Abstract.
Pb diffusion in α-Zr matrix between 823 and 1123 K was measured using heavy ion Rutherford backscattering spectrometry (HIRBS) technique. A deviation from the Arrhenius law was observed, with two different regions. At low temperatures the activation energy Q is close to the expected value for a substitutional diffuser but the pre-exponential factor D0 is higher than expected. Close to the phase transition temperature the opposite occurs, with a low Q value. This behavior is similar to the one observed for Hf and self-diffusion in α-Zr.