Abstract
The results of a study of silicon nitride phase formation in combustion of ferrosilicon in gaseous nitrogen are reported. It was shown that formation of α-or β-modifications of silicon nitride is basically determined by the composition of the batch for self-propagating high-temperature synthesis. When ammonium chloride was added to the initial ferrosilicon, a combustion product with a high (up to 80%) α-Si3N4 content is formed, while dilution with the final product and magnesium fluoride results in predominant (more than 95%) formation of β-Si3N4. The particle size and shape are a function of the conditions of synthesis and are primarily determined by the temperature and the additives incorporated in the initial alloy.
Similar content being viewed by others
References
A. S. Mukas’yan, V. M. Martynenko, A. G. Merzhanov, et al., “Mechanism and characteristics of combustion of silicon in nitrogen,” Fiz. Goreniya Vzryva, No. 5, 43–49 (1986).
A. S. Mukas’yan, B. V. Stepanov, Yu. A. Gal’chenko, and I. P. Borovinskaya, “Mechanism of structure formation of silicon nitride in combustion of silicon in nitrogen,” Fiz. Goreniya Vzryva, No. 1, 45–52 (1990).
L. N. Chukhlomina, Yu. F. Ivanov, Yu. M. Maksimov, et al., “Production of submicron silicon nitride powders by self-propagating high-temperature synthesis,” Neorg. Mater., 41(12), 1294–1300 (2005).
P.-O. Käll, “Quantitative phase analysis of Si3N4-based materials,” Chem. Scr., 28, 439–446 (1988).
P. V. Pavlov and N. V. Belov, “Mechanism of the transition of α-into β-Si3N4 in annealing,” Dokl. Akad. Nauk SSSR, 241(4), 825–827 (1978).
L. N. Chukhlomina, “Mechanism of silicon nitride crystal growth in combustion of ferrosilicon in nitrogen,” in: Fundamental and Applied Problems in Modern Mechanics: Proceedings of the V All-Russian Scientific Conference [in Russian], Tomsk (2006), pp. 30–31.
B. G. Trusov, Modeling of Chemical and Phase Equilibria at High Temperatures, ASTRA-4: Instructions for Users [in Russian], Moscow (1991).
V. V. Zakorzhevskii and I. P. Borovinskaya, “Some regularities of α-Si3N4 synthesis in a commercial SHS reactor,” Int. J. SHS, 9(2), 171–191 (2000).
Author information
Authors and Affiliations
Additional information
__________
Translated from Steklo i Keramika, No. 2, pp. 28–30, February, 2007.
Rights and permissions
About this article
Cite this article
Chukhlomina, L.N., Maksimov, Y.M., Vitushkina, O.G. et al. Phase composition and morphology of products of combustion of ferrosilicon in nitrogen. Glass Ceram 64, 63–65 (2007). https://doi.org/10.1007/s10717-007-0015-6
Issue Date:
DOI: https://doi.org/10.1007/s10717-007-0015-6