Computation of the Distribution of the Fiber-Matrix Interface Cracks in the Edge Trimming of CFRP
- 322 Downloads
Edge trimming is commonly used to bring the CFRP components to right dimension and shape in aerospace industries. However, various forms of undesirable machining damage occur frequently which will significantly decrease the material performance of CFRP. The damage is difficult to predict and control due to the complicated changing laws, causing unsatisfactory machining quality of CFRP components. Since the most of damage has the same essence: the fiber-matrix interface cracks, this study aims to calculate the distribution of them in edge trimming of CFRP, thereby to obtain the effects of the machining parameters, which could be helpful to guide the optimal selection of the machining parameters in engineering. Through the orthogonal cutting experiments, the quantitative relation between the fiber-matrix interface crack depth and the fiber cutting angle, cutting depth as well as cutting speed is established. According to the analysis on material removal process on any location of the workpiece in edge trimming, the instantaneous cutting parameters are calculated, and the formation process of the fiber-matrix interface crack is revealed. Finally, the computational method for the fiber-matrix interface cracks in edge trimming of CFRP is proposed. Upon the computational results, it is found that the fiber orientations of CFRP workpieces is the most significant factor on the fiber-matrix interface cracks, which can not only change the depth of them from micrometers to millimeters, but control the distribution image of them. Other machining parameters, only influence the fiber-matrix interface cracks depth but have little effect on the distribution image.
KeywordsCFRP Edge trimming Machining parameters Fiber-matrix interface crack Computational method
This work is supported by National Natural Science Foundation of China-United with Liaoning Province (No. U1508207), National Natural Science Foundation of China (No. 51575082), National Key Basic Research Program of China (973 Program, No. 2014CB046503), National Innovative Research Group (No. 51321004), Fundamental Research Funds for the Central Universities (No. DUT16TD01). The authors wish to thank the anonymous reviewers for their comments which lead to improvements of this paper.
- 7.López de Lacalle, L.N., Lamikiz, A.: Milling of carbon fiber-reinforced plastics. Adv. Mater. Res. 83, 49–55 (2010)Google Scholar
- 15.Haddad, M., Zitoune, R., Eyma, F.: High speed trimming of carbon fiber reinforced polymers. 15th European Conference on Composite Materials, Venice, Italy, 2012Google Scholar
- 16.Chatelain, J.F., Zaghbani, I., Monier, J.: Effect of ply orientation on roughness for the trimming process of CFRP laminates. World Acad. Sci. Eng. Technol. 6(8), 1516–1522 (2012)Google Scholar
- 24.Janardhan, P., Sheikh-Ahmad, J., Cheraghi, H.: Edge trimming of CFRP with diamond interlocking tools. Proceedings of Aerospace Manufacturing and Automated Fastening Conference, 2006Google Scholar
- 25.Bourcier, D.R.: Exposure evaluation of composite materials with emphasis on cured composite dust. Appl. Ind. Hyg. 12, 40–46 (1989)Google Scholar