Abstract
Small amount of Nickel deposited on SiO2 support by electroless plating was verified to have a significant promoting effect on the catalytic performance of the K2MoO4/SiO2 catalyst for methanethiol synthesis from H2S-rich synthesis gas. The addition of Nickel was found to be in favor of the suppression of the CO2 formation. The results of BET, TPR and Raman characterizations for the Ni-modified SiO2 and the catalyst K2MoO4/Ni-SiO2 showed that the surface properties of Ni-modified SiO2 were similar to those of unmodified SiO2 and that no Raman characteristic band specific to NiO from the catalyst K2MoO4/Ni-SiO2 was detected. For oxidic K2MoO4/Ni-SiO2 catalyst lower reduction temperature was measured. For sulfided catalysts, reduced molybdenum oxides and oxysulfides were detected, which was inferred to be closely related to high catalytic activity of the catalyst.
Similar content being viewed by others
References
Buchholz B (1983) US Patent 4,410,731
Haines PG (1984) US Patent 4,449,006
Ratcliffe CT, Tromp PJ, Wachs IE (1986) US Patent 4,570,020
Boulinguiez M, Forquy C, Barrault J (1987) US Patent 4,665,242
Chersich CC, Wachs IE (1986) EP0167354
Barrault J, Boulinguize M, Forquy C, Maurel R (1987) Appl Catal 33:309
Mul G, Wachs IE, Hirschon AS (2003) Catal Today 78:327
Zhang BJ, Taylor SH, Hutchings GJ (2003) Catal Lett 91:181
Yang YQ, Wang Q, Lin RC, Zhang HB (2005) WO2005040082
Zh L, Yi Chen (1998) J Catal 177:314
Tsai TK, Chuang CC, Chao CG, Liu WL (2003) Diamond Relat Mater 12:1453
Liu WL, Chen WJ, Tsai TK, Hsieh SH, Chang SY (2007) Appl Surf Sci 253:3843
Dai HB, Liang Y, Wang P, Yao XD, Rufford T, Lu M, Cheng HM (2008) Int J Hydrogen Energy 33:4405–4412
Chen AP, Wang Q, Hao YJ, Fang WP, Yang YQ (2007) Catal Lett 118:295
Erdöhelyi A, Fodor K, Solymosi F (1997) J Catal 166:244
Cheng CP, Schrader GL (1979) J Catal 60:276
Kantschewa M, Delannay F, Jeziorowski H, Delgado E, Eder S, Ertl G, Knözinger H (1984) J Catal 87:482
Damyanova S, Spojakina A, Jiratova K (1995) Appl Catal A Gen 125:257
Williams CC, Ekerdt JG, Jehng JM, Hardcastle FD, Turek AM, Wachs IE (1991) J Phys Chem 95:8781
Verbruggen NFD, von Hippel LMJ, Mestl G, Lengeler B, Knözinger H (1994) Langmuir 10:3073
Kim DS, Segawa K, Soeya T, Wachs IE (1992) J Catal 136:539
Jiang M, Bian GZh, Li F, Fu YL (1994) J Catal 146:144
Schrader GL, Cheng CP (1983) J Catal 80:369
Lewis IR, Edwards HGM (2001) Handbook of Raman Spectroscopy from the research laboratory to the process line, USA p. 814
Feng L, Li XG, Dadyburjor DB, Kugler EL (2000) J Catal 190:1
Wang Q (2007) Ph.D thesis, University of Xiamen in China
Acknowledgments
The authors gratefully acknowledge Degussa GmbH (Germany) for financial support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hao, Y., Zhang, Y., Chen, A. et al. Study on Methanethiol Synthesis from H2S-Rich Syngas Over K2MoO4 Catalyst Supported on Electrolessly Ni-Plated SiO2 . Catal Lett 129, 486–492 (2009). https://doi.org/10.1007/s10562-008-9827-4
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10562-008-9827-4