Abstract
Transparent conducting ZnO:F was deposited as thin films on soda lime glass substrates by atmospheric pressure chemical vapor deposition (CVD) deposition at substrate temperatures of 480–500 °C. The precursors diethylzinc, tetramethylethylenediamine and benzoyl fluoride were dissolved in xylene. The solution was nebulized ultrasonically and then flash vaporized by a carrier gas of nitrogen preheated to 150 °C. Ethanol was vaporized separately, and these vapors were then mixed to form a homogeneous vapor mixture. Good reproducibility was achieved using this new CVD method. Uniform thicknesses were obtained by moving the heated glass substrates through the deposition zone. The best electrical and optical properties were obtained when the precursor solution was aged for more than a week before use. The films were polycrystalline and highly oriented with the c-axis perpendicular to the substrate. The electrical resistivity of the films was as low as 5 × 10−4 Ωcm. The mobility was about 45 cm2/Vs. The electron concentration was up to 3 × 1020/cm3. The optical absorption of the films was about 3–4% at a sheet resistance of 7 Ω/square. The diffuse transmittance was about 10% at a thickness of 650 nm. Amorphous silicon solar cells were deposited using the textured ZnO:F films as the front electrode. The short circuit current was increased over similar cells made with fluorine doped tin oxide, but the voltages and fill factors were reduced. The voltage was restored by overcoating the ZnO:F with a thin layer of SnO2:F.
Similar content being viewed by others
References
Hickernell FS (1976) Proc IEEE 64:631
Dutta S, Jackson HE, Boyd JT, Hickernell FS, Davis RL (1981) Appl Phys Lett 39:206
Igasaki Y, Saito H (1991) J Appl Phys 70:3613
Adachi K, Sato K, Gotoh Y, Nishimura H (1991) Proc of 22nd IEEE PVSC
Shiosaki T, Yamamoto T, Yagi M, Kawabata A (1981) Appl Phys Lett 39:399
Shiosaki T (1978) Proc IEEE Ultrasonics Symp 100
Shiosaki T, Ohnishi S, Kawabata A (1979) J Appl Phys 50:3113
Oda S, Tokunaga H, Kitajima N, Hanna J, Shimizu I, Kokado H (1985) Jap J Appl Phys 24:1607
Smith FTJ (1983) Appl Phys Lett 43:1108
Kim JS, Marzouk HA, Reucroft PJ, Harmin CE (1992) Thin Solid Films 217:133
Shimizu M, Katayama T, Shiosaki T, Kawabata A (1990) J Cryst Growth 101:171
Wieldraaijer W, van Balen Blanken J, Kupiers EW (1993) J Cryst Growth 126:305
Souletie P, Bethke S, Wessels BW, Pan H (1988) J Cryst Growth 86:248
Webb JW, Williams DW, Buchanan M (1981) Appl Phys Lett 39:640
Minami T, Nanto H, Takata S (1982) Appl Phys Lett 41:958
Exarhos GJ, Sharma SK (1995) Thin Solid Films 270:27
Jacobsohn E, Shehtman D (1992) Mat Res Soc Symp Proc 242:779
Brody DE, R Singh, Morgan JH, Lesli JD, Moore CJ, and A Dixon (1980) In: Proceedings of the 12th IEEE Photovoltaic Specialist Conference. IEEE, New York
Kruncks M, Mellikov E (1995) Thin Solid Films 270:33
Major S, Banergee A, Chopra KL (1986) J Mater Res 1:300
Aranovich J, Ortiz A, Bube RH (1979) J Vac Sci Technol 16:9
Hu J, Gordon RG (1991) Solar Cells 30:437
Hu J, Gordon RG (1992) J Appl Phys 71:880
Hu J, Gordon RG (1992) J Electrochem Soc 139:2014
Sato H, Minami T, Miyata T, Ishii M (1994) Thin Solid Films 246:65
Minami T, Sato H, Imamoto H, Takata S (1992) Jpn J Appl Phys 31:L257; Minami T, Sato H, Sonohara H, Takata S, Miyata T, Fukuda I (1994) Thin Solid Films 253:14
Jin ZC, Hamberg I, Granqivst CG (1988) J Appl Phys 64:5117
Aktaruzzman AF, Sharma GL, Malhotra LK (1991) Thin Solid Films 198:67
Nishino J, S Ohshio, Kamata K (1992) J Am Ceram Soc 75:3469
Tominaga K, Kataoka M, Ueda T, Chong M, Shintani Y, Mori I (1994) Thin Solid Films 253:9
Hu J, Gordon RG (1992) J Appl Phys 72:5381
Hirata GA, McKittric J, Cheeks T, Siqueiros JM, Diaz JA, Contreras O, Lopez OA (1996) Thin Solid Films 288:29
Wang R, King LLH, Sleight A (1996) J Mater Res 11:1659
Hu J, Gordon RG (1991) Mat Res Soc Symp Proc 283:891
Olvera ML, Maldonado A, Asomoza R, Konagai M, Asomoza M (1993) Thin Solid Films 229:196
Dana’s System of Mineralogy, 7th Ed I 504
Nuffield EW (1966) X-ray diffraction methods. John Wiley & Sons, New York
Chopra KL, Major S, Pandya DK (1983) Thin Solid Films 102:1
Gordon RG, Proscia J, Ellis FB, Delahoy AE (1989) Solar Energy Mater 18:263
Ahmad Nuruddin, PhD Thesis, University of Illinois, 1997; Ahmad Nuruddin and John Abelson, unpublished results
Acknowledgements
This work was supported by the National Renewable Energy Laboratory. Steven Hegedus (Delaware) and David Carlson (Solarex) deposited and characterized the amorphous silicon solar cells. John Thornton, Keith Kramer, Dan Teff and Nicholas DiCeglie provided assistance in the chemical preparations and analyses. The authors would also like to thank Yuan Z. Lu, David Lange, and John Chervinsky for their assistance in making some of the characterization measurements.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Liang, H., Gordon, R.G. Atmospheric pressure chemical vapor deposition of transparent conducting films of fluorine doped zinc oxide and their application to amorphous silicon solar cells. J Mater Sci 42, 6388–6399 (2007). https://doi.org/10.1007/s10853-006-1255-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-1255-5