Abstract
In this study, test materials with several different degradation levels were prepared by isothermal aging heat treatment at 630 °C up to 1820 h. Tensile and fracture tests were performed and those were compared with BI tests and DC potential drop method. These results show that normalized Brinell hardness agrees well with normalized tensile strength at the viewpoint of material degradation and the tensile strength and fracture toughness of degraded material can be determined by Brinell hardness or resistivity.
Similar content being viewed by others
References
R. VISWANATHAN and S. GEHL, idid. 113 (1991) 263.
R. VISWANATHAN and S. M. BRUEMMER, J. Eng. Mater. and Tech. (Transactions of the ASME) 107 (1985) 316.
S. H. NHAM and A. K. KIM, Trans. the Korea Soc. Mech. Eng. A 22 (1998) 814.
F. M. HAGGAG and R. K. NANSTAD, The Amer. Soc. of Mech. Eng. PVP. 170 (1989) 41.
F. M. SMITS, The Bell Sys. Tech. J. 37 (1958), 711.
ASTM E 399-90, in Annual Book of ASTM Standard (1995), p. 412.
F. M. HAGGAG and K. L. MURTY, in “Non-destructive Evaluation and Materials Properties III,” edited by P. K. Liaw et al., (Warrendale PA, TMS, 1997), p. 101.
M. D. MATHEW and K. L. MURTY, J. Mater. Sci. 33 (1999) 1497.
ASTM B193-87, in Annual Book of ASTM Standard (1992) p. 308.
ASTM F84-93, in Annual Book of ASTM Standard (1993) p. 135.
J. SHI and Y. SUN, Rev. Sci. Ins. 68 (1997) 1814.
M. YAMASHITA, T. NISHII and H. KURIHARA, Jap. J. Appl. Phy. 35 (1996) 1948.
M. IKEDA, S.-Y. KOMATSU, T. SUGIMOTO and M. HASEGAWA, Mater. Sci. and Eng. A 243 (1998) 140.
A. M. ABDEL-LATIF, S. M. CORBETT and D. M. R. TAPLIN, Metal Sci. 16 (1982) 90.
A. M. ABDEL-LATIF, J. M. CORBETT, D. SIDEY and D. M. R. TAPLIN, in “Advanced in Fracture Research,” Proc. of 5th Int. Conf. on Fracture (ICF5)), 4 (1981) p. 1613.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Seok, CS., Koo, JM. Evaluation of material degradation of 1Cr-1Mo-0.25V steel by ball indentation and resistivity. J Mater Sci 41, 1081–1087 (2006). https://doi.org/10.1007/s10853-005-3644-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-3644-6