, Volume 25, Issue 5, pp 3067–3078 | Cite as

Superhydrophobic, ultralight and flexible biomass carbon aerogels derived from sisal fibers for highly efficient oil–water separation

  • Yu Liu
  • Yinxian Peng
  • Tao Zhang
  • Fengxian Qiu
  • Dengsen Yuan
Original Paper

Abstract

With the massive discharge of industrial oily wastewater and the frequent occurrence of oil spills at sea in recent years, the fabrication of superhydrophobic and durable oil-absorbing materials is urgently required for oil recovery and disposal of oily water in practical applications. In this paper, ultralight, elastic, superhydrophobic and durable carbon fiber aerogels (CFAs) derived from sisal leaves were prepared via simple alkalization, bleaching, freeze-drying and carbonization. The prepared CFAs were characterized using X-ray diffraction, Fourier transform infrared spectroscopy, N2 adsorption–desorption, contact angle measurement and scanning electron microscopy. The as-prepared CFAs with 3D porous architectures and excellent flexibility under compression were found to be effective oil absorption material for various oils and organic solvents. Textural analyses showed that the CFAs consist of fiber morphologies with high porosity originating from vacancies between individual fibers. The nitrogen sorption analysis confirmed that the material is mesoporous with average pore diameter of 3.03 nm and Brunauer–Emmett–Teller surface area of 399.85 m2/g. The contact angle measurements revealed that CFAs show both superoleophilic and superhydrophobic properties simultaneously with an oil contact angle of 0° and a static water contact angle of 153 ± 1°, thus the aerogels possessed a good oil–water separation ability. Furthermore, the CFAs exhibited a superior absorption capacity in the range from 90 to 188 times of their own weight for different organic solvents and oils. After recycling 10 times, the CFAs still exhibit excellent oils absorption properties, as well as exhibit excellent stability under harsh conditions, showing that the CFAs has excellent reusability performance. This work provides a green strategy to utilize low-cost biomass as raw materials to fabricate superhydrophobic CFAs as an oil absorbent, which has great potential in application of disposal of oily water and environmental protection.

Keywords

Biomass Carbon fiber aerogels Sisal Oil absorption Superhydrophobic 

Notes

Acknowledgments

We thank the Natural Science Foundation of Jiangsu Province (BK20160500, BK20161362 and BK20161264) and National Nature Science Foundation of China (21706100 and U1507115) for financial support. This study was also financially supported by the China Postdoctoral Science Foundation (2016M600373 and 2016M601747), High-Level Personnel Training Project of Jiangsu Province (BRA2016142), Key Research and Development Program of Jiangxi Province (20071BBH80008), China Postdoctoral Science Foundation of Jiangsu Province (1601016A, 1701073C and 1701067C) and Scientific Research Foundation for Advanced Talents, Jiangsu University (15JDG142). The authors also thank Dr. Sheng Tang from Jiangsu University of Science and Technology for revising the manuscript.

Supplementary material

Supplementary material 1 (AVI 19882 kb)

Supplementary material 2 (AVI 14840 kb)

Supplementary material 3 (AVI 8016 kb)

Supplementary material 4 (AVI 45083 kb)

References

  1. Adjalle K, Larose L-V, Bley J, Barnabé S (2017) The effect of organic nitrogenous compound content and different pretreatments on agricultural lignocellulosic biomass characterization methods. Cellulose 24:1395–1406CrossRefGoogle Scholar
  2. Chen D, Zhu G, Lin J, Liu J, Huang S (2015) Renewable reduced graphene oxide-based oil-absorbent aerosols: preparation and essential oils absorption ability. ACS Sustain Chem Eng 3:1428–1433CrossRefGoogle Scholar
  3. Chen F, Song J, Liu Z, Liu J, Zheng H, Huang S, Sun J, Xu W, Liu X (2016) Atmospheric pressure plasma functionalized polymer mesh: an environmentally friendly and efficient tool for oil/water separation. ACS Sustain Chem Eng 4:6828–6837CrossRefGoogle Scholar
  4. French AD (2014) Idealized powder diffraction patterns for cellulose polymorphs. Cellulose 21:885–896CrossRefGoogle Scholar
  5. Hausser N, Marinkovic S, Estrine B (2013) New method for lignocellulosic biomass polysaccharides conversion in butanol, an efficient route for the production of butyl glycosides from wheat straw or poplar wood. Cellulose 20:2179–2184CrossRefGoogle Scholar
  6. Huang T-C, Li P, Yao H, Sue HJ, Kotaki M, Tsai MH (2016) Highly efficient oil–water separators based on dual superhydrophobic and superoleophilic properties of multiwall-carbon nanotube filtration films. RSC Adv 6:12431–12434CrossRefGoogle Scholar
  7. Lei Z, Zhang G, Deng Y, Wang C (2017) Thermo-responsive melamine sponges with switchable wettability by interface-initiated atom transfer radical polymerization for oil/water separation. ACS Appl Mater Interfaces 9(10):8967–8974CrossRefGoogle Scholar
  8. Li Y-Q, Samad YA, Polychronopoulou K, Alhassan SM, Liao K (2014) Carbon aerogel from winter melon for highly efficient and recyclable oils and organic solvents absorption. ACS Sustain Chem Eng 2:1492–1497CrossRefGoogle Scholar
  9. Li L, Li B, Zhang J (2016) Dopamine-mediated fabrication of ultralight graphene aerogels with low volume shrinkage. J Mater Chem A 4:512–518CrossRefGoogle Scholar
  10. Liao CY, Chiou JY, Lin JJ (2015) Temperature-dependent oil absorption of poly(oxypropylene)amine-intercalated clays for environmental remediation. RSC Adv 5:100702–100708CrossRefGoogle Scholar
  11. Loow Y-L, Wu TY, Yang GH, Md. Jahim J, Teoh WH, Mohammad AW (2016) Role of energy irradiation in aiding pretreatment of lignocellulosic biomass for improving reducing sugar recovery. Cellulose 23:2761–2789CrossRefGoogle Scholar
  12. Loow Y-L, New EK, Yang GH, Ang LY, Foo LYW, Wu TY (2017) Potential use of deep eutectic solvents to facilitate lignocellulosic biomass utilization and conversion. Cellulose 24:3591–3618CrossRefGoogle Scholar
  13. Nardecchia S, Carriazo D, Ferrer ML, Gutierrez MC, del Monte F (2013) Three dimensional macroporous architectures and aerogels built of carbon nanotubes and/or graphene: synthesis and applications. Chem Soc Rev 42:794–830CrossRefGoogle Scholar
  14. Nishiyama Y, Langan P, Chanzy H (2002) Crystal structure and hydrogen-bonding system in cellulose Iβ from synchrotron X-ray and neutron fiber diffraction. J Am Chem Soc 124:9074–9082CrossRefGoogle Scholar
  15. Patowary M, Ananthakrishnan R, Pathak K (2014) Chemical modification of hygroscopic magnesium carbonate into superhydrophobic and oleophilic sorbent suitable for removal of oil spill in water. Appl Surf Sci 320:294–300CrossRefGoogle Scholar
  16. Rong J, Qiu F, Zhang T, Zhang X, Zhu Y, Xu J, Yang D, Dai Y (2017) A facile strategy toward 3D hydrophobic composite resin network decorated with biological ellipsoidal structure rapeseed flower carbon for enhanced oils and organic solvents selective absorption. Chem Eng J 322:397–407CrossRefGoogle Scholar
  17. Saboktakin A, Saboktakin MR (2015) Improvements of reinforced silica aerogel nanocomposites thermal properties for architecture applications. Int J Biol Macromol 72:230–234CrossRefGoogle Scholar
  18. Saththasivam J, Loganathan K, Sarp S (2016) An overview of oil–water separation using gas flotation systems. Chemosphere 144:671–680CrossRefGoogle Scholar
  19. Shi H, Shi D, Yin L, Yang Z, Luan S, Gao J, Zha J, Yin J, Li RKY (2014) Ultrasonication assisted preparation of carbonaceous nanoparticles modified polyurethane foam with good conductivity and high oil absorption properties. Nanoscale 6:13748–13753CrossRefGoogle Scholar
  20. Wang T, Yang W-L, Hong Y, Hou Y-L (2016) Magnetic nanoparticles grafted with amino-riched dendrimer as magnetic flocculant for efficient harvesting of oleaginous microalgae. Chem Eng J 297:304–314CrossRefGoogle Scholar
  21. Wu L, Li L, Li B, Zhang J, Wang A (2015) Magnetic, durable, and superhydrophobic polyurethane@Fe3O4@SiO2@fluoropolymer sponges for selective oil absorption and oil/water separation. ACS Appl Mater Interfaces 7:4936–4946CrossRefGoogle Scholar
  22. Xu Z, Jiang X, Zhou H, Li J (2017) Preparation of magnetic hydrophobic polyvinyl alcohol (PVA)–cellulose nanofiber (CNF) aerogels as effective oil absorbents. Cellulose.  https://doi.org/10.1007/s10570-017-1619-9 Google Scholar
  23. Yang S, Chen L, Mu L, Hao B, Ma P-C (2015) Low cost carbon fiber aerogel derived from bamboo for the adsorption of oils and organic solvents with excellent performances. RSC Adv 5:38470–38478CrossRefGoogle Scholar
  24. Yuan D, Zhang T, Guo Q, Qiu F, Yang D, Ou Z (2017) A novel hierarchical hollow SiO2@MnO2 cubes reinforced elastic polyurethane foam for the highly efficient removal of oil from water. Chem Eng J 327:539–547CrossRefGoogle Scholar
  25. Yue X, Zhang T, Yang D, Qiu F, Rong J, Xu J, Fang J (2017) The synthesis of hierarchical porous Al2O3/acrylic resin composites as durable, efficient and recyclable absorbents for oil/water separation. Chem Eng J 309:522–531CrossRefGoogle Scholar
  26. Zhang T, Zhang Q, Wang X, Li Q, Rong J, Qiu F (2015) Synthesis of Mn2O3/poly(styrene-co-butyl methacrylate) resin composites and their oil-absorbing properties. RSC Adv 5:101186–101192CrossRefGoogle Scholar
  27. Zhang Z, Yang X, Jia H, Zhang H (2016) Kerogen beneficiation from Longkou oil shale using gravity separation method. Energy Fuels 30:2841–2845CrossRefGoogle Scholar
  28. Zhang C, Yang D, Zhang T, Qiu F, Dai Y, Xu J, Jing Z (2017a) Synthesis of MnO2/poly(n-butylacrylate-co-butyl methacrylate-co-methyl methacrylate) hybrid resins for efficient oils and organic solvents absorption. J Clean Prod 148:398–406CrossRefGoogle Scholar
  29. Zhang T, Kong L, Dai Y, Yue X, Rong J, Qiu F, Pan J (2017b) Enhanced oils and organic solvents absorption by polyurethane foams composites modified with MnO2 nanowires. Chem Eng J 309:7–14CrossRefGoogle Scholar
  30. Zhou S, Liu P, Wang M, Zhao H, Yang J, Xu F (2016) Sustainable, reusable, and superhydrophobic aerogels from microfibrillated cellulose for highly effective oil/water separation. ACS Sustain Chem Eng 4:6409–6416CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media B.V., part of Springer Nature 2018

Authors and Affiliations

  1. 1.School of Environmental and Chemical EngineeringJiangsu University of Science and TechnologyZhenjiangChina
  2. 2.School of Chemistry and Chemical EngineeringJiangsu UniversityZhenjiangChina

Personalised recommendations