Abstract
Alumina and zirconia ceramics joints were made by diffusion bonding through platinum and palladium gaskets in air at temperatures between 1300 and 1550°C. The instrumentation and the procedure for these joints manufacturing are described. The effects of temperature, pressure and exposition time on 3-pt bending strength of resulting joints were established. The maximum bending strength of the samples reached 500 MPa. During thermal resistance testing the samples withstood several hundreds of thermal cycles at temperatures up to 800°C in air.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
M. A. RUBASHEV, G. I. BERDOV, V. N. GAVRILOV, et al., “Heat-Resistant Dielectrics and Their Junctions with Metals in New Engineering” (Atomizdat, Moskow, 1980) p. 246 (Russian).
N. F. KAZAKOV, “Diffusion Bonding of Materials” (Engineering, Moskow, 1976) p. 312 (Russian).
YU. V. NAIDICH, V. A. KONDRATSKY, V. S. ZHURAVLEV, et al., Adhesiya rasplavov i paika materialov 1 (1976) 74 (Russian).
YU. V. NAIDICH, I. I. GAB, V. S. ZHURAVLEV, et al., Avtomaticheskaya svarka 11 (1996) 33 (Russian).
YU. V. NAIDICH, V. S. ZHURAVLEV and N. I. FRUMINA, Adhesiya rasplavov i paika materialov 3 (1978) 99 (Russian).
N. F. GRIGORENKO, A. I. STEGNY, I. E. KASICH-PILIPENKO, et al., in “HTC’94,” edited by N. Eustathopoulos (Institute of Inorganic Chemistry Slovak Academy of Science, Bratislava, 1994) p. 123.
R. V. ALLEN and W. E. BORBIDGE, J. Mater. Sci. 18(9) (1983) 2835.
J. CHRISTENSEN and K. GOTTHJAEIP, DVS-Ber. 148 (1992) 187.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Naidich, Y., Gab, I., Stetsyuk, T. et al. High-strength oxide ceramics joints obtained by diffusion bonding with the use of platinum and palladium gaskets. J Mater Sci 40, 2477–2479 (2005). https://doi.org/10.1007/s10853-005-1978-8
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-1978-8