Abstract
The growth of decagonal quasicrystals was investigated by the directional solidification of highly undercooled Al72Ni12Co16 melts. The maximum single-grain decagonal quasicrystal contained in the grown crystals was about 0.5 mm in diameter and 6 mm in length. The quality of the grown crystals was examined by the X-ray powder diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscopy (TEM).
Similar content being viewed by others
References
D. SHECHTMAN, I. BLECH, D. GRATIAS and J. W. CAHN, Phys. Rev. Lett. 53 (1984) 1951.
A. P. TSAI, Y. YOKOYAMA, A. INOUE and T. MASUMOTO, Jpn. J. Appl. Phys. 29 (1990) L1161.
Idem., Mater. Trans. JIM. 31 (1990) 98.
Idem., Jpn. J. Appl. Phys. 26 (1987) L1505.
Idem., ibid. 27 (1988) L1587.
A. P. TSAI, A. INOUE and T. MASUMOTO, ibid. 30 (1989) 463.
P. GUYOT, P. KRAMER and M. DE BOISSIEU, Rep. Prog. Phys. 54 (1991) 1371.
D. P. DIVINCENZO and P. J. STEINHARD (eds), in “Quasicrystals: The State of the Art,” (World Scientific, Singapore, 1991).
M. QUILICHINI and T. JANSSEN, Rev. Mod. Phys. 69 (1997) 277.
Y. YOKOYAMA, R. NOTE, S. KIMURA, et al., Mater. Trans. JIM 38 (1997) 943.
T. J. SATO, T. HIRANO and A. P. TSAI, J. Cryst. Growth 191 (1998) 545.
Y. WU, T. J. PICCONE and Y. SHIOHARA, Metall. Trans. 18A (1987) 915.
T. Z. KATTAMIS and M. C. FLEMINGS, A. F. S. Trans. 75 (1967) 191.
J. LI, G. YANG and Y. ZHOU, Mater. Res. Bull. 33 (1998) 141.
A. YAMAMOTO and K. N. ISHIHARA, Acta Crystallor. B49 (1993) 661.
K. CHATTOPADHYAY, et al., Prog. Crystal Growth and Charact. 34 (1997) 237.
Y. C. LIU, X. F. GUO, et al., J. Cryst. Growth 209 (2000) 963.
J. F. LI, Y. L. LU, G. C. YANG, et al., Prog. in Natural Sci. 7 (1997) 736.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Liu, X., Li, J. & Yang, G. Growth of large single-grain decagonal quasicrystal by directional solidification of undercooled Al72Ni12Co16 alloy melt. J Mater Sci 40, 5255–5258 (2005). https://doi.org/10.1007/s10853-005-4420-3
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-4420-3