Synthesis and properties of Fe-W powder

  • D. M. Minić
  • T. Žák
  • O. Schneeweiss
  • N. Pizúrová
  • M. M. Ristić


This paper deals with the study of Fe-W powders, which were prepared by electrolyzing, and their stabilized properties. The synthesized Fe-W powders were studied using X-ray diffraction, thermal analysis, Mössbauer spectroscopy and thermomagnetic measurement. A poor hydrogen absorption occurred. After the heat treatment at 800°C, the amorphous and α-Fe(W) phases were decomposed into prevailing α-Fe with approx. 3 at.% W accompanied by the W(Fe), λ-Fe2W, and Fe2+ in oxide phases.


76.80.+y 61.43.Dq 

Key words

chemical synthesis amorphous materials X-ray diffraction Mössbauer effect hydrogen absorption 


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. [1]
    M. Zdujić, M. Sokić, V. Petrović, and D. Uskoković: Powder Metall. Int.18 (1986) 275.Google Scholar
  2. [2]
    K. Uenishi and P.H. Shingu, inSintering 87, (Ed. S. Simiya) Elsevier, 1988, p. 189.Google Scholar
  3. [3]
    T. Watandle: New Mater. New Proces.3 (1987) 307.Google Scholar
  4. [4]
    D.M. Minić and M.V. Šušić: Mater. Chem. Phys.40 (1995) 281.CrossRefGoogle Scholar
  5. [5]
    D.M. Minić and M.V. Šušić: Mater. Chem. Phys.45 (1995) 280.Google Scholar
  6. [6]
    K. Zeng, T. Klassen, W. Oelerich, and R. Bormann: J. Alloys Compounds283 (1999) 151.CrossRefGoogle Scholar
  7. [7]
    H.P. Klug and L.E. Alexander:X-ray Diffraction procedures. John Wiley & Sons, New York-London-Sidney-Tokio, 1974, pp. 687–690.Google Scholar
  8. [8]
    E. Thilo, K. Dostal, and Z. Anorg: Allg. Chem.298 (1959) 100.CrossRefGoogle Scholar
  9. [9]
    T. Žák: inMössbauer spectroscopy in Material Science (Eds. M. Miglierini and D. Petridis). NATO Science Series, Kluver, Dordrecht, 1999, p. 385.Google Scholar
  10. [10]
    G. Rixecker, R. Birringer, U. Gonser, and H. Gleiter: Phys. Status Solidi A173 (1999) 305.CrossRefADSGoogle Scholar
  11. [11]
    S.M. Dubiel and W. Zinn: Phys. Rev. B30 (1984) 3783.CrossRefADSGoogle Scholar
  12. [12]
    D.L. Williamson, S. Nasu, and U. Gonser: Acta Metall.24 (1976) 1003.CrossRefGoogle Scholar
  13. [13]
    U. Gonser and M. Ron: inApplications of Mössbauer Spectroscopy, Vol. II (Ed. R.L. Cohen). Academic Press, New York, 1980, p. 281.Google Scholar
  14. [14]
    G. Le Caër, P. Delcroix, T.D. Shen, and B. Malaman: Phys. Rev. B54 (1996) 12775.CrossRefADSGoogle Scholar
  15. [15]
    A.A. Novakova, T.Yu. Kiseleva, V.V. Lyovina, D.V. Kuznetsov, and A.L. Dzidziguri: J. Alloy Compounds317–318 (2001) 423.CrossRefGoogle Scholar
  16. [16]
    Y. Tsunoda, S. Imada, and N. Kunitomi: J. Phys. F: Met. Phys.18 (1988) 1421.CrossRefADSGoogle Scholar
  17. [17]
    S.V. Nagender Naidu, A.M. Sriramamurthy, and P. Rama Rao: J. Alloy Phase Diagrams2 (1986), No. 3.Google Scholar

Copyright information

© Institute of Physics, Acad. Sci. CR 2005

Authors and Affiliations

  • D. M. Minić
    • 1
  • T. Žák
    • 2
  • O. Schneeweiss
    • 2
  • N. Pizúrová
    • 2
  • M. M. Ristić
    • 3
  1. 1.Faculty of Physical ChemistryUniversity of BelgradeBelgradeSerbia and Montenegro
  2. 2.Institute of Physics of MaterialsAcad. Sci. CRBrnoCzech Republic
  3. 3.Institute of Technical Sciences SASABelgradeSerbia and Montenegro

Personalised recommendations