Abstract
Inorganic/organic composite membranes have been prepared from polybenzimidazole and two different heteropolyacids; namely phosphotungstic acid and silicotungstic acid. The membranes were characterized using SEM, XRD, and proton conductivity. The conductivity of the composite membrane was relatively high when compared to PBI membrane. The fuel cell performance with the composite membranes doped with phosphoric acid was investigated using hydrogen. It was found that pre-treatment of PWA and SiWA influenced the fuel cell performance and that the performance was enhanced with the use of the composite membrane. However, from the electrode polarization and crossover current data it was revealed that the expected high performance of the fuel cell was not achieved because of voltage losses associated with contact resistance and poor ionic conductivity in the catalyst layer. The best performance of the fuel cell was achieved with a 40% SiWA/PBI composite membrane.
Similar content being viewed by others
References
Lobato J, Canizares P, Rodrigo MA, Linares JJ, Aguilar JA (2007) J Membr Sci 306:47, doi:10.1016/j.memsci.2007.08.028
Scott K, Pilditch S, Mamlouk M (2007) J Appl Electrochem 37:1245, doi:10.1007/s10800-007-9414-1
Li M, Shao Z, Scott K (2008) J Power Sources 183:69, doi:10.1016/j.jpowsour.2008.04.093
Chen D, Zhang Q, Wang G, Zhang H, Li J (2007) Electrochem Comm 9:2755
Hatakeyama K, Sakaguchi H, Ogawa K, Inoue H, Iwakura C, Esaka T (2003) J Power Sources 124:559, doi:10.1016/S0378-7753(03)00741-9
Lakshmi N, Chandra S (2002) J Power Sources 108:256, doi:10.1016/S0378-7753(02)00021-6
Li Q, He R, Jensen JO, Bjerrum NJ (2003) Chem Mater 15:4896, doi:10.1021/cm0310519
Staiti P, Minutoli MJ (2001) J Power Sources 94:9, doi:10.1016/S0378-7753(00)00597-8
Staiti P, Hocevar S, Giordano N (1997) Int J Hydrogen Energy 22:809, doi:10.1016/S0360-3199(96)00222-4
He R, Li Q, Xiao G, Bjerrum NJ (2003) J Membr Sci 226:169, doi:10.1016/j.memsci.2003.09.002
Zhang H, Pang JH, Li A, Li X, Jiang Z (2005) J Membr Sci 264:56, doi:10.1016/j.memsci.2005.04.021
Staiti P (2001) Mater Lett 47:241, doi:10.1016/S0167-577X(00)00241-X
Staiti P, Minutoli M, Hocevar S (2000) J Power Sources 90:231, doi:10.1016/S0378-7753(00)00401-8
Lobato J, Canizares P, Rodrigo MA, Linares JJ, Manjavacas G (2006) J Membr Sci 280:351, doi:10.1016/j.memsci.2006.01.049
Yamazaki Y, Jang MY, Taniyama T (2004) Sci Technol Adv Mater 5:455, doi:10.1016/j.stam.2004.02.005
Jang MY, Yamakazi Y (2004) Solid State Ion 167:107, doi:10.1016/j.ssi.2003.12.003
Lobato J, Canizares P, Rodrigo MA, Linares JJ (2007) Electrochim Acta 52:3910, doi:10.1016/j.electacta.2006.11.014
M Mamlouk PhD thesis Newcastle University
Acknowledgment
The authors gratefully acknowledge the British Council for the UK India Education and Research Initiative (UKIERI) Research Fellowship to Dr. Anil Verma (IIT Guwahati) for carrying the research work at Newcastle University, UK and Dr. M Mamlouk for useful technical discussion.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Verma, A., Scott, K. Development of high-temperature PEMFC based on heteropolyacids and polybenzimidazole. J Solid State Electrochem 14, 213–219 (2010). https://doi.org/10.1007/s10008-008-0678-0
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10008-008-0678-0