Abstract
La0.8Sr0.2MnO3 (LSM) catalyst has been successfully prepared by solid phase method (G-LSM-T), sol–gel method (C-LSM-T) and molten salt method (S-LSM-T), using as-prepared MnCO3 microspheres as templates, respectively. It was shown that the S-LSM-550 catalyst presented well-formed perovskite structures, large specific surface area (49.65m2/g) and promising catalytic activity in CO oxidation, which T50 and T90 for CO conversion over fresh S-LSM-550 were 145.14 °C and 170.73 °C. The S-LSM-550 calcined at 550 °C for 2 h exhibited excellent thermal stability and catalytic activity compared with the samples prepared by solid phase method and sol–gel method. Its superior catalytic performance could be greatly attributed to its stable microstructure, high surface Mn4+/Mn3+ molar ratio and more available surface adsorbed oxygen species.
Graphical Abstract
Similar content being viewed by others
References
Apergis N, Bhattacharya M, Hadhri W (2020) Environ Sci Pollut Res 27:8142–8156
Pahalagedara L, Kriz DA, Wasalathanthri N, Weerakkody C, Meng Y, Dissanayake S, Pahalagedara M, Luo Z, Suib SL, Nandi P, Meyer RJ (2017) Appl Catal B 204:411–420
Dey S, Dhal GC, Mohan D, Prasad R (2017) Mater Discov 8:26–34
Dey S, Dhal GC, Mohan D, Prasad R (2017) Mater Discov 8:18–25
Chee SW, Arce-Ramos JM, Li W et al (2020) Nat Commun 11:2133
Santos VP, Carabineiro SAC, Tavares PB, Pereira MFR, Órfão JJM, Figueiredo JL (2010) Appl Catal B 99(1–2):198–205
Seyfi B, Baghalha M, Kazemian H (2009) Chem Eng J 148(2–3):306–311
Tarjomannejad A, Farzi A, Gómez MJI et al (2016) Catal Lett 146:2330–2340
Zhang J, Weng X, Wu Z, Liu Y, Wang H (2012) Appl Catal B 126:231–238
Shuai T, Farheen S, Shize Y, Zhengyuan L, Jingjie W, Pulickel MA (2019) ACS Mater Lett 1(2):230–236
Ding Y, Wang S, Zhang L, Chen Z, Wang M, Wang S (2017) Catal Commun 97:88–92
Wang Y, Xie S, Deng J, Deng S, Wang H, Yan H, Dai H (2014) ACS Appl Mater Interfaces 6(20):17394–17401
Predoana L, Malic B, Kosec M, Carata M, Caldararu M, Zaharescu M (2007) J Eur Ceram Soc 27(13–15):4407–4411
Dodiya N, Varshney D (2013) J Mol Struct 1031:104–109
Vradman L, Zana J, Kirschner A, Herskowitz M (2013) Phys Chem Chem Phys 15(26):10914–10920
Huang X, Pan H, Chen K, Yin Z, Hong J (2018) CrystEngComm 20(43):7020–7029
Huang X, Niu P, Pan H, Shang X (2018) J Solid State Chem 265:218–226
Yu C, Zhang L, Shi J, Zhao J, Gao J, Yan D (2008) Adv Func Mater 18(10):1544–1554
Huang F, Sun X, Zheng Y, Xiao Y, Zheng Y (2018) Mater Lett 210:287–290
Lang X, Mo H, Hu X, Tian H (2017) Dalton Trans 46(40):13720–13730
Bie S, Zhu Y, Su J, Jin C, Liu S, Yang R, Wu J (2015) J Mater Chem A 3(44):22448–22453
Tang X, Gao F, Xiang Y, Yi H, Zhao S, Liu X, Li Y (2015) Ind Eng Chem Res 54(37):9116–9123
Huang X, Shang X, Niu P (2017) Acta Phys Chim Sin 33(7):1462–1473
Martinovic F, Tran QN, Deorsola FA et al (2020) Catal Sci Technol 10(7):2193–2202
Acknowledgements
This research did not receive any specific grant from funding agencies in the public, commercial, or not-for-profit sectors.
Funding
The authors have not disclosed any funding.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors have not disclosed any competing interests.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Huang, X., Yang, N., Li, X. et al. La0.8Sr0.2MnO3 Perovskite Catalysts Prepared by Different Methods for CO Oxidation. Catal Lett 152, 3843–3852 (2022). https://doi.org/10.1007/s10562-022-03921-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10562-022-03921-8