The surgical sheets that are currently used for congenital cardiovascular surgery have several drawbacks, including material deterioration, calcification, and pseudo-intimal proliferation resulting in hemodynamic disturbance. The aim of this study was to evaluate a newly developed sheet made from a combination of silk fibroin (SF) and a synthetic polymer, thermoplastic polyurethane (TPU), for surgical use.


The hybrid SF/TPU sheet was a non-woven fabric with nanofibers that was made using the electrospinning method. The mechanical properties of the SF/TPU sheet were characterized. To determine its biocompatibility, part of the wall of the canine descending aorta was replaced with a SF/TPU sheet as a patch. The patches were removed after 3 months and a histological examination was performed.


The flexibility, water permeability, and suture retention strength of the SF/TPU sheet were excellent and equivalent to those of existing sheets. The SF/TPU sheet had excellent handling properties and fit well into the vascular wall without needle hole bleeding. The histological examination revealed that the intimal tissue was restored well over the intraluminal surface of the explanted SF/TPU sheet, the absence of calcium deposition, and minimal inflammatory reaction, without signs of degradation.


The SF/TPU sheet had excellent mechanical properties and tissue biocompatibility. These favorable features and possible biodegradability of the SF portion warrant a long-term follow-up study.


Silk fibroin Polyurethane Electrospinning Surgical sheet Cardiovascular surgery 



We would like to express our sincere gratitude to Ms. Atsuko Ueda and to Ms. Madoka Omura for their careful management and surgery of the animal experiments in this study. This work is supported by a Scientific technique research promotion program of agriculture, forestry, fishery and food industry (26051A) from the Japanese Ministry of Agriculture, Forestry and Fisheries and a Grant-in-aid for Scientific Research (KAKENHI: 26462094 and 15H03020) from the Japanese Ministry of Education, Culture, Sports, Science and Technology Japan.

Compliance with ethical standards

Conflict of interest

The authors declare no conflicts of interest in association with the present study.


  1. 1.
    Martin P, Mahmood A, Smith SRG, Simms MH, Vohra RK. Randomized trial comparing quixil surgical sealant with kaltostat hemostatic dressing to control suture line bleeding after carotid endarterectomy with ePTFE patch reconstruction. World J Surg. 2005;29:1259–62.CrossRefGoogle Scholar
  2. 2.
    Hayabuchi Y, Mori K, Kitagawa T, Sakata M, Kagami S. Polytetrafluoroethylene graft calcification in patients with surgically repaired congenital heart disease: evaluation using multidetector-row computed tomography. Am Heart J. 2007;153:806.e1–8.CrossRefGoogle Scholar
  3. 3.
    Woo JS, Fishbein MC, Reemtsen B. Histologic examination of decellularized porcine intestinal submucosa extracellular matrix (CorMatrix) in pediatric congenital heart surgery. Cardiovasc Pathol. 2016;25(1):12 – 7.CrossRefPubMedGoogle Scholar
  4. 4.
    Iwai S, Sawa Y, Ichikawa H, Taketani S, Uchimura E, Chen C, et al. Biodegradable polymer with collagen microsponge serves as a new bioenginnered cardiovascular prosthesis. J Thorac Cardiovasc Surg. 2004;128:472–9.CrossRefPubMedGoogle Scholar
  5. 5.
    Moy RL, Lee A, Zalka A. Commonly used suture materials in skin surgery. Am Fam Physician. 1992;44:2123–8.Google Scholar
  6. 6.
    Hollander DH. Interstitial cystitis and silk allergy. Med Hypotheses. 1994;43:155–6.CrossRefPubMedGoogle Scholar
  7. 7.
    Nakazawa Y, Asakura T. Development of tissue engineering materials based on silk fibroin. Jpn J Silk Sci Tech. 2014;22:23–9. (Japanese).Google Scholar
  8. 8.
    Altman GH, Diaz F, Jakuba C, Calabro T, Horan RL, Chen J, et al. Silk based biomaterials. Biomaterials. 2003;24:401–16.CrossRefPubMedGoogle Scholar
  9. 9.
    Kim U-J, Park J, Kim HJ, Wada M, Kaplan DL. Three-dimensional aqueous-derived biomaterial scaffolds from silk fibroin. Biomaterials. 2005;26:2775–85.CrossRefPubMedGoogle Scholar
  10. 10.
    Ohgo K, Zhao C, Kobayashi M, Asakura T. Preparation of non-woven nanofibers of Bombyx mori silk, Samia cynthia ricini silk and recombinant hybrid silk with electrospinning method. Polymer. 2003;44:841–6.CrossRefGoogle Scholar
  11. 11.
    Shimada K, Higuchi A, Kubo R, Murakami T, Nakazawa Y, Tanaka R. The effect of a silk fibroin/polyurethane blend patch on rat vessels. Organogenesis. 2017;13(4):115–124.CrossRefPubMedGoogle Scholar
  12. 12.
    Nakazawa C, Higuchi A, Asano A. Solid-state NMR studies for the development of non-woven biomaterials based on silk fibroin and polyurethane. Polymer J. 2017;49:583–586.CrossRefGoogle Scholar
  13. 13.
    Tamada Y, Kobayashi K, Sumi N. Fibroin sponge safety evaluations (in Japanese). Jpn J Silk Sci Tech. 2015;23:71–3.Google Scholar
  14. 14.
    Nakazawa Y, Sato M, Takahashi R, Aytemiz D, Takabayashi C, Tamura T, et al. Development of small-diameter vascular grafts based on silk fibroin form Bombyx mori for vascular regeneration. J Biomater Sci Polym Ed. 2011;22:195–206.CrossRefPubMedGoogle Scholar
  15. 15.
    Enomoto S, Sumi M, Kajimoto K, Nakazawa Y, Takahashi R, Takabayashi C. Long-term patency of small-diameter vascular graft made from fibroin, a silk-based biodegradable material. J Vasc Surg. 2010;51:155–64.CrossRefPubMedGoogle Scholar
  16. 16.
    Szyche MR: Biostability of polyurethane elastomers: a critical review. J Biomater Appl 1988; 3:297–402.CrossRefGoogle Scholar
  17. 17.
    Stokes K, McVenes R, Anderson J. Polyurethane elastomer biostability. J Biomater Appl. 1995;9:321–54.CrossRefPubMedGoogle Scholar
  18. 18.
    Dan K, Molamma PP, Guorui J, Seeram R. Guided orientation of cardiomyocytes on electrospun aligned nanofibers for cardiac tissue engineering. J Biomed Mater Res Part B. 2011;98B:379–86.CrossRefGoogle Scholar
  19. 19.
    Vaz CM, van Tuijl S,.Bouten CV, Baaijens FP. Design of scaffolds for blood vessel tissue engineering using a multi-layering electrospinning technique. Acta Biomater. 2005;1(5):575–82.CrossRefPubMedGoogle Scholar
  20. 20.
    Nakazawa Y, Asano A, Nakazawa TC, Tsukatani T, Asakura T. Structural characterization of silk-polyurethane composite material for biomaterials using solid-state NMR. Polym J. 2012;44:802–7.CrossRefGoogle Scholar
  21. 21.
    Strange G, Brizard CP, Karl TR, Neethling L. An evaluation of Admedus’ tissue engineering process-treated (ADAPT) bovine pericardium patch (CardioCel) for the repair of cardiac and vascular defects. Expert Rev Med Devices. 2015;12(2):135–41.CrossRefPubMedGoogle Scholar
  22. 22.
    Nowocin AK, Southgate A, Gabe SM, Ansari T. Biocompatibility and potential of decellularized porcine small intestine to support cellular attachment and grow. J Tissue Eng Regen Med. 2016;10(1):E23–E33.CrossRefPubMedGoogle Scholar

Copyright information

© Springer Japan KK, part of Springer Nature 2017

Authors and Affiliations

  • Ryo Shimada
    • 1
  • Hayato Konishi
    • 1
  • Hideki Ozawa
    • 1
  • Takahiro Katsumata
    • 1
  • Ryou Tanaka
    • 2
  • Yasumoto Nakazawa
    • 3
  • Shintaro Nemoto
    • 1
  1. 1.Department of Thoracic and Cardiovascular SurgeryOsaka Medical CollegeTakatsukiJapan
  2. 2.Department of Surgery and Veterinary MedicineTokyo University of Agriculture and TechnologyKoganeiJapan
  3. 3.Department of Biotechnology and Life ScienceTokyo University of Agriculture and TechnologyKoganeiJapan

Personalised recommendations