Active Sites on the Surface of Nano-Sized SiO2–TiO2 Composites
- 48 Downloads
The nature and amount of active sites on the surface of nano-sized SiO2–TiO2 oxides were studied by FTIR spectroscopy and back-titration methods. Increasing the TiO2 content in the SiO2–TiO2 composites increased the amount of activated surface H2O and adsorbed CO2. This increased the amount of active basic centers on the oxide surface and caused the first of two observed mechanisms for benzaldehyde adsorption (with and without its activation) to begin to prevail.
KeywordsSiO2–TiO2 composite nano-sized oxide sol–gel method active site heterogeneous catalysis adsorption back-titration method
Unable to display preview. Download preview PDF.
- 2.V. G. Kharchuk, O. V. Koryakova, E. F. Khmara, and M. A. Uimin, Analitika Kontrol’, 9, No. 4, 423–427 (2005).Google Scholar
- 6.A. N. Murashkevich, O. A. Alisienok, I. M. Zharskiy, and E. K. Yukhno, J. Sol-Gel Sci. Technol., 65, 367–373 (2013).Google Scholar
- 8.GOST 2642.6-97. Refractories and refractory raw materials. Methods for the determination of titanium(IV) oxide.Google Scholar
- 9.GOST 18307. Soot white. Specifi cations.Google Scholar
- 10.V. N. Borodin, Zh. Fiz. Khim., 51, 928–929 (1977).Google Scholar
- 11.A. B. Shishmakov, Yu. V. Mikushina, O. V. Koryakova, V. V. Matskevich, N. A. Zhuravlev, V. G. Kharchuk, and L. A. Petrov, Zh. Neorg. Khim., 53, No. 10, 1667–1672 (2008).Google Scholar
- 12.L. J. Bellamy, The Infra-Red Spectra of Complex Molecules, 2nd edn., Methuen & Co., London (1958).Google Scholar