Abstract
Since their discovery carbon nanotubes (CNT) have attracted much attention due to their singular physical, mechanical and chemical properties. Catalytic chemical vapor deposition (CCVD) of hydrocarbons over metal catalysts is the most promising method for the synthesis of CNT, because of the advantages of low cost and large-scale production and the relatively low temperature used in the process, compared to the other methods (laser ablation and discharge between graphite electrodes). In this study, CNT were synthesized by CCVD using Ni supported on SiO2 as a catalyst. The carbon deposited in the reaction was analyzed by Raman spectroscopy, thermogravimetric analysis (TGA), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The effects of reaction temperature and Ni loading on the carbon nanotube formation were evaluated. The catalyst with 5% Ni favored high yield of CNT at lower temperature, with abundant “multi-walled carbon nanotubes” (MWNTs) at 625 °C, while single-walled carbon nanotubes (SWNTs) and MWNTs were obtained at 650 °C. With an increase in the reaction temperature a marked decrease in the yield of CNT was observed, probably due to the sintering of the catalyst. The catalyst with 1% Ni gave SWNTs with a high degree of order at all reaction temperatures, but in low quantity.
Similar content being viewed by others
References
Iijima S (1991) Nature 354:56
Iijima S, Ichihashi T (1993) Nature 363:603
Guo T, Nikolaev P, Thess A, Colbert DT, Smalley RE (1995) Chem Phys Lett 243:49
Kong J, Cassel AM, Dai H (1998) Chem Phys Lett 292:4
Dai HX, Rinzler P, Nikolacv P, Thess A, Colbert DT, Smalley RE (1996) Chem Phys Lett 260:471
Colomer JF, Bister G, Willems I, Konya Z, Fonseca A, Van Tendeloo G, Nagy JB (1999) Chem Commun 1343
Peigney A, Laurent Ch, Dobigcon F, Roussel A (1997) J Mater Res 12:613
Kong J, Cassel AM, Dai H (1998) Chem Phys Lett 292:567
Hafner JH, Bronikowski MJ, Azamian BR, Nikolaev P, Rinzler AG, Colbert DT, Smith KA, Smalley RE (1998) Chem Phys Lett 296:195
Cassel AM, Kong JA, Dai HJ (1999) Phys Chem B103:6484
Colomer JF, Stephan C, Lefrant S, Van Tendeloo G, Willems I, Kónya Z, Fonseca A, Laurent C, Nagy JB (2000) Chem Phys Lett 317:83
Li Q, Yan H, Zhang J, Liu Z (2004) Carbon 42:829
Shajahan M, Mo YH, Kibria AKMF, Kim MJ, Nahm KS (2004) Carbon 42:2245
Murakami Y, Yamakita S, Okubo T, Maruyama S (2003) Chem Phys Lett 375:393
Javey A, Kim H, Brink M, Wang Q, Ural A, Guo J, Mcintyre P, Mceuen P, Lundstrom M, Dai H (2002) Nat Mater 1:241
Seidel R, Liebau M, Duesberg BS, Kreupl F, Unger E, Graham AP, Hoenlein W, Pompe W (2003) Nanoletters 3:965
Seidel R, Duesberg GS, Unger E, Graham AP, Liebau M, Kreupl F (2004) J Phys Chem B108:1888
Tang S, Zhong Z, Xiong Z, Liu L, Lin J, Shen ZX, Tan KL (2001) Chem Phys Lett 350:19
Kitiyanan B, Alvarez WE, Harwel JH, Resasco DE (2000) Chem Phys Lett 317:497
Pimenta MA, Marucci A, Empedocles S, Bawendi M, Hanlon EB, Rao AM, Eklund PC, Smalley G, Dresselhaus RE, Dresselhaus MS (1998) Phys Rev B58:R16012
Alvarez L, Righi A, Guillard T, Rols S, Anglaret E, Laplaze D, Dauvajol JL (2000) Chem Phys Lett 316:186
Liao H, Hafner JH (2004) J Phys Chem B108:6941
Maruyama S, Kojima R, Miyauchi Y, Chiashi S, Kohno M (2002) Chem Phys Lett 360:229
Méhn D, Fonseca A, Bister G, Nagy JB (2004) Chem Phys Lett 393:378
Acknowledgements
Thanks to CNPq, Prodoc CAPES, Laboratory of Molecular Spectroscopy of Chemistry Institute, São Paulo University for the utilization of Renishaw Raman System 3000.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Noda, L.K., Gonçalves, N.S., Valentini, A. et al. Effect of Ni loading and reaction temperature on the formation of carbon nanotubes from methane catalytic decomposition over Ni/SiO2 . J Mater Sci 42, 914–922 (2007). https://doi.org/10.1007/s10853-006-0009-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-0009-8