Abstract
The superplastic behavior of cast and hot-extruded NiAl–28Cr–6Mo is observed in the strain rates between \( \dot \varepsilon \) = 1.04 × 10−3 and 5.02 × 10−2 s−1 at 1323–1373 K. The synchronous operation of dislocation glide and dynamic recovery is responsible for the tested alloy to exhibit superplastic behavior.
Similar content being viewed by others
References
Miracle DB (1993) Acta Metall Mater 41:649
Noebe RD, Bowman RR, Nathal MV (1994) NASA technical paper, April:3398
Johnson DR, Chen XF, Oliver BF, Noebe RD, Whittenberger JD (1995) Intermetallics 3:99
Johnson DR, Chen XF, Oliver BF, Noebe RD, Whittenberger JD (1995) Intermetallics 3:493
Sakka Y, Matsumoto T, Suzuki TS, Morita K, Kim B-N, Hiraga K, Moriyoshi Y (2003) Adv Eng Mater 5(3):130
Langdon TG (1999) Mater Trans JIM 40(8):716
Oomori T, Yoneyama T, Oikama H (1988) Trans JIM 29:399
Guha S, Baker I, Munroe PR, Michael JR (1992) Mater Sci Eng A 152:2588
Sherby OD, Wadsorth J (1989) Prog Mater ScI 33:169
Jiang DT, Guo JT, Zhou LZ (1998) Mater Sci Eng 255A:154
Griffiths P, Hammond C (1972) Acta Metall 12:935
Hart EW (1967) Acta Metall 15:351
Jia D (2001) Appl Phys Lett 79:611
Lin D, Hu J, Jiang D (2005) Intermetallics 13:343
Lin TL, Shan AD, Li DQ Scripta Metall Mater 31:1455
Hu J, Lin D (2004) Mater Lett 58:1297
Kim WY, Hanada S (1997) Mater Sci Eng A 248A:78
Acknowledgements
The authors would like to acknowledge the projects (05YB31) supported by the scientific research initial foundation for doctor of Shenyang Institute of Aeronautical Engineering.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Xinghao, D., Baolin, W., Lee, C.J. et al. Superplastic behavior of an extruded eutectic NiAl/Cr(Mo) alloy at intermediate strain rate region. J Mater Sci 42, 6578–6582 (2007). https://doi.org/10.1007/s10853-007-1511-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-007-1511-3