IR spectroelectrochemical studies of Fe₂V₄O₁₃, FeVO₄ and InVO₄ thin films obtained via sol-gel synthesis

Abstract.

In this paper we generalize the IR spectroscopic properties of M³⁺VO₄ (M=Fe, In) orthovanadate and Fe₂V₄O₁₃ films. The films were prepared using the sol-gel synthesis route from M³⁺ nitrates and vanadium oxoisopropoxide. The vibrational bands in the IR absorbance spectra of the films are classified in terms of terminal V-O stretching (1050–880 cm^–1), bridging V-O^...Fe and V^...O^...Fe stretching (880–550 cm^–1), mixed V-O-V deformations and Fe-O stretching (<550 cm^–1) modes. Ex situ IR spectra of films were measured after consecutive charging/discharging to various intercalation coefficients x and correlated to the current peaks in the cyclic voltammetry curves measured in 1 M LiClO₄/propylene carbonate electrolyte. We classified the ex situ IR spectra of charged/discharged films according to their vibrational band changes. The results reveal that, for small values of the intercalation coefficient, crystalline FeVO₄, InVO₄ and Fe₂V₄O₁₃ films exhibit a simultaneous decrease in the intensity of all IR bands while the band frequencies remain unaffected. For the higher intercalation levels, IR mode frequencies are shifted, signaling the presence of reduced vanadium. Further charging leads to an amorphization of the film structure, which was established from the similarity of the IR spectra of charged films with those of amorphous films prepared at lower annealing temperatures. The results confirm that ex situ IR spectroelectrochemical measurement is an effective way to assess the structural changes in films with different levels of intercalation.