Gettering efficiencies for Cu and Ni as a function of size and density of oxygen precipitates in p/p- silicon epitaxial wafers

Abstract.

We have measured the gettering efficiencies for Cu and Ni in p/p-Si epitaxial wafers. The wafers were pretreated to obtain oxygen precipitates of different sizes and densities in the bulk. Gettering tests started with a reproducible spin-on spiking in the range of 10¹² atoms/cm², followed by thermal treatment to drive-in and redistribute the impurities in the wafer. Subsequently, the wafers were analyzed by a novel stratigraphical layer-by-layer etching technique in combination with inductively coupled plasma mass spectrometry. Gettering efficiencies for Ni did not depend on oxygen precipitate sizes and densities as long as ΔO_i was larger than 0.2×10¹⁷ atoms/cm³ and the bulk micro defect densities were detectable by preferential etching (10⁷ cm^-3). In these cases, gettering efficiencies were 96–99% for Ni, while wafers not containing any measurable BMDs exhibited no detectable gettering. Cu exhibited a more complex behavior because the total Cu contamination was found to be divided into two species, one mobile and the other immobile species. A dependence on BMD size and BMD density of the Cu distributions in the wafers was also detected. Gettering effects were increased with increasing BMD densities and sizes. For BMD densities <10⁹ cm^-3, Cu was not efficiently gettered by oxygen precipitates. Even for BMD densities >10¹⁰ cm^-3, gettering effects due to oxygen precipitates were one order of magnitude lower than in heavily boron-doped silicon.