It is shown that zirconium-free frit should be used to obtain semi-fritted durable glass-crystal coatings, thereby decreasing the total fuel-energy consumption on the production of floor tiles by lowering the synthesis temperature of the frit by 80 – 100°C and decreasing the amount of frit in the raw material mix to 20 – 22.5%.
Similar content being viewed by others
References
Z. A. Nosova, Zirconium Glazes [in Russian], Stroiizdat, Moscow (1973).
O. S. Grum-Grzhimailo, Light-Scattering Glass-Crystal Glazes for Rapidly Sintering Building Ceramic, Author’s Abstract of Doctoral Thesis [in Russian], D. I. Mendeleev Moscow Chemical Technology Institute, Moscow (1988).
Yu. G. Steinberg, Glassy Coatings for Ceramics [in Russian], Stroiizdat, Leningrad (1989).
A. M. Kalinina, I. Ya. Tugucheva, and V. N. Filipovich, “Dependence of the crystallization kinetic of ZrSiO4 on the particlesize in the initial glass of the zirconium glaze,” Fiz. Khim. Stekla, 7(3), 306 – 31 (1981).
I. A. Levitskii, S. E. Barantseva, and N. V. Mazura, “Particulars of structure and phase formation in zirconium-containing frits and glazes,” Steklo Keram., No. 7, 25 – 28 (2009).
I. A. Levitskii, et al., “Processes resulting in the formation of semi-fritted durable zirconium-containing coatings of ceramic floor tiles,” in: Coll. Works of BGTU. Ser. III, Applied Chemistry of Inorganic Matters [in Russian], Minsk (2009), Issue XVII, pp. 34 – 39.
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Steklo i Keramika, No. 9, pp. 29 – 32, September, 2010.
Rights and permissions
About this article
Cite this article
Levitskii, I.A., Barantseva, S.E., Lugin, V.G. et al. Optimization of the composition of the fritted component of the raw material mix of durable coatings. Glass Ceram 67, 291–294 (2011). https://doi.org/10.1007/s10717-011-9282-3
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10717-011-9282-3