Abstract
Diffusion rates for the three tetravalent cations U, Th and Hf have been measured in synthetic zircon. Diffusant sources included oxide powders and ground pre-synthesized silicates. Rutherford backscattering spectrometry (RBS) was used to measure depth profiles. Over the temperature range 1400–1650 °C, the following Arrhenius relations were obtained (diffusion coefficients in m2sec−1):
log D Th = (1.936 ± 0.9820) + (− 792 ± 34 kJ mol−1 /2.303 RT)
log D U = (0.212 ± 2.440) + (− 726 ± 83 kJ mol−1 /2.303 RT)
log D Hf = (3.206 ± 1.592) + (− 812 ± 54 kJ mol−1 /2.303 RT)
The data show a systematic increase in diffusivity with decreasing ionic radius (i.e., faster diffusion rates for Hf than for U or Th), a trend also observed in our earlier study of rare earth diffusion in zircon. Diffusive fractionation may be a factor in the Lu-Hf system given the much slower diffusion rates of tetravalent cations when compared with the trivalent rare earths. The very slow diffusion rates measured for these tetravalent cations suggest that they are essentially immobile under most geologic conditions, permitting the preservation of fine-scale chemical zoning and isotopic signatures of inherited cores.
Similar content being viewed by others
Author information
Authors and Affiliations
Additional information
Received: 12 July 1996 / Accepted: 2 December 1996
Rights and permissions
About this article
Cite this article
Cherniak, D., Hanchar, J. & Watson, E. Diffusion of tetravalent cations in zircon. Contrib Mineral Petrol 127, 383–390 (1997). https://doi.org/10.1007/s004100050287
Issue Date:
DOI: https://doi.org/10.1007/s004100050287