Abstract
Single-crystalline indium oxide (In2O3) nanocubes were successfully prepared via dehydration of indium hydroxide (In(OH)3) nanocubes synthesized by a hydrothermal method. In situ x-ray diffraction patterns of the phase transition were obtained. Transmission electron microscopy indicated that the morphology of the In2O3 nanocrystallites was the same as that of their precursors, In(OH)3 nanocrystallites. The reported method, the dehydration of In(OH)3 nanocrystallites prepared by a hydrothermal method, shows a simple and effective synthesis route for In2O3 nanostructured materials.
Similar content being viewed by others
REFERENCES
Hamberg, I. and Granqvist, C.G., J. Appl. Phys., 1986, vol. 60, p. R123.
Granqvist, C.G., Appl. Phys. A, 1993, vol. 57, p. 19.
Shinri Sato, J. Photochem. Photobiol., A, 1988, vol. 45, p. 361.
Liess, M., Thin Solid Films, 2002, vol. 410, p. 183.
Chung, W., Sakai, G., Shimanoe, K., et al., Sens. Actuators, B, 1998, vol. 46, p. 139.
Tamaki, J., Naruo, C., Yamamoto, Y., and Matsuoka, M., Sens. Actuators, B, 2002, vol. 83, p. 190.
Takada, T., Tanjou, H., Satio, T., and Harrada, K., Sens. Actuators, B, 1995, vol. 24/25, p. 548.
Gurlo, A., Ivanovskaya, M., Barsan, N., et al., Sens. Actuators, B, 1997, vol. 44, p. 327.
Li, C., Zhang, D.H., Han, S., et al., Adv. Mater., 2003, vol. 15, p. 143.
Liang, C.H., Meng, G.W., Lei, Y., et al., Adv. Mater., 2001, vol. 13, p. 1330.
Yubao Li, Yoshio Bando, and Golberg, D., Adv. Mater., 2003, vol. 15, p. 581.
Peng, X., Meng, G., Zhang, J., et al., J. Mater. Chem., 2002, vol. 12, p. 1602.
Poznyak, S.K., Golubev, A.N., and Kulak, A.I., Surf. Sci., 2000, vols. 454–456, p. 396.
Poznyak, S.K. and Kulak, A.I., Electrochim. Acta, 2000, vol. 45, p. 1595.
Zheng, M.J., Zhang, L.D., Li, G.H., et al., Appl. Phys. Lett., 2001, vol. 79, p. 839.
Zhou, H., Cai, W., and Zhang, L., Mater. Res. Bull., 1999, vol. 34, p. 845.
Won Seok Seo, Hyong Hoon Jo, Kwangyeol Lee, and Park, J.T., Adv. Mater., 2003, vol. 15, p. 795.
Yang, H., Tang, A.D., Zhang, X.C., et al., Scr. Mater., 2004, vol. 50, p. 413.
Ryzhikov, A.S., Vasiliev, R.B., Rumyantsevaa, M.N., et al., Mater. Sci. Eng., B, 2002, vol. 96, p. 268.
Zhu, H., Yao, K., Wo, Y., and Wang, N., Semicond. Sci. Technol., 2004, vol. 19, p. 1020.
Zhu, H., Wang, Y., Wang, N., et al., Mater. Lett., 2004, vol. 58, p. 2631.
Wang, L., Perez-Maqueda, L.A., and Matijevie, E., Colloid Polym. Sci., 1998, vol. 276, p. 847.
Zhang, X., Xie, S., Ni, Z., et al., Inorg. Chem. Commun., 2003, vol. 6, p. 1445.
Roy, R. and Shafer, M.W., J. Phys. Chem., 1954, vol. 58, p. 372.
Author information
Authors and Affiliations
Additional information
__________
From Neorganicheskie Materialy, Vol. 41, No. 6, 2005, pp. 702–705.
Original English Text Copyright © 2005 by Hongliang Zhu, Naiyan Wang, Lina Wang, Kuihong Yao, Xiaofei Shen.
This article was submitted by the authors in English.
Rights and permissions
About this article
Cite this article
Zhu, H., Wang, N., Wang, L. et al. In Situ X-ray Diffraction Study of the Phase Transition of Nanocrystalline In(OH)3 to In2O3 . Inorg Mater 41, 609–612 (2005). https://doi.org/10.1007/s10789-005-0178-x
Received:
Issue Date:
DOI: https://doi.org/10.1007/s10789-005-0178-x