Abstract
A method for manufacturing of profiled Ni-YSZ anode support sheets by water-based viscous processing has been developed. Mechanical and electrical properties have been studied and were found to correlate with the microstructures and heat treatment. Electrical conductivities in the order of 1000 S/cm were obtained at 1000°C. The results reveal a linear dependence between the conductivity and pre-test reduction temperature: the conductivity increases by a factor of about 6 when reducing the anode support at 1000°C compared to 650°C. Heat treatment after the reduction at low temperature does not improve the conductivity. Insignificant degradation with time was observed at test temperatures between 800 and 1000°C. However, very high electrical loads did lower the conductivity. The developed microstructure withstood two redox cycles without decrease in conductivity. The mechanical strength of components, optimised with respect to both conductivity and strength, showed little change in strength upon reduction, i.e. when changing the structure from NiO/YSZ to Ni/YSZ, revealing that the YSZ matrix governs the mechanical strength.
Similar content being viewed by others
References
N. CHRISTIANSEN, S. KRISTENSEN, H. HOLM-LARSEN, P. H. LARSEN, M. MOGENSEN, P. V. HENDRIKSEN and S. LINDEROTH, Status of SOFC Development at Haldor Topsøe/Risø, Luzern 2002.
P. H. LARSEN, C. BAGGER, S. LINDEROTH, M. MOGENSEN, S. PRIMDAHL, M. J. JøRGENSEN, P. V. HENDRIKSEN, B. KINDL, N. BONANOS, F. W. POULSEN and K. A. MAEGAARD, Status of the Danish SOFC Program,in “Solid Oxide Fuel Cells IV”, edited by S. C. Singhal and M. Dokiya (The Electrochemical Society Proceedings Series, Pennington, NJ 1995) PV 95-1, p. 138.
K. A. NIELSEN, S. LINDEROTH, J. BILDE-SøRENSEN and P. H. LARSEN, in “Test and Performance Analysis of SOFC Stack Units”, Luzern 2002.
M. MOGENSEN, S. SUNDE and S. PRIMDAHL, SOFC anode kinetics, in “Proceedings of the 17th Risø International Symposium on Materials Science: High Temperature Electrochemistry; Ceramics and Metals,” edited by F. W. Poulsen et al. (Risø, Roskilde, Denmark, 1996).
N. Q. MINH, Development of thin-film solid oxide fuel cells for power generation applications, in “Solid Oxide Fuel Cells IV,” edited by S. C. Singhal and M. Dokiya (The Electrochemical Society Proceedings Series, Pennington, NJ 1995) PV 95-1. p. 138.
J. P. ACKERMAN and J. E. YOUNG, Solid Oxide Fuel Cell having Monolithic Core. US Patent No. 4 476 198 (1984).
N. Q. MINH, C. R. HORNE, F. LIU, P. R. STASZAK, P. R. STILLWAGON and J. J. VAN ACKEREN, Forming and processing of monolithic solid oxide fuel cells, in edited by S. C. Singhal, Proc. First Intl. Symp. on Solid Oxide Fuel Cells. (Electrochemical Society, Inc. 1989) p. 307.
N. Q. MINH and R. A. GIBSON, Production of reduced-temperature solid oxide fuel cells by tape calendering, in“Proceedings First European Solid Oxide Fuel Cell Forum,” edited by U. Bossel, (1995) p. 587.
N. Q. MINH, Ceramic fuel cells, J. Am. Ceram. Soc. 76, (1993) 563.
K. KENDALL, E. WRIGHT and A. GOLDS, Co-formed components for solid oxide fuel cells, in “Solid oxide fuel cells (SOFC-IV)”, edited by M. Dokiya, O. Yamamoto, H. Tagawa and S. C. Singhal, (Electrochemical Society, Inc. 1995) p. 229.
T. SHOHO and K. MORINAGA, in Fabrication of electrolyte for SOFC by extrusion, in “Solid oxide fuel cells (SOFC-IV)”, edited by M. Dokiya, O. Yamamoto, H. Tagawa and S. C. Singhal (Electrochemical Society, Inc. 1995) p. 326.
H. ITOH, T. YAMAMOTO, M. MORI, T. HORITA, N. SAKAI, H. YOKOKAWA and M. DOKIYA, Configurational and electrical behaviour of Ni-YSZ cermet with novel microstructure for solid oxide fuel cell anodes. J. Electrochem. Soc. 144(2) (1997) 641.
W. WEIBULL, A Statistical theory of the strength of materials. (Ingeniörsvetenskapsakademiens Handlingar nr. 151), (1931) 1.
J. D. SULLIVAN and P. H. LAUZON, Experimental probability estimators for weibull plots. J. Mater. Sci. Letters 5 (1986) 1245.
L. GRAHL-MADSEN, Oxid baseret konstruktionskeramik: Fremstilling og karakterisering. unpubl. Ph.D. thesis DTU, Denmark, (1988) p. 1.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Grahl-Madsen, L., Larsen, P.H., Bonanos, N. et al. Mechanical strength and electrical conductivity of Ni-YSZ cermets fabricated by viscous processing. J Mater Sci 41, 1097–1107 (2006). https://doi.org/10.1007/s10853-005-3647-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-3647-3