 412–414:1326
Falter M, HaβLer W, Schlobach B, Holzapfel B (2002) Physica C 372–376:46
Engel S, Knoth K, Huhne R, Schultz L, Holzapfel B (2005) Supercond Sci Technol 18:1385
Knoth K, Schlobach B, Huhne R, Schultz L, Holzapfel B (2005) Physica C 426–431:979
Chen S, Wang SS, Shi S, Liu Q, Han Z (2005) Physica C 419:7
Acknowledgments
Thanks to Eric Robinson, Robert Stearn and Keith Page for their help in building the printer; Domino UK Ltd for donating hardware and Mary Vickers for her valuable discussions. This research was funded by Coated Conductor (COCON) project. T. Mouganie thanks Prima Wood Ltd for funding.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Cordero-Cabrera, M.C., Mouganie, T., Glowacki, B.A. et al. Highly textured La2Zr2O7 and CeO2 buffer layers by ink jet printing for coated conductors. J Mater Sci 42, 7129–7134 (2007). https://doi.org/10.1007/s10853-007-1542-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-007-1542-9