Abstract
In this paper, a new numerical method that combines a surface-based cohesive model and extended finite element method (XFEM) without predefining the crack paths is presented to simulate the microscopic damage evolution in composites under uniaxial transverse tension. The proposed method is verified to accurately capture the crack kinking into the matrix after fiber/matrix debonding. A statistical representative volume element (SRVE) under periodic boundary conditions is used to approximate the microstructure of the composites. The interface parameters of the cohesive models are investigated, in which the initial interface stiffness has a great effect on the predictions of the fiber/matrix debonding. The detailed debonding states of SRVE with strong and weak interfaces are compared based on the surface-based and element-based cohesive models. The mechanism of damage in composites under transverse tension is described as the appearance of the interface cracks and their induced matrix micro-cracking, both of which coalesce into transversal macro-cracks. Good agreement is found between the predictions of the model and the in situ experimental observations, demonstrating the efficiency of the presented model for simulating the microscopic damage evolution in composites.
Similar content being viewed by others
References
Liu, P.F., Zheng, J.Y.: Recent developments on damage modeling and finite element analysis for composite laminates: a review. Mater. Des. 31(8), 3825–3834 (2010)
Mishnaevsky, L., Brøndsted, P.: Micromechanical modeling of damage and fracture of unidirectional fiber reinforced composites: a review. Comput. Mater. Sci. 44(4), 1351–1359 (2009)
Sun, C.T., Vaidya, R.S.: Prediction of composite properties from a representative volume element. Compos. Sci. Technol. 56(2), 171–179 (1996)
Asp, L.E., Berglund, L.A., Talreja, R.: Prediction of matrix-initiated transverse failure in polymer composites. Compos. Sci. Technol. 56(9), 1089–1097 (1996)
Xu, Q., Lu, Z.: An elastic–plastic cohesive zone model for metal-ceramic interfaces at finite deformations. Int. J. Plast. 41, 147–164 (2013)
París, F., Correa, E., Mantič, V.: Kinking of transversal interface cracks between fiber and matrix. J. Appl. Mech. 74(4), 703–716 (2007)
Trias, D., Costa, J., Mayugo, J.A., Hurtado, J.E.: Random models versus periodic models for fibre reinforced composites. Comput. Mater. Sci. 38(2), 316–324 (2006)
González, C., LLorca, J.: Mechanical behavior of unidirectional fiber-reinforced polymers under transverse compression: microscopic mechanisms and modeling. Compos. Sci. Technol. 67(13), 2795–2806 (2007)
Totry, E., González, C., LLorca, J.: Prediction of the failure locus of C/PEEK composites under transverse compression and longitudinal shear through computational micromechanics. Compos. Sci. Technol. 68(15), 3128–3136 (2008)
Totry, E., González, C., LLorca, J.: Failure locus of fiber-reinforced composites under transverse compression and out-of-plane shear. Compos. Sci. Technol. 68(3), 829–839 (2008)
Vaughan, T.J., McCarthy, C.T.: Micromechanical modelling of the transverse damage behaviour in fibre reinforced composites. Compos. Sci. Technol. 71(3), 388–396 (2011)
Vaughan, T.J., McCarthy, C.T.: A micromechanical study on the effect of intra-ply properties on transverse shear fracture in fibre reinforced composites. Compos. A: Appl. Sci. Manuf. 42(9), 1217–1228 (2011)
O’Dwyer, D.J., O’Dowd, N.P., McCarthy, C.T.: Numerical micromechanical investigation of interfacial strength parameters in a carbon fibre composite material. J. Compos. Mater. 48(6), 749–760 (2014)
Romanowicz, M.: Progressive failure analysis of unidirectional fiber-reinforced polymers with inhomogeneous interphase and randomly distributed fibers under transverse tensile loading. Compos. A: Appl. Sci. Manuf. 41(12), 1829–1838 (2010)
Romanowicz, M.: Determination of the first ply failure load for a cross ply laminate subjected to uniaxial tension through computational micromechanics. Int. J. Solids Struct. 51(13), 2549–2556 (2014)
Yang, L., Yan, Y., Liu, Y.J., Ran, Z.G.: Microscopic failure mechanisms of fiber-reinforced polymer composites under transverse tension and compression. Compos. Sci. Technol. 72(15), 1818–1825 (2012)
Melro, A.R., Camanho, P.P., Pires, F.M.A., Pinho, S.T.: Micromechanical analysis of polymer composites reinforced by unidirectional fibres: Part II-Micromechanical analyses. Int. J. Solids Struct. 50(11), 1906–1915 (2013)
Arteiro, A., Catalanotti, G., Melro, A.R., Linde, P., Camanho, P.P.: Micro-mechanical analysis of the in situ effect in polymer composite laminates. Compos. Struct. 116, 827–840 (2014)
Melro, A.R., Camanho, P.P., Pires, F.M.A., Pinho, S.T.: Micromechanical analysis of polymer composites reinforced by unidirectional fibres: Part I-Constitutive modelling. Int. J. Solids Struct. 50(11), 1897–1905 (2013)
Canal, L.P., González, C., Segurado, J., LLorca, J.: Intraply fracture of fiber-reinforced composites: microscopic mechanisms and modeling. Compos. Sci. Technol. 72(11), 1223–1232 (2012)
Cid Alfaro, M.V., Suiker, A.S.J., De Borst, R.: Transverse failure behavior of fibre-epoxy systems. J. Compos. Mater. 44(12), 1493–1516 (2010)
Moës, N., Dolbow, N., Belytschko, T.: A finite element method for crack growth without remeshing. Int. J. Numer. Methods Eng. 46(1), 131–150 (1999)
Wells, G.N., Sluys, L.J.: A new method for modelling cohesive cracks using finite elements. Int. J. Numer. Methods Eng. 50(12), 2667–2682 (2001)
Belytschko, T., Gracie, R., Ventura, G.: A review of extended/generalized finite element methods for material modeling. Model. Simul. Mater. Sci. Eng. 17(4), 043001 (2009)
Bouhala, L., Makradi, A., Belouettar, S., Kiefer-Kamal, H., Fréres, P.: Modelling of failure in long fibres reinforced composites by X-FEM and cohesive zone model. Compos. Part B 55, 352–361 (2013)
Bieniaś, J., Dębski, H., Surowska, B., Sadowski, T.: Analysis of microstructure damage in carbon/epoxy composites using FEM. Comput. Mater. Sci. 64, 168–172 (2012)
Mollenhauer, D.H., Breitzman, T., Iarve, E.V., Hoos, K., Swindeman, M., Zhou, E.: Simulation of Mode I fracture at the micro-level in polymer matrix composite laminate plies. In: Proceedings of the 53rd AIAA/ASME/ASCE/AHS/ASC structures, structural dynamics and materials Conference, Honolulu, HI, AIAA 2012–1651 (2012)
Soden, P.D., Hinton, M.J., Kaddour, A.S.: Lamina properties, lay-up configurations and loading conditions for a range of fibre-reinforced composite laminates. Compos. Sci. Technol. 58(7), 1011–1022 (1998)
Yang, L., Yan, Y., Ran, Z.G., Liu, Y.J.: A new method for generating random fibre distributions for fibre reinforced composites. Compos. Sci. Technol. 76, 14–20 (2013)
van der Sluis, O., Schreurs, P.J.G., Brekelmans, W.A.M., Meijer, H.E.H.: Overall behaviour of heterogeneous elastoviscoplastic materials: effect of microstructural modelling. Mech. Mater. 32(8), 449–462 (2000)
Remmers, J.J., De Borst, R.E., Needleman, A.: The simulation of dynamic crack propagation using the cohesive segments method. J. Mech. Phys. Solids 56(1), 70–92 (2008)
Abaqus User’s manual
Fang, X.J., Yang, Q.D., Cox, B.N., Zhou, Z.Q.: An augmented cohesive zone element for arbitrary crack coalescence and bifurcation in heterogeneous materials. Int. J. Numer. Methods Eng. 88(9), 841–861 (2011)
Tay, T.E., Sun, X.S., Tan, V.B.C.: Recent efforts toward modeling interactions of matrix cracks and delaminations: an integrated XFEM-CE approach. Adv. Compos. Mater. 23(5–6), 391–408 (2014)
Zhao, L.B., Gong, Y., Qin, T.L., Mehmood, S., Zhang, J.Y.: Failure prediction of out-of-plane woven composite joints using cohesive element. Compos. Struct. 106, 407–416 (2013)
Zhao, L.B., Gong, Y., Zhang, J.Y., Chen, Y.L., Fei, B.J.: Simulation of delamination growth in multidirectional laminates under mode I and mixed mode I/II loadings using cohesive elements. Compos. Struct. 116, 509–522 (2014)
Varna, J., Berglund, L.A., Ericson, M.L.: Transverse single-fibre test for interfacial debonding in composites: 2. Modelling. Compos. A: Appl. Sci. Manuf. 28(4), 317–326 (1997)
Hobbiebrunken, T., Hojo, M., Adachi, T., De Jong, C., Fiedler, B.: Evaluation of interfacial strength in CF/epoxies using FEM and in-situ experiments. Compos. A: Appl. Sci. Manuf. 37(12), 2248–2256 (2006)
Zhou, X.F., Wagner, H.D., Nutt, S.R.: Interfacial properties of polymer composites measured by push-out and fragmentation tests. Compos. A: Appl. Sci. Manuf. 32(11), 1543–1551 (2001)
Soni, G., Singh, R., Mitra, M., Falzon, B.G.: Modelling matrix damage and fibre-matrix interfacial decohesion in composite laminates via a multi-fibre multi-layer representative volume element (M2RVE). Int. J. Solids Struct. 51(2), 449–461 (2014)
Romanowicz, M.: Effect of interfacial debonding on the failure behavior in a fiber-reinforced composite subjected to transverse tension. Comput. Mater. Sci. 47(1), 225–231 (2009)
O’Dwyer, D.J., O’Dowd, N.P., McCarthy, C.T.: Micromechanical investigation of damage processes at composite-adhesive interfaces. Compos. Sci. Technol. 86, 61–69 (2013)
Acknowledgments
The research work is supported by the National Science Foundation of China (11372020).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhi, J., Zhao, L., Zhang, J. et al. A Numerical Method for Simulating the Microscopic Damage Evolution in Composites Under Uniaxial Transverse Tension. Appl Compos Mater 23, 255–269 (2016). https://doi.org/10.1007/s10443-015-9459-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10443-015-9459-y