Abstract
Nanocrystalline chromium boride (CrB) powders were successfully synthesized at 600 °C through a solid-state reaction. The synthesis was carried out in an autoclave by using CrCl3, Mg and MgB2 as the reactants. The X-ray powder diffraction pattern indicates the formation of orthorhombic CrB. Transmission electron microscopy image shows that typical CrB crystallites are composed of floss-like particles with less than 10 nm in diameter and about 50–100 nm in length. Thermogravimetric analysis revealed that the oxidation resistance for nanocrystalline CrB is much lower than that of bulk CrB.
Similar content being viewed by others
References
Erdemir A, Halter M, Fenske GR (1997) Wear 205:236
Bulfon C, Leithe-Jasper A, Sassik H, Rogl P (1997) J Solid State Chem 133:113
Adams RM (1964) Boron, metallo-boron compounds, and boranes. Interscience, New York, pp 335
Aronsson B, Lundstrom T, Rundqvist S (1965) Borides, silicides, and phosphides: a critical review of their preparation, properties and crystal chemistry. Methuen, London, p 3
Thomson R (1990) In: Freer R (ed) The physics and chemistry of carbides, nitrides and borides, vol 185, Kluwer Academic Pub., Boston, MA, NATO ASI Series E, p113
Gu Y, Yitai Q, Chen L, Zhou F (2003) J Alloy Compd 352:325
Latini A, Pascasio FD, Gozzi D (2002) J Alloy Compd 346:311
Aleshin VG (1979) J Less Common Metals 67:173
Zhou M, Nose M, Makino Y, Nogi K (1999) Thin Solid Films 343–344:234
Matkovich VI (1977) Boron and refractory borides. Springe, New York
Acknowledgements
This work was supported by the Key Project of Science and Technology Research of Education Ministry of China, the Natural Science Foundation of Heilongjiang Province, the Postdoctoral Start-up Found of Heilongjiang Province, the Skeleton Teacher Innovative Ability Project of General high-Level College of Heilongjiang Province, the Science and Research Supported Project of the Oversea Person with Ability, Education Bureau of Heilongjiang Province.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Qin, L., Zhang, X., Liang, Y. et al. Preparation and characterization of nanocrystalline chromium boride. J Mater Sci 41, 7617–7619 (2006). https://doi.org/10.1007/s10853-006-0853-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-0853-6