Single crystals of the indide Er2.30(1)Ni1.84(1)In0.70(1) were isolated from an arc-melted sample of the initial composition 5Er:2Ni:1In. Er2.30Ni1.84In0.70 crystallizes with a new superstructure of the Mo2FeB2 type: P4/m, a = 738.6(2), c = 361.4(1) pm, wR2 = 0.0393, 487 F 2 values, 22 variables, BASF = 0.500(3) (meroedric twin matrix 010 100 00\(\bar(1)\)). The structure may be described as an intergrowth variant of slightly distorted AlB2 and CsCl related slabs. Formation of the superstructure results in two crystallographically independent sites 1a and 1c that center the CsCl slab. These sites have different size and they are occupied by 90% In + 10% Er (1c) and 51% In + 49% Er (1a), respectively. The crystal chemical consequences are discussed on the basis of a group-subgroup scheme.
Similar content being viewed by others
References
W Rieger H Nowotny F Benesovsky (1964) Monatsh Chem 95 1502 Occurrence Handle1:CAS:528:DyaF2MXkslOisA%3D%3D
WH Zachariasen (1949) Acta Crystallogr 2 94 Occurrence Handle1:CAS:528:DyaH1MXjsF2isw%3D%3D
K Remsching T Le Bihan H Noël P Rogl (1992) J Solid State Chem 97 391
M Lukachuk R Pöttgen (2003) Z Kristallogr 218 767 Occurrence Handle1:CAS:528:DC%2BD2cXmvFSmtA%3D%3D Occurrence Handle10.1524/zkri.218.12.767.20545
R Kraft R Pöttgen (2004) Monatsh Chem 135 1327 Occurrence Handle1:CAS:528:DC%2BD2cXptlygt70%3D
R Kraft R Pöttgen (2005) Monatsh Chem 136 1707 Occurrence Handle10.1007/s00706-005-0365-0 Occurrence Handle1:CAS:528:DC%2BD2MXhtVGntrnK
P Gravereau F Mirambet B Chevalier F Weill L Fournès D Laffargue F Bourrée J Etourneau (1994) J Mater Chem 4 1893 Occurrence Handle10.1039/jm9940401893 Occurrence Handle1:CAS:528:DyaK2MXivVaku74%3D
R Pöttgen (1994) Z Naturforsch 49b 1309
M Lukachuk YaM Kalychak R Pöttgen (2004) Z Naturforsch 59b 893
M Lukachuk YaM Kalychak M Dzevenko R Pöttgen (2005) J Solid State Chem 178 1247 Occurrence Handle1:CAS:528:DC%2BD2MXivFOhsrc%3D
R Pöttgen Th Gulden A Simon (1999) GIT Labor-Fachzeitschrift 43 133
K Yvon W Jeitschko E Parthé (1977) J Appl Crystallogr 10 73 Occurrence Handle10.1107/S0021889877012898
Wondratschek H, Müller U (2004) International Tables for Crystallography, Vol A1: Symmetry relations between space groups. Kluwer, Dordrecht
H Bärnighausen (1980) Commun Math Chem 9 139
Bärnighausen H, Müller U (1996) Symmetriebeziehungen zwischen den Raumgruppen als Hilfsmittel zur straffen Darstellung von Strukturzusammenhängen in der Kristallchemie. University of Karlsruhe and University/GH Kassel
Sheldrick GM (1997) SHELXL-97, Program for Crystal Structure Refinement, University of Göttingen
YaM Kalychak VI Zaremba VM Baranyak Pyu Zavalii VA Bruskov LV Sysa OV Dmytrakh (1990) Izv Akad Nauk SSSR Neorg Mater 26 94 Occurrence Handle1:CAS:528:DyaK3cXhs12mt7Y%3D
Th Fickenscher UCh Rodewald D Niepmann R Mishra M Eschen R Pöttgen (2005) Z Naturforsch 60b 271
Donohue J (1974) The Structures of the Elements. Wiley, New York
Emsley J (1999) The Elements. Oxford University Press, Oxford
R Pöttgen R Dronskowski (1996) Z Anorg Allg Chem 622 355
Leineweber A, Nitsche H, Hlukhyy V, Hoffmann R-D, Pöttgen R (2005) Intermetallics (in press)
Rodewald UCh, Lukachuk M, Hoffmann R-D, Pöttgen R (2005) Monatsh Chem (in press)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Rodewald, U., Lukachuk, M., Heying, B. et al. The Indide Er2.30(1)Ni1.84(1)In0.70(1) – A New Superstructure of the U3Si2 Family. Monatsh. Chem. 137, 7–13 (2006). https://doi.org/10.1007/s00706-005-0409-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00706-005-0409-5