Abstract
In this work, isotactic polypropylene (iPP) composites filled with multiwalled carbon nanotubes (MWCNTs) were prepared by compounding iPP melt with MWCNT aqueous suspension using a corotating twin-screw extruder, and the morphology and crystallization behavior of the composites were investigated. Scanning electron microscopy micrographs showed that MWCNTs dispersed individually at nanoscale in the iPP matrix when the MWCNTs concentration was low, though MWCNTs aggregates were detected when the filler concentration increased. The results of differential scanning calorimetry, wide-angle X-ray diffraction, and polarized light microscopy indicated that the β-form crystal of iPP was induced by MWCNTs at the concentration of 0.1 wt.% which was dispersed individually in the iPP matrix. At higher content, however, MWCNTs acted as α-nucleating agent, and the crystals in the iPP/MWCNT composites showed higher degree of perfection than that of pure iPP though smaller in dimension. Crystallization rate of iPP increased significantly with increasing MWCNT content.
References
Chang TE, Jensen LR, Kisliuk A, Pipes RB, Pyrz R, Sokolov AP (2005) Polymer 46:439
Hou ZC, Wang K, Zhao P, Zhang Q, Ynag CY, Chen DQ, Du RN, Fu Q (2008) Polymer 49:3582
Grady BP, Pompeo F, Shambaugh RL, Resasco DE (2002) J Phys Chem B 106:5852
Bhattacharyya AR, Sreekumar TV, Liu T, Kumar S, Ericson LM, Hauge RH, Smalley RE (2003) Polymer 44:2373
Assouline E, Lusiger A, Barber AH, Cooper CA, Klein E, Wachtel E, Wagner HD (2003) J Polym Sci Part B Polym Phys 41:520
Valentini L, Biagiotti J, Kenny JM, Santucci S (2003) Compos Sci Technol 63:1149
Seo MK, Lee JR, Park S (2005) J Mater Sci Eng A 404:79
Leelapornpisit W, Ton-That M, Perrin-Sarazin F, Cole KC, Denault J, Simard B (2005) J Polym Sci Part B Polym Phys 43:2445
Avila-Orta CA, Medellín-Rodríguez FJ, Dávila-Podríguez MV, Aguirre-Figueroa YA, Yoon K, Hsiao BS (2007) J Appl Polym Sci 106:2640
Wu DF, Sun YR, Wu L, Zhang M (2008) J Appl Polym Sci 108:1506
Lee GW, Jagannathan S, Chae HG, Minus ML, Kumar S (2008) Polymer 49:1831
Bikiaris D, Vassiliou A, Chrissafis K, Pataskevopoulos KM, Jannakoudakis A, Docoslis A (2008) Polym Degrad Stab 93:952
McIntosh D, Khabashesku VN, Barrera EV (2006) Chem Mater 18:4561
McIntosh D, Khabashesku VN, Barrera EV (2007) J Phys Chem C 111:1592
Zhou Z, Wang S, Lu L, Zhang Y, Zhang Y (2007) J Polym Sci Part B Polym Phys 45:1616
Kelarakis A, Yoon K, Sics I, Somani RH, Chen XM, Hsiao BS, Chu B (2006) J Macromol Sci Part B 45:247
Ristolainen N, Vainio U, Paavola S, Torkkeli M, Serimaa R, Seppälä J (2005) J Polym Sci Part B Polym Phys 43:1892
Liu ZY, Yu RZ, Yang MB, Feng JM, Yang W, Yin B (2008) Front Chem Eng China 2:115
Li W, Liu ZY, Yang MB. J Appl Polym Sci (2008)
Li ZF, Luo GH, Zhou WP, Wei F, Xiang R, Liu YP (2006) Nanotechnology 17:3692
Marsh DH, Rance GA, Zaka MH, Whitby RJ, Khlobystoy AN (2007) Phys Chem Chem Phys 9:5490
Medellín-Rodríguez FJ, Mata-Padilla JM, Hsiao BS, Waldo-Mendoza MA, Ramírez-Vargas E, Sánchez-Valdes S (2007) Polym Eng Sci 47:1889
Acknowledgement
The authors gratefully acknowledge the financial support of this work by the National Natural Science Foundation Commission of China (grant number 10590351).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yin, CL., Liu, ZY., Yang, W. et al. Crystallization and morphology of iPP/MWCNT prepared by compounding iPP melt with MWCNT aqueous suspension. Colloid Polym Sci 287, 615–620 (2009). https://doi.org/10.1007/s00396-009-2016-1
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00396-009-2016-1