Phase Equilibria in the Ni–Al–W System at 900°C

Summary.

Multicomponent Ni-base alloys exhibit good mechanical properties even at elevated temperatures and they are widely used for industrial production of exertion-resistive parts of engines. These properties are mainly determined by the coexistence of a disordered γ matrix with a face centred cubic lattice and cuboidal domains of its ordered γ′ structure. Therefore it is useful to study phase equilibria in Ni-base systems, namely in the regions involving both mentioned phases. One of the conclusions of our recent work on Ni–Al–Cr–W system was a necessity of modification of selected thermodynamic parameters of the ternary Ni–Al–W subsystem in order to achieve a better agreement of our experimental observations with theoretical modelling. This involves new measurements of the microstructure of selected samples of the Ni–Al–W system at 900°C and the comparison of the results with existing literature data in order to confirm our conclusions on higher order system investigated before. It is a first step on the way to an assessment of the Ni–Al–W system, which has not been done before.