Abstract
A new alloy exhibiting high glass-forming ability was developed with the composition Fe70.7C6.7P10.4B5Si1.1Mn0.1Cr2Mo2Ga2. This alloy exhibited excellent castability enabling net-shape-casting. The samples were prepared by copper-mould casting in conical rod form which has a small diameter of 3 mm, a large diameter of 4 mm, and a length of 54 mm, as well as in ring form with an outer diameter of 26 mm, an inner diameter of 18 mm and a thickness of 1 mm. The B S and H C values in DC conditions determined for the ring sample in the as-cast state are 0.45 T and 1.7 A/m, respectively, and for the ribbon in the as-cast state 0.5 T and 3.8 A/m, respectively. On the basis of the measured properties, large industrial use of this new alloy can be predicted.
Similar content being viewed by others
References
F.E. Luborsky: in Amorphous Metallic Alloys (Ed. F.E. Luborsky), Butterworths, London, 1983, p. 360.
M. Shapaan, J Lendvai, and L.K. Varga: J. Non-Cryst. Solids 330 (2003) 150.
M. Stoica, J. Eckert, and S. Roth: J. Metastable Nanocryst. Mater. 12 (2002) 77; www.scientific.net/jmnm.
A. Inoue: Non-Equilibrium Processing of Materials, Pergamon, Oxford, 1999, ch. 14, p. 375.
M. Shapaan, A. Bardos, J. Labar, J. Lendvai, and L.K. Varga: Phys. Status Solidi A 201 (2004) 476.
[6] A.L. Greer: in Rapidly Solidified Alloys (Ed. H.H. Liebermann), Marcel Dekker, New York, 1993, ch. 10, p. 269.
S. Roth, M. Stoica, J. Degmova, H. Grahl, J. Eckert, and L. Schulz: in Proc. Seventh Int. Workshop on 1 and 2 Dimensional Magnetic Measurement and Testing, Luedenscheid, Germany, 16–17 September 2002, (Ed. J. Sievert), Rep. Ser. of the Phys.-Tech. Bundesanstalt Braunschweig, PTB-E-81, 2002, p. 31.
A. Lovas, L.F. Kiss, B. Varga, P. Kamasa, I. Balogh, and I. Bakonyi: J. Phys. IV (France) 8 (1998) Pr2–291.
A. Lovas and E. Kisdi-Koszo: J. Mater. Sci. 22 (1987) 1535.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Bardos, A., Lovas, A., Roth, S. et al. Multicomponent Magnetically Soft Alloy with High Glass-forming Ability and Improved Castability. Czech J Phys 55, 593–599 (2005). https://doi.org/10.1007/s10582-005-0063-5
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10582-005-0063-5