Functionalization of cotton fabrics with corona/air RF plasma and colloidal TiO2 nanoparticles

  • Published:
Cellulose Aims and scope Submit manuscript

Abstract

This study discusses the possibility of using a corona discharge at atmospheric pressure and air RF plasma at low pressure for the cotton fibre activation prior to deposition of colloidal TiO2 nanoparticles in order to enhance antibacterial, UV protective and self-cleaning properties. X-ray photoelectron spectroscopy (XPS) analysis confirmed the presence of TiO2 nanoparticles on the surface of cotton fibres. XPS elemental mapping indicated that TiO2 nanoparticles were more evenly distributed across the surface of untreated and corona pre-treated cotton fabrics in comparison with RF plasma pre-treated fabric. Atomic absorption spectroscopy measurements revealed that the equivalent total content of TiO2 in the cotton fabrics pre-treated by corona and RF plasma was 31% higher than in the fabric that did not undergo any treatment prior to loading of TiO2 nanoparticles. In order to achieve maximum bacteria (Gram-negative bacteria Escherichia coli) reduction, untreated cotton fabric had to be loaded with colloidal TiO2 nanoparticles twice, but only once following corona or RF plasma pre-treatment. Deposition of TiO2 nanoparticles onto cotton fabrics provided maximum UV protective rating of 50+. Extraordinary photocatalytic activity of TiO2 nanoparticles deposited onto cotton fabrics was proved by self-cleaning of blueberry juice stains and photodegradation of methylene blue in aqueous solution under UV illumination.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

Similar content being viewed by others

References

  • Bozzi A, Yuranova T, Kiwi J (2005a) Self-cleaning of wool-polyamide and polyester textiles by TiO2-rutile modification under daylight irradiation at ambient temperature. J Photochem Photobio A 172:27–34

    Article  CAS  Google Scholar 

  • Bozzi A, Yuranova T, Guasaquillo I, Laub D, Kiwi J (2005b) Self-cleaning of modified cotton textiles by TiO2 at low temperatures under daylight irradiation. J Photochem Photobio A 174:156–164

    Article  CAS  Google Scholar 

  • Cai Z, Qiu Y, Zhang C, Hwang YH, McCord M (2003) Effect of atmospheric plasma treatment on desizing of PVA on cotton. Text Res J 73:670–674

    Article  CAS  Google Scholar 

  • Chung C, Lee M, Kyung Choe E (2004) Characterization of cotton fabric scouring by FTIR ATR spectroscopy. Carbohyd Polym 58:417–420

    Article  CAS  Google Scholar 

  • Clemencic D, Simoncic B, Tomsic B, Orel B (2010) Biodegradation of silver functionalised cellulose fibres. Carbohyd Polym 80:426–435

    Article  Google Scholar 

  • Daoud WA, Xin JH (2004) Low temperature sol-gel processed photocatalytic Titania coating. J Sol-Gel Sci Techn 29:25–29

    Article  CAS  Google Scholar 

  • Daoud WA, Xin JH, Zhang YH (2005) Surface functionalization of cellulose fibres with titanium dioxide nanoparticles and their combined bactericidal activities. Surf Sci 599:69–75

    Article  CAS  Google Scholar 

  • Fras L, Johansson LS, Stenius P, Laine J, Stana-Kleinschek K, Ribitsch V (2005) Analysis of the oxidation of cellulose fibres by titration and XPS. Colloid Surf A 260:101–108

    Article  CAS  Google Scholar 

  • Ghoranneviss M, Bahareh M, Shahidi S, Anvari A, Rashidi A (2006) Decolourization of denim fabrics with cold plasmas in the presence of magnetic field. Plasma Proc Polym 3:316–321

    Article  CAS  Google Scholar 

  • Johansson K (2007) Plasma modification of natural cellulosic fibres. In: Shishoo R (ed) Plasma technologies for textiles. Woodhead publishing in textiles, Cambridge, pp 251–260

    Google Scholar 

  • Johansson LS, Campbell JM (2004) Reproducible XPS on biopolymers: cellulose studies. Surf Interface Anal 36:1018–1022

    Article  CAS  Google Scholar 

  • Karahan HA, Özdoğan E (2008) Improvements of surface functionality of cotton fibres by atmospheric plasma treatment. Fiber Polym 9:21–26

    Article  CAS  Google Scholar 

  • Kiwi J, Pulgarin C (2010) Innovative self-cleaning and bactericide textiles. Catal Today 151:2–7

    Article  CAS  Google Scholar 

  • Kontturi E, Thüne PC, Niemantsverdriet JW (2003) Novel method for preparing cellulose model surfaces by spin coating. Polymer 44:3621–3625

    Article  CAS  Google Scholar 

  • Lee HJ, Yeo SY, Jeong SH (2003) Antibacterial effect of nanosized silver colloidal solution on textiles fabrics. J Mater Sci 38:2199–2204

    Article  CAS  Google Scholar 

  • Mejía MI, Marín JM, Restrepo G, Pulgarín C, Mielczarski E, Mielczarski J, Arroyo Y, Lavanchy JC, Kiwi J (2009) Self-cleaning modified TiO2 cotton pre-treated by UVC-light (185 nm) and RF-plasma in vacuum and also under atmospheric pressure. Appl Catal B 91:481–488

    Article  Google Scholar 

  • Mihailović D, Šaponjić Z, Radoičić M, Molina R, Radetić T, Jovančić P, Nedeljković J, Radetić M (2010a) Novel properties of PES fabrics modified by corona discharge and colloidal TiO2 nanoparticles. Polym Advan Technol. doi:10.1002/pat.1568

  • Mihailović D, Šaponjić Z, Molina R, Radoičić M, Esquena J, Jovančić P, Nedeljković J, Radetić M (2010b) Multifunctional properties of polyester fabrics modified by corona discharge/air RF plasma and colloidal TiO2 nanoparticles. Polym Composit. doi:10.1002/pc.21053

  • Mihailović D, Šaponjić Z, Radoičić M, Radetić T, Jovančić P, Nedeljković J, Radetić M (2010c) Functionalization of polyester fabrics with alginates and TiO2 nanoparticles. Carbohyd Polym 79:526–532

    Article  Google Scholar 

  • Morent R, De Geyter N, Verschuren J, De Clerck K, Kiekens P, Leys C (2008) Non-thermal plasma treatment of textiles. Surf Coat Tech 202:3427–3449

    Article  CAS  Google Scholar 

  • Navaneetha Pandiyaraj K, Selvarajan V (2008) Non-thermal plasma treatment for hydrophilicity improvement of grey cotton fabrics. J Mater Process Tech 199:130–139

    Article  Google Scholar 

  • Paul R, Bautista L, De la Varga M, Botet JM, Casals E, Puntes V, Marsal F (2010) Nano-cotton fabrics with high ultraviolet protection. Text Res J 80:454–462

    Article  CAS  Google Scholar 

  • Qi K, Daoud WA, Xin JH, Mak CL, Tang W, Cheung WP (2006) Self-cleaning cotton. J Mater Chem 16:4567–4574

    Article  CAS  Google Scholar 

  • Qi K, Xin JH, Daoud WA, Mak CL (2007) Functionalizing polyester fiber with a self-cleaning property using anatase TiO2 and low-temperature plasma treatment. Int J Appl Ceram Tec 4:554–563

    Article  CAS  Google Scholar 

  • Radetić M, Jovančić P, Puač N, Petrović ZLj, Šaponjić Z (2009) Plasma induced decolorization of indigo dyed denim fabrics related to mechanical properties and fiber surface morphology. Text Res J 79:558–565

    Article  Google Scholar 

  • Sun D, Stylios GK (2006) Fabric surface properties affected by low temperature plasma treatment. J Mater Process Tech 173:172–177

    Article  CAS  Google Scholar 

  • Sun D, Stylos G (2004) The effect of low temperature plasma treatment on the scouring and dyeing processes of natural fabrics. Text Res J 74:751–756

    Article  CAS  Google Scholar 

  • Thomas H (2007) Plasma modification of wool. In: Shishoo R (ed) Plasma technologies for textiles. Woodhead publishing in textiles, Cambridge, pp 228–246

    Chapter  Google Scholar 

  • Topalovic T, Nierstrasz VA, Bautista L, Jocic D, Navarro A, Warmoeskerken MMCG (2007) XPS and contact angle of cotton surface oxidation by catalytic bleaching. Colloid Surf A 296:76–85

    Article  CAS  Google Scholar 

  • Tourrette O, De Geyterb N, Jocic D, Morent R, Warmoeskerken MMCG, Leys C (2009) Incorporation of poly(N-isopropylacrylamide)/chitosan microgel onto plasma functionalized cotton fibre surface. Colloid Surf A 352:126–135

    Article  CAS  Google Scholar 

  • Tung WS, Daoud WA (2009) Photocatalytic self-cleaning keratines: a feasibility study. Acta Biomater 5:50–56

    Article  CAS  Google Scholar 

  • Uddin MJ, Cesano F, Bonino F, Bordiga S, Spoto G, Scarano D, Zecchina A (2007) Photoactive TiO2 films on cellulose fibres: synthesis and characterization. J Photochem Photobio A 189:286–294

    Article  CAS  Google Scholar 

  • Ueda M, Tokino S (1996) Physico-chemical modifications of fibres and their effect on coloration and finishing. Rev Progress Color 26:9–19

    Article  CAS  Google Scholar 

  • Wakida T, Tokino S (1996) Surface modification of fibre and polymeric materials by discharge treatment and its application to textile processing. Ind J Fibre Text Res 21:69–78

    CAS  Google Scholar 

  • Wu D, Long M, Zhou J, Cai W, Zhu X, Chen C, Wu Y (2009) Synthesis and characterization of self-cleaning cotton fabrics modified by TiO2 through a facile approach. Surf Coat Tech 203:3728–3733

    Article  CAS  Google Scholar 

  • Xin JH, Daoud WA, Kong YY (2004) A new approach to UV-blocking treatment for cotton fabrics. Text Res J 74:97–100

    Article  CAS  Google Scholar 

  • Yuen CWM, Kan CW (2007) Influence of low-temperature plasma on the ink-jet-printed cotton fabric. J Appl Polym Sci 104:3214–3219

    Article  CAS  Google Scholar 

  • Yuranova T, Mosteo R, Bandara J, Laub D, Kiwi J (2006) Self-cleaning cotton textiles surfaces modified by photoactive SiO2/TiO2 coating. J Molec Catal A 244:160–167

    Article  CAS  Google Scholar 

  • Yuranova T, Laub D, Kiwi J (2007) Synthesis, activity and characterization of textiles showing self-cleaning activity under daylight irradiation. Catal Today 122:109–117

    Article  CAS  Google Scholar 

Download references

Acknowledgments

The financial support for this work was provided by the Ministry of Science of Republic of Serbia 45020 and 172056.

Author information

Authors and Affiliations

  1. Textile Engineering Department, Faculty of Technology and Metallurgy, University of Belgrade, Belgrade, Serbia

    D. Mihailović, P. Jovančić & M. Radetić

  2. Vinča Institute of Nuclear Sciences, Belgrade, Serbia

    Z. Šaponjić, M. Radoičić & J. Nedeljković

  3. Institute of Physics, Zemun, Serbia

    S. Lazović

  4. Thermo Fisher Scientific, West Sussex, UK

    C. J. Baily

Authors
  1. D. Mihailović
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Z. Šaponjić
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. M. Radoičić
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. S. Lazović
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. C. J. Baily
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. P. Jovančić
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. J. Nedeljković
    View author publications

    You can also search for this author in PubMed Google Scholar

  8. M. Radetić
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to M. Radetić.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Mihailović, D., Šaponjić, Z., Radoičić, M. et al. Functionalization of cotton fabrics with corona/air RF plasma and colloidal TiO2 nanoparticles. Cellulose 18, 811–825 (2011). https://doi.org/10.1007/s10570-011-9510-6

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10570-011-9510-6

Keywords

Search

Navigation