1 Correction to: Applied Physics A (2018) 124:428 https://doi.org/10.1007/s00339-018-1862-4
Dear readers,
The authors recently found a few mistakes in their published paper.
On page 6 of this paper.
The units of ‘Eb or E’ in Fig. 7b, Table 2 and Line 7 of paragraph 1 should be corrected as ‘V/cm’ instead of ‘kV/cm’.
Combining common sense with the results of Fig. 8b, it is easy to find that the units of ‘Eb or E’ mentioned above are uncorrect.
These errors do not alter the results or discussions. The authors express sincere apologies for any inconvenience caused.
-
1.
The abscissa unit of Fig. 7b should be corrected as E (V/cm) instead of E (kV/cm). Figure 7 is corrected in this corrigendum, as follows:
-
2.
The unit of Eb in Table 2 should be corrected as Eb (V/cm).
Table 2 is corrected in this corrigendum, as follows:
Sintering temperature/duration
x/duration
α
Eb (V/cm)
ρ (105 Ω m)
1020 °C/8 h
0.1/8 h
5.664
590.2
6.47
1040 °C/8 h
0.1/8 h
3.933
4248.7
32.9
1060 °C/8 h
0.05/8 h
4.209
473.6
0.45
1060 °C/8 h
0.1/8 h
3.012
90.2
0.40
1060 °C/8 h
0.15/8 h
4.112
109.9
0.22
1080 °C/8 h
0.1/8 h
3.269
184.3
1.88
-
3.
On Page 6, Line 7 of paragraph 1, the sentence ‘the minimum α (3.012), Eb (90.2 kV/cm) and nearly the lowest ρ (4 × 104 Ω m)’ should be corrected as ‘the minimum α (3.012), Eb (90.2 V/cm) and nearly the lowest ρ (4 × 104 Ω m)’.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Sun, L., Ni, Q., Guo, J. et al. Correction to: Dielectric properties and nonlinear I–V electrical behavior of (Li1+, Al3+) co-doped CaCu3Ti4O12 ceramics. Appl. Phys. A 125, 646 (2019). https://doi.org/10.1007/s00339-019-2908-y
Published:
DOI: https://doi.org/10.1007/s00339-019-2908-y