Methods of Synthesizing Alumomagnesium Spinel Powders for Obtaining Transparent Ceramic (Review)

  • Published:
Glass and Ceramics Aims and scope Submit manuscript

The prospects for using optically transparent ceramic made from alumomagnesium spinel are examined. The technologies for synthesizing spinel powders for subsequent use in obtaining transparent ceramic are described.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1.
Fig. 2.
Fig. 3.

Similar content being viewed by others

References

  1. I. F. Kobylkin and V. V. Selivanov, Materials and Structures of Lightweight Armor, MGTU im. N. É. Baumana, Moscow (2014).

  2. G. M. Saibotalov and M. E. Baranov, “Use of armor ceramic for protection of the units of missile complexes,” in: Reshetnev Lectures: Proc. 18th International Scientific Conference Dedicated to the 90th Birthday Anniversary of General Designer of Rocket and Space Systems Academician M. F. Reshetnev [in Russian], Siberian State Aerospace University, Krasnoyarsk (2014), Part 1, pp. 333 – 335.

  3. V. V. Sharypin and S. K. Evstrop’ev, “Enhancement of the optical transparency of the MgAl2O4 with the use of two-step uniaxial pressing,” Opt. Zh., 83(3), 60 – 65 (2016).

    Google Scholar 

  4. E. S. Lukin, N. A. Popov, V. S. Glazachev, et al., “Technology, properties, and applications of optically transparent oxide ceramic: prospects for development,” Konstr. Kompozit. Mater., No. 3, 24 – 36 (2015).

  5. E. V. Gol’eva, M. D. Mikhailov, A. A. Dunaev, and B. A. Ignatenkov, “Effect of synthesis regimes and the structure of the initial nanocrystalline powders on the optical properties of transparent ceramics MgAl2O4,” Opt. zh., 83(2), 67 – 72 (2016).

    Google Scholar 

  6. D. Mamonova, Synthesis and Study of the Properties of Nanoparticles of Complex Oxides for the Example of Yttrium Aluminum Garnet and Bismuth Ferrite, Author’s Abstract of Candidate’s Thesis [in Russian], St. Petersburg State University, St. Petersburg (2015).

  7. E. S. Lukin, Theoretical Principles of the Production and Technology of Optically Transparent Ceramics [in Russian], MKhTI im. D. I. Mendeleev, Moscow (1982).

  8. A. Geras’kin, Synthesis and Properties of Mg(Fe0.8Ga0.2)2O4–𝛿 on Si Substrates with Thermally Stable Interphase Boundaries, Author’s Abstract of Candidate’s Thesis [in Russian], IONKh im. N. S. Kurnakova RAN, Moscow (2014).

  9. M. K. Alekseev, G. I. Kulikova, M. Yu. Rusin, et al., “Transparent ceramic obtained by spark plasma sintering from ultrapure alumomagnesium spinel nanopowders,” Neorg. Mater., 52(3), 367 – 373 (2016).

    Article  Google Scholar 

  10. S. S. Balabanov, V. E. Vaganov, E. M. Gavrishchuk, et al., “Effect of the conditions of hydrolysis of magnesium-aluminum isopropylate on the properties of alumomagnesium spinel powders,” Neorg. Mater., 50(8), 895 – 901 (2014).

  11. D. V. Tolstikova, E. V. Gol’eva, V. S. Lebanin, et al., “Synthesis and study of nanocrystalline powders for optical ceramics made from alumomagnesium spinel,” Opt. Zh., 81(12), 69 – 73 (2014).

    Google Scholar 

  12. A. V. Novikov, “Production of MgAl2O4 nanopowders by hydrolysis of double aluminum-magnesium alkoxide,” in: 15th All-Russia Youth Scientific Conf. with Elements of the Scientific School ‘Functional Materials: Properties and Applications’: Collection of Abstracts [in Russian], Lema, St. Petersburg (2014), pp. 191 – 192.

  13. G. I. Belykh, V. T. Gritsyna, and L. V. Udalov, “Structural and mechanical properties of optical ceramics made from magnesium-aluminum spinel,” Vopr. At. Nauki Tekh., No. 3, 101 – 107 (2004).

  14. D. A. Martyukhova, V. Skroznikova, and N. V. Popovich, “Effect of the sol-gel synthesis regime on the properties of coatings for float glass,” in: Proc. 10th Intern. Congress of Young Scientists in Chemistry and Chemical Technology (Moscow, 28 – 31 October 2014) [in Russian], Moscow (2014), pp. 65 – 67.

  15. P. P. Faikov, Synthesis and Sinterability of Powders Obtained in the MgO–Al2O3 System by the Sol-Gel Method, Author’s Abstract of Candidate’s Thesis [in Russian], RKhTU im. D. I. Mendeleeva, Moscow (2007).

  16. I. D. Borshchishin, I. V. Lutsyuk, Ya. I. Vahhula, and V. V. Kochubei, “Synthesis of alumomagnesium highly dispersed spinel by the citrate-gel method,” Ogneup. Tekh. Keram., No. 10, 32 – 34 (2009).

  17. L. V. Morozova, M. V. Kalinina, I. A. Drozdova, et al, “Synthesis and study of spinel-class nanoceramics,” Fiz. Khim. Stekla, 21(6), 879 – 886 (2014).

    Google Scholar 

  18. S. V. Kuznetsov, P. P. Fedorov, V. V. Voronov, and V. V. Osiko, “Synthesis of MgAl2O4 nanopowders,” Neorg. Mater., 47(8), 988 – 991 (2011).

    Article  Google Scholar 

  19. V. A. Sokol, D. A. Rokhlenko, L. I. Konovalov, and A. V. Bromberg, “Alumomagnesium spinel for transparent ceramic,” Neorg. Mater., 17(5), 896 – 901 (1981).

    Google Scholar 

  20. E. G. Ledovskaya, S. V. Gabelkov, L. M. Litvinenko, et al., “Low-temperature synthesis of magnesium-aluminum spinel,” Vopr. At. Nauki Tekh., No. 1, 160 – 163 (2006).

  21. S. V. Gabelkov, R. V. Tarasov, N. A. Poltavtsev, et al., “Phase transformation in low-temperature synthesis of MgAl2O4,”Neorg. Mater., No. 4, 462 – 470 (2007).

  22. Ji-Guang Li, Takayasu Ikegami, Jong-Heun Lee, and Toshiyuki Mori, “Fabrication of Translucent Magnesium Aluminum Spinel Ceramics,” J. Am. Ceram. Soc., 83, 2866 – 2868 (2000).

    Article  Google Scholar 

  23. K. Nikoofar, M. Haghighi, and Z. Khademi, “Preparation, characterization, and catalytic application of metallic nanocrystalline MgAl2O4 in the synthesis of 3-hydroxy-3-indolyl-indolin-2-ones, symmetrical and unsymmetrical 3,30-bis(indolyl) indolin-2-ones, and 3,30-bis(indolyl)methanes,” Arabian J. Chem.; URL: http://www.sciencedirect.com/science/article/pii/S1878535216000241 (query date: May 16, 2016).

  24. Shuvendu Tripathy, Deepash Shekhar Saini, and Debasis Bhattacharya, “Synthesis and fabrication of MgAl2O4 ceramic foam via a simple, low-cost and eco-friendly method,” J. Asian Ceram. Soc., Vol. 4, 149 – 154 (2016).

  25. G. G. Galimov, A. Yu. Sidorov, and A. A. Nikiforov, “Investigation of the effect of the difference of the decomposition temperatures of the initial compounds to magnesium and aluminum oxides on the rate of the spinel formation reaction,” Ogneup. Tekh. Keram., No. 9, 21 – 26 (2014).

  26. P. V. Kovtunenko, “Effect of gamma nonstoichiometry on spinel inversion,” Steklo Keram., No. 8, 242 – 246 (1997); P. V. Kovtunenko, “Effect of gamma nonstoichiometry on spinel inversion,” Glass Ceram., 54(7 – 8), 242 – 246 (1997).

  27. G. A. Vydrik, T. B. Solov’eva, and F. Ya. Kharitonov, Transparent Ceramics [in Russian], Énergiya, Moscow (1980).

  28. S. K. Eevstrop’ev, V. V. Sharypina, A. N. Smirnov, et al., “Batches for the manufacture of alumomagnesium spinel ceramics,” in: Proc. 10th Intern. Conf. on Applied Optics 2012 [in Russian], S. I. Vavilov State Optical Institute, St. Petersburg (2012), pp. 235 – 237.

  29. O. L. Belousov, A. I. Domanskii, V. L. Ugolkov, and L. F. Dikin, “Influence of yttrium oxide on the phase formation and sintering of ceramics based on spinel MgAl2O4,” Fiz. Khim. Stekla, 34(4), 616 – 621 (2008).

    Google Scholar 

  30. S. F. Wang, J. Zhang, D. W. Luo, et al., “Transparent ceramics: Processing, materials and applications,” in: Progress in Solid State Chemistry, 41, 20 – 54 (2013).

  31. Tsukuma Koji, “Transparent MgAl2O4 spinel ceramics produced by HIP post-sintering,” J. Soc. Japan, 114, 802 – 806 (2006).

    Google Scholar 

  32. S. K. Evstrop’ev, A. N. Smirnov, and V. V. Sharypin, “Nanosize sintering additive based on B2O3 for obtaining ceramic from aluminum-magnesium spinel,” Steklo Keram., No. 7, 16 – 20 (2014); S. K. Evstrop’ev, A. N. Smirnov, and V. V. Sharypin, “Nanosize sintering additive based on B2O3 for obtaining ceramic from aluminum-magnesium spinel,” Glass Ceram., 71(7 – 8), 236 – 239 (2014).

  33. A. D. Gledhill, D. Li, T. Mroz, et al., “Strengthening of transparent Spinel/Si3N4 nanocomposites,” Acta Mater., 60, 1570 – 1575 (2012).

    Article  Google Scholar 

  34. A. A. Kachaev, D. V. Grashchenkov, Yu. E. Lebedeva, et al., “Optically transparent ceramic (Review),” Steklo Keram., No. 4, 3 – 10 (2016); A. A. Kachaev, D. V. Grashchenkov, Yu. E. Lebedeva, et al., “Optically transparent ceramic (Review),” Glass Ceram., 73(3 – 4), 117 – 123 (2016).

Download references

This research was supported by a grant from the Russian Science Foundation (contract No. 14-29-00194) at the Mendeleev Russian University of Chemical Technology.

Author information

Authors and Affiliations

  1. D. I. Mendeleev Russian Chemical Technology University, Moscow, Russia

    M. O. Senina, D. O. Lemeshev & V. A. Kolesnikov

Authors
  1. M. O. Senina
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. D. O. Lemeshev
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. V. A. Kolesnikov
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to D. O. Lemeshev.

Additional information

Translated from Steklo i Keramika, No. 10, pp. 19 – 25, October, 2017.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Senina, M.O., Lemeshev, D.O. & Kolesnikov, V.A. Methods of Synthesizing Alumomagnesium Spinel Powders for Obtaining Transparent Ceramic (Review). Glass Ceram 74, 358–363 (2018). https://doi.org/10.1007/s10717-018-9994-8

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10717-018-9994-8

Key words

Search

Navigation