Abstract
Precipitates that form as a result of phase transformation are studied with regard to mechanical behaviour and initiation of internal cracks. The focus is on precipitates occupying a larger volume than the surrounding matrix. Further the study is restricted to precipitates growing by incorporating material transformed from being matrix material to the phase of the precipitate. The phase transformation is here treated as a simple homogeneous swelling. The classical solutions for expanding inclusions predict that the inclusion becomes subjected to a constant homogeneous hydrostatic compression. During the process analysed here, added transformed material progressively relieve the compressive stress in the interior of the precipitate. As the process continues the stresses change from compression to tension in both radial and tangential directions in the centre of the precipitate. Further, growth of cracks in precipitates with poor fracture mechanical properties are studied. To simplify the analysis it is assumed that the fracture toughness is insignificant. The prediction is that around a third of the precipitate will fracture. The presence of a crack only has an insignificant effect on the load exerted by the swelling precipitate on the matrix.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
ABAQUS: (2007) User’s manual. HKS, Providence
Eshelby JD (1957) The determination of the elastic field of an ellipsoidal inclusion, and related problems. Proc R Soc Lond Ser A Math Phys Sci 241: 376–396
Grange M, Besson J, Andrieu E (2000) An anisotropic Gurson type model to represent the ductile rupture of hydrided Zircaloy-4 sheets. Int J Fract 105: 273–293
Hill R, Lee EH, Tupper SJ (1947) The theory of combined plastic and elastic deformation with particular reference to a thick tube under internal pressure. Proc R Soc Lond Ser A Math Phys Sci 191(1026): 278–303
Hill R (1950) The mathematical theory of plasticity. Clarendon Press, Oxford
Leitch BW, Puls MP (1992) Finite element calculation of the accommodation energy of a misfitting precipitate in an elastic-plastic matrix. Metall Trans 23A: 797
Leitch BW, Shi S-Q (1996) Accommodation energy of formation and dissolution for a misfitting precipitate in an elastic-plastic matrix. Model Simul Mater Sci Eng 4: 281–292
Matvienko YG (2004) The cohesive zone model in a problem of delayed hydride cracking of zirconium alloys. Int J Fract 128: 73–79
Puls MP (1984) Hydrogen-induced cracking: 2 effect of stress on nucleation, growth and coarsening of Zirconium hydride precipitates. Atomic Energy of Canada Ltd. Report No AECL-8381
Puls MP (1990) Effect of crack tip stress states and hydride matrix interaction stresses on delayed hydride cracking. Metall Trans A, 21A
Shi S-Q (1999) Diffusion-controlled hydride growth near crack tip in zirconium under temperature transients. J Nucl Mater 275: 318–323
Simpson LA, Cann CD (1979) Fracture toughness of zirconium hydride and its influence on the crack resistance of Zirconium alloys. J Nucl Mater 87: 303–316
Singh RN, Ståhle P (2006) Fracture of Zr-alloy pressure tubes due to hydride blister formation. In: Presented at 19th Nordic seminar in computational mechanics—NSCM19 hosted by Lund University, Faculty of Engineering on 20–21 Oct 2006, Lund, Sweden
Singh RN, Ståhle P, Banks-Sills L, Ristmanaa M, Banerjee S (2008a) δ-hydride habit plane determination in α-Zirconium at 298 K by strain energy minimization technique. Defect Diffus Forum 279: 105–110
Singh, RN, Ståhle P, Sairam K, Chakravartty JK, Kashyap BP (2008b) Stress-field Computation for hydride blister forming in Zr-alloys. Water reactor fuel performance meeting—WRFPM2008 Seoul, South Korea 19–23 Oct 2008, paper No 8137
Singh RN, Kishore R, Singh SS et al (2004) Stress-reorientation of hydrides and hydride embrittlement of Zr–2.5 wt% Nb pressure tube alloy. J Nucl Mater 325: 26–33
Singh RN (2009) Private communication
Taylor GI (1948) The formation and enlargement of a circular hole in a thin plastic sheet. Q J Mech Appl Math 1: 103–124
Acknowledgments
Financial support from Bahbah Atomic Research Centre, Mumbai, India and the European commission under the Marie Curie fellowship programme for Dr. R.N. Singh are gratefully acknowledged. A code for generation of suitable indata to ABAQUS was provided by Mr. N. Lalanne-Aulet.
Open Access
This article is distributed under the terms of the Creative Commons Attribution Noncommercial License which permits any noncommercial use, distribution, and reproduction in any medium, provided the original author(s) and source are credited.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This is an open access article distributed under the terms of the Creative Commons Attribution Noncommercial License (https://creativecommons.org/licenses/by-nc/2.0), which permits any noncommercial use, distribution, and reproduction in any medium, provided the original author(s) and source are credited.
About this article
Cite this article
Ståhle, P., Singh, R.N. & Banerjee, S. Spontaneous fracture of growing precipitates with large misfit strain. Int J Fract 165, 189–197 (2010). https://doi.org/10.1007/s10704-010-9489-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10704-010-9489-2