Favourable experience is summarized for manufacturing, welding, storage, and operation of superheaters made of heat-resistant chromium-manganese steel DI59, and a mechanism is described for overall corrosion breakdown and oxidation over pipe metal grain boundaries under action of active components fuel combustion products of V2O5 and sulfur compounds.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
E. V. Kuznetsov, A. I. Maksimov, L. A. Chechel’, and A V. Ryabchenkov, “High-temperature corrosion processes for steels in sulfur-containing fuel combustion products and intentional creation of heat-resistance materials,” Trudy TsNIITMASh, No. 207 (1988).
L. A. Chechel’, E. V. Kuznetsov, A. S. Orlov, and B. É. Shkol’-nikova, “Heat resistance and high-temperature strength of chromium-manganese steel DI59,” Vestn. MGTU im. G. I. Nosova, No. 4 (2008).
V. F. Rezinskikh, B. É, Shkol’nikova, and G. A. Urusova, “Prospective steels for SKD boiler superheaters,” Teplotekhnika, No. 10 (2000).
TU 14-1-2870–80. Tube workpiece of corrosion-resistant steels grades 12Kh13G12AS2N2 (DI50) and 10Kh13G12BS2N2D2 (DI59) [in Russian].
TU 14-131-871–93. Tube workpiece of corrosion-resistant steel grade 10Kh13G12BS2N2D2-Sh (DI59-Sh) [in Russian].
TU 14-3-917–80. Tubes of cold-worked heat-resistant steels grades 12Kh13G12AS2N2 (DI50) and 10Kh13G12BS2N2D2 (DI59) [in Russian].
TU 14-3P-55–2001. Jointless steel tubes for steam boilers and pipelines [in Russian].
GSSSD 116–88. Corrosion-resistant steel 0Kh13G12S2N2D2D (DI59). Nominal stress-rupture strength at 500 – 650°C [in Russian].
B. É. Shkol’nikova and I. Sh. Zagretdinov, “Experience and operating prospects of using tubes of chromium-manganese steel for thermal power station boiler superheaters,” Nov. Ross. Élektroenerget., No. 12 (2006).
V. A. Bogachev, A. N. Samodurov, and A. V. Tarzanov, “Disruption of stability and damage of platen superheater coils,” Teploénergetika, No. 2 (2008).
V. A. Bogachev, T. P.. Pshechenkova, and B. É. Shkol’nikova, “Reason for damage of superheater tubes of steel DI59 of the TPE-216m boiler of the Kharanor state regional power station,” Élektr. Stantsii, No. 5 (2013).
V. A. Bogachev, G. A. Urasova, and M. A. Shumovskaya, “Study of stress-rupture strength of steel grade DI 59 boiler superheaters type TPE-216M of the Kharanor state regional power station,” Élektr. Stantsii, No. 19 (2014)
V. A. Bogachev, V. V. Svetushkov, Yu. G. Potapovich, G. A. Urasova, and M. A. Shumovskaya, “Method for determining the residual life of steel grade DI59 superheaters,” Élektr. Stantsii, No. 5 (2015).
V. A. Bogachev, G. A. Urusova, and M. A. Shumovskaya, “Development of dependences for determining the equivalent operating temperature for DI59 grade steel superheaters,” Élektr. Stantsii, No. 3 (2015).
A. S. Orlov and N. S. Ershov, Recommendations “Anticorrosion protection of internal and outer surfaces of objects of pipe steel DI59 for specifications of RF standards during transportation and storage” [in Russian], JSC NPO TsNIITMASh, Moscow (2014).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Élektricheskie Stantsii, No. 3, March 2018, pp. 53 – 56.
Rights and permissions
About this article
Cite this article
Ershov, N.S., Orlov, A.S. & Gavrilov, E.V. Experience of Using Steel DI59 for Manufacturing Boiler Superheaters. Power Technol Eng 52, 342–344 (2018). https://doi.org/10.1007/s10749-018-0956-7
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10749-018-0956-7