Abstract
Hybrid materials based on polymethylphenylsiloxane (PMPS) and organic functionalized silica were synthesized via condensation reaction between silanol and alkoxysilyl groups in the presence of quaternary ammonium hydroxide. The structure of prepared materials was investigated by FTIR and NMR, which indicate that the products have incorporated modified silica into the polymer matrix. The prepared hybrid materials show a satisfactory thermal resistance because the initial decomposition of typical product occurred at nearly 100 K higher than that of the pure polymer according to the thermogravimetric analysis (TGA) results. Differential thermogravimetric analysis (DTGA) data confirm that the thermal degradation of prepared hybrid materials comprises of two steps, of which the first one could be controlled by adjusting the content of silica particles and the ratio of surface groups on the particles. The coating films obtained from hybrid products exhibit good thermal mechanical properties. Therefore, the materials are hoped to be used for the application in thermal resistant coating.
Similar content being viewed by others
References
Sun, J., Huang, Y., Cao, H. and Gong, G., Polym. Degrad. Stab., 2004, 85: 725
Jia, M., Wu, C., Li, W. and Gao, D., J. Appl. Polym. Sci., 2009, 114: 971
Patel, M. and Swain, A.C., Polym. Degrad. Stab., 2004, 83: 539
Patel, M., Swain, A.C., Cunningham, J.L., Maxwell, R.S. and Chinn, S.C., Polym. Degrad. Stab., 2006, 91: 548
Kickelbick, G., “Hybrid materials”, WILEY-VCH, Weinheim, 2007
Canto, C.F., Prado, L.A.S.de A., Radovanovic, E. and Yoshida, I.V.P., Polym. Eng. & Sci., 2008, 48: 141
Ivanković, M., Brnardić, I., Ivanković, H., Huskić, M. and Gajović, A., Polymer, 2009, 50: 2544
Chen, G., Liu, G., Yao, J. and Du, N., Biaomian Jishu (in Chinese), 2008, 37: 47
Huang, K.Y., Weng, C.J., Lin, S.Y., Yu, Y.H. and Yeh, J.M., J. Appl. Polym. Sci., 2009, 112: 1933
Radhakrishnan, S., Siju, C.R., Mahanta, D., Patil, S. and Madras, G., Electrochim. Acta, 2009, 54: 1249
Weng, C.J., Huang, J.Y., Huang, K.Y., Jhuo, Y.S., Tsai, M.H. and Yeh, J.M., Electrochim. Acta, 2010, 55: 8430
Yeh, J., Weng, C., Liao, W. and Mau, Y., Surface and Coatings Technology, 2006, 201: 1788
Yan, W., Li, W. and Chen, J., Huagong Xuebao (in Chinese), 2002, 53: 45
Duo, S., Li, M., Zhu, M. and Zhou, Y., Mater. Chem. Phys., 2008, 112: 1093
Hu, L., Li, M. and Zhou, Y., J. Mater. Sci. Technol. (in Chinese), 2009, 25: 483
Wang, H., Xiong, X., Wang, C. and Shi, T., Polym Mater. Sci. Eng., 1999, 15: 92
McCarthy, D.W., Mark, J.E., Clarson, S.J. and Schaefer, D.W., J. Polym. Sci. B: Polym. Phys., 1998, 36: 1191
McCarthy, D.W., Mark, J.E. and Schaefer, D.W., J. Polym. Sci. B: Polym. Phys., 1998, 36: 1167
Pires de Souza, M.E., Ariza, E., Ballester, M., Yoshida, I.V.P., Rocha, L.A. and Freire, C.M.d.A., Mater. Res. Sao Carlos, Braz., 2006, 9: 59
Guibergia-Pierron, M. and Sauvet, G., Eur. Polym. J., 1992, 28: 29
Jost, C., Kuhnle, A., Cornelis, H. and Abbenhuis, L., 2005, U.S. Pat., 20050010012
Jones, R.G., Wataru, A. and Chojnowski, J., “Silicon-containing polymers: the science and technology of their synthesis and applications”, Kluwer Academic/Springer, Berlin, 2000
Author information
Authors and Affiliations
Corresponding author
Additional information
This work was financially supported by the Open Fund from State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology.
Rights and permissions
About this article
Cite this article
Gao, Dh., Jia, Mq. & Luo, Y. Crosslinked organosiloxane hybrid materials prepared by condensation of silanol and modified silica: Synthesis and characterization. Chin J Polym Sci 31, 974–983 (2013). https://doi.org/10.1007/s10118-013-1289-5
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10118-013-1289-5