Abstract
Cu2ZnSnS4 (CZTS) thin films have been prepared via sol–gel method and deposited on ordinary glass substrates by dip-coating technique. The chemical composition of Cu/(Zn + Sn) ratio was varied between 0.85, 0.95 and 1.05 to study its effect on structural, optical, morphological, compositional and electrical properties of deposited films. The films were investigated using different techniques such as X-ray diffractometer (XRD), Raman spectroscopy, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), UV–vis spectrophotometer and four-point probe method. The X-ray diffraction showed the single kesterite phase with the preferential orientation along (112) plane. The crystallites size was found to be between 6.95 and 9.30 nm. Raman scattering measurements for CZTS films deposited at Cu/(Zn + Sn) equal to 0.85 and 1.05 were confirmed the presence of pure CZTS phase by the characteristic peak at 332 cm−1. The morphological properties show a dense surface morphology and the elemental composition indicates CZTS films with a near-stoichoimetric composition. The optical properties were calculated using transmittance and absorbance data in the wavelength range between 450 and 850 nm. The obtained band gap energy values were found to be between 1.41 and 1.47 eV. The electrical sheet resistance showed values between 0.68 and 1.07 × 103 Ω square−1. A best sheet resistance and favorable optical band gap make our dip-coated CZTS thin films suitable to be used as an absorber layer for photovoltaic applications.
Similar content being viewed by others
References
P. Jackson, D. Hariskos, E. Lotter, S. Paetel, R. Wuerz, R. Menner, W. Wischmann, M. Powalla, Appl. 19, 894–897 (2011)
M. Ganchev, L. Kaupmees, J. Iliyna, J. Raudoja, O. Volobujeva, H. Dikov, M. Altosaar, E. Mellikov, T. Varema, Energy Proc. 2, 65–70 (2010)
A. Walsh, S. Chen, S.-H. Wei, X.-G. Gong, Adv. Energy Mater. 2, 400–409 (2012)
C. Wadia, A.P. Alivisatos, D.M. Kammen, Environ. Sci. Technol. 43, 2072 (2009)
D.B. Mitzi, L.L. Kosbar, C.E. Murray, M. Copel, A. Afzali, Nature 428, 299 (2004)
D.B. Mitzi, M. Yuan, W. Liu, A.J. Kellock, S.J. Chey, V. Deline, A.G. Schrott, Adv. Mater. 20, 3657 (2008)
H. Katagiri, N. Sasaguchi, S. Hando, S. Hoshino, J. Ohashi, T. Yokota, Sol. Energy Mater. Sol. Cells 49, 407–414 (1997)
T. Kobayashi, K. Jimbo, K. Tsuchida, S. Shinoda, T. Oyanagi, H. Katagiri, Jpn. J. Appl. Phys. 44, 783–787 (2005)
H. Katagiri, Cu2ZnSnS4 thin film solar cells. Thin Solid Films 480–481, 426–432 (2005)
H. Katagiri, K. Jimbo, S. Yamada, T. Kamimura, W.S. Maw, T. Fukano, T. Ito, T. Motohiro, Appl. Phys. Express 1(2), 041201 (2008) (2pp)
H. Katagiri, K. Jimbo, W.S. Maw, K. Oishi, M. Yamazaki, H. Araki, A. Takeuchi, Thin Solid Films 517, 2455–2460 (2009)
T.K. Todorov, K.B. Reuter, D.B. Mitzi, Adv. Mater. 22, 156 (2010)
K. Tanaka, M. Oonuki, N. Moritake, H. Uchiki, Sol. Energy Mater. Sol. Cells 93, 583 (2009)
Z. Zhou, Y. Wang, D. Xu, Y. Zhang, Sol. Energy Mater. Sol. Cells 94, 2042 (2010)
K. Tanaka, N. Moritake, H. Uchiki, Sol. Energy Mater. Sol. Cells 91, 1199 (2007)
Y. Miyamoto, K. Tanaka, M. Oonuki, N. Moritake, H. Uchiki, Jpn. J. Appl. Phys. 1, 596 (2008)
T.K. Todorov, M. Kita, J. Carda, P. Escribano, Thin Solid Films 517, 2541 (2009)
N. Moritake, Y. Fukui, M. Oonuki, K. Tanaka, H. Uchiki, Phys. Status Solidi (c) 6, 1233 (2009)
K. Tanaka, K. Moritake, M. Oonuki, H. Uchiki, Jpn. J. Appl. Phys. 47, 598 (2008)
H.J. Tchognia Nkuissi, B. Hartiti, Micro and Nano Technologies, chap. 44 (Elsevier, 2018), pp. 799–828
K. Todorov, K.B. Reuter, D.B. Mitzi, Adv. Mater. 22(20), E156–E159 (2010)
D.A.R. Barkhouse, O. Gunawan, T. Gokmen, T.K. Todorov, D.B. Mitzi, Prog. Photovolt. Res. Appl. 20, 6–11 (2012)
T.K. Todorov, J. Tang, S. Bag, O. Gunawan, T. Gokmen, Y. Zhu, D.B. Mitzi, Adv. Energy Mater. 3, 34–38 (2013)
W. Wang, M.T. Winkler, O. Gunawan, T. Gokmen, T.K. Todorov, Y. Zhu, D.B. Mitzi, Adv. Energy Mater. 4, 1–5 (2014)
P. Prabeesh, P. Saritha, I. Packia Selvam, S.N. Potty, Mater. Res. Bull. 86, 295–301 (2017)
F. Aslan, A. Gökta, A. Tumbul, Mater. Sci. Semicond. Process. 43, 139–143 (2016)
M. Faustini, B. Louis, P.A. Albouy, M. Kuemmel, D. Grosso, J. Phys. Chem. C 114, 7637–7645 (2010)
S.A. Khalate, R.S. Kate, J.H. Kim, S.M. Pawar, R.J. Deokate, Superlattices Microstruct. 103, 335–342 (2017)
H. Park, Y. Hwan, B.-S. Bae, J. Sol-Gel. Sci. Technol. 65, 23–27 (2013)
R. Moreno, E.A. Ramirez, G.G. Guzmán, J. Phys. Conf. Ser. 687, 012041 (2016)
S. Kahraman, S. Çetinkaya, H.A. Çetinkara, H.S. Güder, Thin Solid Films 550, 36–39 (2014)
A.-S. Gadallah, M.M. El-Nahass, Cond. Matter Phys. 2013, 234546 (2013)
J. He, L. Sun, Y. Chen, J. Jiang, P. Yang, J. Chu, RSC Adv. 4, 43080 (2014)
S. Chen, X.G. Gong, A. Walsh, S.-H. Wei, Appl. Phys. Lett. 94, 041903 (2009)
P.A. Fernandes, P.M.P. Salomé, A.F. da Cunha, Thin Solid Films 517, 2519–2523 (2009)
Y.-L. Zhou, W.-H. Zhou, M. Li, Y.-F. Du, S.-X. Wu, J. Phys. Chem. C 115, 19632–19639 (2011)
Z. Guan, W. Luo, Z. Zou, Cryst Eng Commun. 16, 2929 (2014)
F. Biccari, R. Chierchia, M. Valentini, P. Mangiapane, E. Salza, C. Malerba, C.L. Azanza Ricardo, L. Mannarino, P. Scardi, A. Mittig, Energy Proc. 10, 187–191 (2011)
P.A. Fernandes, P.M.P. Salom, A.F. da Cunha, J. Alloys Compd. 509(28), 7600–7606 (2011)
P.R. Ghediya, T.K. Chaudhuri, J. Phys. D Appl. Phys. 48, 455109 (2015) (9pp)
T. Truong Mau, H. Kim, J. Ceram. Process. Res. 13(3), 301–304 (2012)
D. Seo, S. Lim, J. Mater. Sci. Mater. Electron. N.Y. 24(10), 3756–3763 (2013)
J.P. Leitão, N.M. Santos, P.A. Fernandes, P.M.P. Salomé, A.F. da Cunha, J.C. González, F.M. Matinaga, Thin Solid Films 519, 7390–7393 (2011)
J. Tauc, R. Grigorovici, A. Vancu, Optical properties and electronic structure of amorphous germanium. Phys. Stat. Sol. 15, 627–637 (1966)
D. Seo, C. Kim, E. Oh, C.W. Hong, J.H. Kim, S. Lim, J Mater Sci. Mater Electron. 25(8), 3420–3426 (2014)
N. Vipul Kheraj, K.K. Patel, S.J. Patel, D.V. Shah, J. Cryst. Growth 362, 174–177 (2013)
T. Zdanowicz, T. Rodziewicz, M. Zabkowska-Waclawek, Sol. Energy Mater. Sol. Cells 87, 757–769 (2005)
G. Suresh Babu, Y.B. Kishore Kumar, P. Uday Bhaskar, S.R. Vanjari, Solar Energy Mater. Solar Cells 94, 221–226 (2010)
K. Maeda. K. Tanaka. Y. Fukui. H. Uchiki, Sol. Energy Mater. Sol. Cells 95, 2855 (2011)
S. Nakamura, T. Meada, T. Wada, Phys. Status Solid C 6, 1261 (2009)
J. Paier, R. Asahi, A. Nagoya, G. Kresse, Phys. Rev. B 79, 115126 (2009)
M. Cao, Y. Shen, J. Cryst. Growth 318, 1117 (2011)
D. Seo, S. Lim, J. Mater. Sci. Mater. Electron. 24, 3756–3763 (2013)
R.R. Ddy, M. Rai Kumar, T.V.R. Rao, lirfrarcd Phys. 34(1), 9SW (1993)
S. Ahmad, M. Mohib-ul Haq, Iran. J. Phys. Res. 14(3), 89–93 (2014)
K.R. Nemade, S.A. Waghuley, Int. J. Metals 2014, 389416 (2014)
K. Sangwal, Kucharczyk “Relationship between density and refractive index of inorganic solids”. J. Phys. D: Appl. Phys. 20, 522 (1987) and W.
I.S. Babichuk, V.O. Yukhymchuk, M.O. Semenenko, N.I. Klyui, R. Caballero, O.M. Hreshchuk, I.S. Lemishko, I.V. Babichuk, V.O. Ganus, M. Leon, Semicond. Phys. Quantum Electron. Optoelectron. 17(3), 284–290 (2014)
R. Hosseinpour, M. Izadifard, M.E. Ghazi, B. Bahramian, J. Electr. Mater. 47(2), 1080–1090 (2018)
K. Punitha, R. Sivakumar, C. Sanjeeviraja, J. Appl. Phys. 115, 113512 (2014)
K. Sharma, A.S. Al-Kabbi, G.S.S. Saini, S.K. Tripathi, Mater. Res. Bull. 47, 1400–1406 (2012)
H. Padma Kumar, S. Vidya, S. Saravana Kumar, C. Vijayakumar, S. Solomonb, J.K. Thomas, J. Asian Ceram. Soc. 3, 64–69 (2015)
E.A. Davis, N.F. Mott, J. Theor. Exp. Appl. Phys. 22(179), 903–922 (1970)
J. Henry, K. Mohanraj, G. Sivakumar, J. Asian Ceram. Soc. 4, 81–84 (2016)
W. Daranfed, M.S. Aida, N. Attaf, J. Bougdira, H. Rinnert, J. Alloy. Compd. 542, 22–27 (2012)
L. Majula, N.R. Mlyuka, M.E. Samiji, J. Korean Phys. Soc. 67(6), 1078–1081 (2015)
Acknowledgements
Prof. Bouchaib HARTITI, Senior Associate at ICTP (The Abdus Salam International Centre for Theoretical Physics) is very grateful to ICTP for financial support. Technical support from LMOPS (University of Lorraine, France) and Kamal ABDERRAFI is also acknowledged.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Ziti, A., Hartiti, B., Labrim, H. et al. Effect of copper concentration on physical properties of CZTS thin films deposited by dip-coating technique. Appl. Phys. A 125, 218 (2019). https://doi.org/10.1007/s00339-019-2513-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s00339-019-2513-0