Y2O3 hollow spheres are prepared by coating the anionic poly (styrene-methyl acrylic acid) (PSA-A) latex with an amorphous yttrium layer and subsequent calcining at elevated temperatures in air. The aging temperature, aging time, the concentrations of Y(III) and urea are systematically varied to establish the optimum conditions for the formation of the coating shell. Zeta potential measurement, transmission electron microscopy, scanning electron microscopy, X-ray diffraction and infrared measurements are used to characterize the PSA-A latex, core-shell spheres and Y2O3 hollow spheres. A mechanism for the formation of the PSA-A/yttrium compounds core-shell spheres is suggested. The key factor to prepare smooth-coated spheres is obtained.
Similar content being viewed by others
References
J. K. COCHRAN, Curr. Opin. Solid State Mater. Sci. 3 (1998) 474.
S. EIDEN and G. MARET, J. Coll. Interf. Sci. 2250 (2002) 281.
H. SHIHO and N. KAWAHASHI, J. Colloid Polym. Sci. 278(3) (2000) 270.
H. BAMNOLKER, B. NITZAN, S. GURA and S. MARGEI, J. Mater. Sci. Lett. 16(16) (1997) 1412.
H. SHIHO and N. KAWAHASHI, J. Coll. Interf. Sci. 226 (2000) 91.
C. SONG, G. GU, Y. LIN, H. WANG, Y. GUO, X. FU and Z. HU, J. Mater. Res. Bull. 38 (2003) 917.
C. SONG, D. WANG, G. GU, Y. LIN, J. YANG, L. CHEN, X. FUN and Z. HU, J. coll. Interf. Sci. 272 (2004) 340.
R. A. CARUSO, A. SUSHA and F. CARUSO, J. Chem. Mat. 13(2) (2001) 400.
Y. LU, Y. YIN and Y. XIA, Adv. Mater. 13 (2001) 271.
N. KAWAHASHI and E. MATIJEVIC, J. Coll. Interf. Sci. 138(2) (1990) 534.
Idem.,ibid.143 (1991) 103.
Y. GUO, G. GU, Y. JIAO, F. XUN and Z. HU, J. Poly. Mater. Sci. Engng. (China) 19(4) (2003) 40.
B. AIKEN, W. P. HSU and E. MATIJEVIC, J. Amer. Ceram. Soc. 71 (1987) 845.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Han, C., Wu, X., Lin, Y. et al. Preparation and characterization of Y2O3 hollow spheres. J Mater Sci 41, 3679–3682 (2006). https://doi.org/10.1007/s10853-006-6296-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-6296-2