The results of a study of the swelling and in-reactor creep of EI-847, EP-172, and ChS-68 austenitic steel after irradiation in materials science assemblies in the range 330–700°C and damaging dose 20–96 dpa are presented. The temperature dependences of the volume change of steel were obtained from measurements of the diameter of unloaded ampuls. It is shown that the swelling of the steel increases linearly with increasing tangential stress. The modulus of in-reactor creep in the interval 410–630°C for the steel investigated in the cold-deformed state varies in the range (0.5–3)·10–6 MPa–1·dpa–1. For lower and higher temperatures, the creep modulus increases to (5–8)·10–6 MPa–1·dpa–1.
Similar content being viewed by others
References
A. N. Vorobyev, N. I. Budylkin, E. G. Mironova, et al., “Irradiation creep and stress-enhanced swelling of Fe–16Cr–15Ni–Nb austenitic steel in BN-350,” J. Nucl. Mater., 258–263 , 1618–1622 (1998).
S. I. Porollo, A. N. Vorobyev, Yu. V. Konobeev, et al., “Irradiation creep and stress-affected swelling in austenitic stainless steel 16Cr–15Ni–3MO–Nb–B irradiation in the BN-350 reactor,” in: Proc. 19th Int. Symp. on Effect of Radiation on Materials, US, ASTM STP 1366 (2000), pp. 679–687.
N. I. Budylkin, E. G. Mironova, A. N. Vorobiev, and V. D. Dmitriev, “In-reactor creep of steels and alloys with different iron-chromium-nickel base under the conditions of a commercial fast reactor BN-350,” in: Int. Conf. on Radiation Materials Science, Alushta (1990), Vol. 7, pp. 146–152.
S. I. Porollo, A. N. Vorobyev, and V. D. Dmitriev, “Post-irradiation examination of the BN-600 pins,” in: Proc. Int. Conf. on Fast Reactor Core and Fuel Structural Behavior, Inverness, UK (1990), pp. 237–241.
V. N. Bykov, V. D. Dmitriev, L. G. Kostromin, et al., “Empirical dependence of the swelling 0Kh16N15M3B steel on the dose and temperature of irradiation,” At. Énerg., 40, No. 4, 293–295 (1976).
S. I. Porollo,Yu. V. Konobeev, and S. V. Shulepin, “Analysis of the behavior of BN-600 fuel-element cladding from 0Kh16N15M3BR steel at high fuel burnup,” ibid., 106, No. 4, 188–195 (2009).
V. D. Dmitriev, S. I. Porollo, A. N. Vorobiov, et al., “Investigation of swelling and mechanical properties of fuel-element cladding from 06Kh16N15M2G2TFR steel after irradiation in BN-600 reactor to damaging dose 87.5 dpa,” in: Int. Conf. on Radiation Materials Science, Alushta (1990), Vol. 3, 49–55.
V. D. Dmitriev, S. I. Porollo, V. S. Ageev, et al., “Electron microscopic studies of austenitic stainless steel 06Kh16N15M2G2TFR in a cold-deformed state, irradiated with damaging doses to 87 dpa in a BN-600 reactor,” ibid., pp. 56–65.
S. I. Porollo, Yu. V. Konobeev, and F. A. Garner, “Swelling and microstructure of austenitic stainless steel ChS-68 after high dose irradiation,” J. Nucl. Mater., 393, 61–66 (2009).
J. Dupouy, J. Lehmann, and J. Boutard, “Swelling and irradiation creep of type 316 stainless steel,” in: Conf. on Reactor Materials Science, Alushta (1978), Vol. 5, pp. 280–296.
J. Bates and R. Powell, “Irradiation-induced swelling in commercial alloys,” J. Nucl. Mater., 102, 200–216 (1981).
J. Watkin, T. Gittus, and J. Standring, “The influence of alloy constitution on the swelling of austenitic stainless steels and nickel based alloys,” in: Proc. Conf. on Radiation Effects in Breeder Reactor Structural Materials, Scottsdale, Arizona (1977), pp. 476–480.
B. Loomis, A. Taylor, and S. Gerber, “Void swelling of Nb and Nb–1%Zr induced by 58Ni+ bombardment,” J. Nucl. Mater., 56, 25–37 (1975).
P. Neuzinger and P. Sacchetti, “Dose-rate dependence of swelling and damage in ion-irradiated nickel,” ibid., 57,193–197 (1975).
H. Brager and J. Straalsund, “Irradiation instability of cold-worked type 304 stainless steel,” Trans. ANS, 14, No. 2, 555 (1971).
J. Foster and J. Flinn, “Residual stress behavior in fast neutron irradiated SA AISI 304 L stainless steel cylindrical tubing,” J. Nucl. Mater., 89, 99–112 (1980).
J. Bates and E. Gilbert, “Experimental evidence for stress enhanced swelling,” ibid., 59, 95–102 (1976).
J. Bates and E. Gilbert, “Effects of stress on swelling in 316 stainless steel,” ibid., 71, 286–292 (1978).
V. K. Shamardin, V. N. Golovanov, A. V. Povstyanko, et al., “Irradiation creep and swelling of 0X16N15M3B steel and its modification 0X16H15M3MP steel,” in: Proc. 14th Int. Symp. on Effects of Radiation on Materials, US, ASTM STP 1046 (1990), Vol. II, pp. 753–765.
K. Ehrlich, “Deformation behavior of austenitic stainless steels after and during neutron irradiation,” J. Nucl. Mater., 133–134, 119–126 (1985).
F. A. Garner, “Irradiation performance of cladding and structural steels in liquid metal reactors,” Mater. Sci. Technol., 10A, 420–543 (1994).
I. Shibahara, S. Ukai, S. Onose, and S. Shikakura, “Irradiation performance of modified 316 stainless steel for Monju fuel,” J. Nucl. Mater., 204, 131–140 (1993).
V. A. Krasnoselov, A. N. Kolesnikov, and V. I. Prokhorov, “Study of the radiation changes of the shape of a hexahedral jacket of a materials science assembly of the BOR-60 reactor,” At. Énerg., 63, No. 4, 240–242 (1987).
S. I. Porollo, Yu. V. Konobeev, A. M. Dvoriashin, et al., “Irradiation creep and mechanical properties of two ferriticmartensitic steels irradiated in the BN-350 fast reactor,” J. Nucl. Mater., 283–287, 239–243 (2000).
Author information
Authors and Affiliations
Additional information
Translated from Atomnaya Énergiya, Vol. 110, No. 4, pp. 207–214, April, 2011.
Rights and permissions
About this article
Cite this article
Porollo, S.I., Shulepin, S.V., Ivanov, A.A. et al. Swelling and radiation creep of austenitic corrosion-resistant steel irradiated by neutrons in wide dose and temperature ranges. At Energy 110, 248–258 (2011). https://doi.org/10.1007/s10512-011-9419-z
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10512-011-9419-z