Abstract
We report the growth of vertically aligned carbon nanotube bundles on Si substrate by thermal chemical vapor deposition technique. Vertical alignment was achieved without any carrier gas or lithography-assisted deposition. Growth has been carried out at 850 °C for different quantities of solution of xylene and ferrocene ranging from 2.25 to 3.00 ml in steps of 0.25 ml at a fixed concentration of 0.02 gm (ferrocene) per ml. To understand the growth mechanism, deposition was carried out for different concentrations of the solution by changing only the ferrocene quantity, ranging from 0.01 to 0.03 gm/ml. A tunable vertical alignment of multi-walled carbon nanotubes (CNTs) has been achieved by this process and examined by scanning and transmission electron microscopic techniques. Micro-crystalline structural analysis has been done using Raman spectroscopy. A systematic variation in field emission (FE) current density has been observed. The highest FE current density is seen for the film grown with 0.02 gm/ml concentration, which is attributed to the better alignment of CNTs, less structural disorder and less entanglement of CNTs on the surface. The alignment of CNTs has been qualitatively understood on the basis of self-assembled catalytic particles.
Similar content being viewed by others
References
S. Iijima, Helical microtubules of graphitic carbon. Nature 354, 56–58 (1991)
M.-F. Yu, O. Lourie, M.J. Dyer, K. Moloni, T.F. Kelly, R.S. Ruoff, Strength and breaking mechanism of multi-walled carbon nanotubes under tensile load. Science 287, 637–640 (2000)
H. Dai, E.W. Wong, C.M. Lieber, Probing electrical transport in nanomaterials: conductivity of individual carbon nanotubes. Science 272, 523–526 (1999)
J. Hone, M. Whitney, A. Zettl, Thermal conductivity of single-walled carbon nanotubes. Synth. Met. 103, 2498–2499 (1999)
X.S. Wang, Q.Q. Li, J. Xie, Z. Jin, J.Y. Wang, Y. Li et al., Fabrication of ultralong and electrically uniform single-walled carbon nanotubes on clean substrates. Nano Lett. 9, 3137–3141 (2009)
R.Q. Yu, L.W. Chen, Q.P. Liu, J.Y. Lin, K.L. Tan, S.C. Ng et al., Platinum deposition on carbon nanotubes via chemical modification. Chem. Mater. 10, 718–722 (1998)
R. Chau, B. Doyle, S. Datta, J. Kavalieros, K. Zhang, Integrated nanoelectronics for the future. Nat. Mater. 6, 810–812 (2007)
W.A. de Heer, A. Chatelain, D. Ugarte, A carbon nanotube field emission electron source. Science 270, 1179–1180 (1995)
J.M. Bonard, M. Croci, C. Klinke, R. Kurt, O. Noury, N. Weiss, Carbon nanotube films as electron field emitters. Carbon 40, 1715–1728 (2002)
J.-M. Bonard, K.A. Dean, B.F. Coll, C. Klinke, Field emission of individual carbon nanotubes in the scanning electron microscope. Phys. Rev. Lett. 89, 197602–19761-4 (2002)
K.B.K. Teo, E. Minoux, L. Hudanski, F. Peauger, J.-P. Schnell, L. Gangloff et al., Microwave devices: carbon nanotubes as cold cathodes. Nature 437, 968–968 (2005)
Y. Chen, D.T. Shaw, X.D. Bai, E.G. Wang, C. Lund, W.M. Lu et al., Hydrogen storage in aligned carbon nanotubes. Appl. Phys. Lett. 78, 2128–2130 (2001)
J.M. Bonard, T. Stöckli, O. Noury, A. Chatelain, Field emission from cylindrical carbon nanotube cathodes: possibilities for luminescent tubes. Appl. Phys. Lett. 78, 2775–2777 (2001)
J.Q. Wei, Y. Jia, Q.K. Shu, Z.Y. Gu, K.L. Wang, D.M. Zhuang et al., Double-walled carbon nanotube solar cells. Nano Lett. 7, 2317–2321 (2007)
L. Valentini, I. Armentano, J.M. Kenny, C. Cantalini, L. Lozzi, S. Santucci, Sensors for subppm NO2 gas detection based on carbon nanotube thin films. Appl. Phys. Lett. 82, 961–963 (2003)
J.V. Veetil, K. Ye, Tailored carbon nanotubes for tissue engineering applications. Biotechnol. Prog. 25, 709–721 (2009)
W.Z. Li, S.S. Xie, L.X. Qian, B.H. Chang, B.S. Zou, W.Y. Zhou et al., Large-scale synthesis of aligned carbon nanotubes. Science 274, 1701–1703 (1996)
Y.H. Wang, J. Lin, C.H.A. Huan, G.S. Chen, Synthesis of large area aligned carbon nanotube arrays from C2H2-H2 mixture by rf plasma-enhanced chemical vapor deposition. Appl. Phys. Lett. 79, 680–682 (2001)
R. Patra, S. Ghosh, E. Sheremet, M. Jha, R.D. Rodriguez, D. Lehmann et al., Enhanced field emission from cerium hexaboride coated multiwalled carbon nanotube composite films: a potential material for next generation electron sources. J. Appl. Phys. 115, 094302 (2014)
C.D. Scott, S. Arepalli, P. Nikolaev, R.E. Smalley, Growth mechanisms for single-wall carbon nanotubes in a laser-ablation process. Appl. Phys. A 72, 573–580 (2001)
P.M. Ajayan, O. Stephan, C. Colliex, D. Trauth, Aligned carbon nanotube arrays formed by cutting a polymer resin-nanotube composite. Science 265, 1212–1214 (1994)
W.A. de Heer, W.S. Bacsa, A. Châtelain, T. Gerfin, R. Humphrey-Baker, L. Forro et al., Aligned carbon nanotube films: production and optical and electronic properties. Science 268, 845–847 (1995)
T. Kyotani, L.-F. Tsai, A. Tomita, Preparation of ultrafine carbon tubes in nanochannels of an anodic aluminum oxide film. Chem. Mater. 8, 2109–2113 (1996)
M. Terrones, N. Grobert, J. Olivares, J.P. Zhang, H. Terrones, K. Kordatos et al., Controlled production of aligned-nanotube bundles. Nature 388, 52–55 (1997)
Z.F. Ren, Z.P. Huang, J.W. Xu, J.H. Wang, P. Bush, M.P. Siegal et al., Synthesis of large arrays of well-aligned carbon nanotubes on glass. Science 282, 1105–1107 (1998)
C.N.R. Rao, R. Sen, B.C. Satishkumar, A. Govindaraj, Large aligned-nanotube bundles from ferrocene pyrolysis. Chem. Commun. 15, 1525–1526 (1998)
B.C. Satishkumar, A. Govindaraj, C.N.R. Rao, Bundles of aligned carbon nanotubes obtained by the pyrolysis of ferrocene-hydrocarbon mixtures: role of the metal nanoparticles produced in situ. Chem. Phys. Lett. 307, 158–162 (1999)
S. Huang, L. Dai, A.W.H. Mau, Patterned growth and contact transfer of well-aligned carbon nanotube films. J. Phys. Chem. B 103, 4223–4227 (1999)
S. Fan, M.G. Chapline, N.R. Franklin, T.W. Tombler, A.M. Cassell, H. Dai, Self-oriented regular arrays of carbon nanotubes and their field emission properties. Science 283, 512–514 (1999)
R. Andrews, D. Jacques, A.M. Rao, F. Derbyshire, D. Qian, X. Fan et al., Continuous production of aligned carbon nanotubes: a step closer to commercial realization. Chem. Phys. Lett. 303, 467–474 (1999)
M. Chhowalla, K.B.K. Teo, C. Ducati, N.L. Rupesinghe, G.A.J. Amaratunga, A.C. Ferrari et al., Growth process conditions of vertically aligned carbon nanotubes using plasma enhanced chemical vapor deposition. J. Appl. Phys. 90, 5308–5317 (2001)
K. Hata, D.N. Futaba, K. Mizuno, T. Namai, M. Yumura, S. Iijima, Water-assisted highly efficient synthesis of impurity-free single-walled carbon nanotubes. Science 306, 1362–1364 (2004)
V.K. Kayastha, Y.K. Yap, Z. Pan, I.N. Ivanov, A.A. Puretzky, D.B. Geohegan, High density vertically aligned multiwalled carbon nanotubes with tubular structures. Appl. Phys. Lett. 86, 253105 (2005)
P. Mahanandia, K.K. Nanda, A one-step technique to prepare aligned arrays of carbon nanotubes. Nanotechnology 19, 155602 (2008)
L. Qu, F. Du, L. Dai, Preferential syntheses of semiconducting vertically-aligned single-walled carbon nanotubes for direct use in FETs. Nano Lett. 8, 2682–2687 (2008)
Q. Zhang, M.-Q. Zhao, J.-Q. Huang, Y. Liu, Y. Wang, W.-Z. Qian et al., Vertically aligned carbon nanotube arrays grown on a lamellar catalyst by fluidized bed catalytic chemical vapor deposition. Carbon 47, 2600–2610 (2009)
H. Murakami, M. Hirakawa, C. Tanaka, H. Yamakawa, Field emission from well-aligned, patterned, carbon nanotube emitters. Appl. Phys. Lett. 76, 1776–1778 (2000)
J.-H. Han, W.-S. Yang, J.-B. Yoo, C.-Y. Park, Growth and emission characteristics of vertically well-aligned carbon nanotubes grown on glass substrate by hot filament plasma-enhanced chemical vapor deposition. J. Appl. Phys. 88, 7363–7365 (2000)
G. Chen, D.H. Shin, T. Iwasaki, H. Kawarada, C.J. Lee, Enhanced field emission properties of vertically aligned double-walled carbon nanotube arrays. Nanotechnology 19, 415703 (2008)
J.L. Silan, D.L. Niemann, B.P. Ribaya, M. Rahman, M. Meyyappan, C.V. Nguyen, Carbon nanotube pillar arrays for achieving high emission current densities. Appl. Phys. Lett. 95, 133111 (2009)
C. Li, Y. Zhang, M. Mann, D. Hasko, W. Lei, B. Wang et al., High emission current density, vertically aligned carbon nanotube mesh, field emitter array. Appl. Phys. Lett. 97, 113107 (2010)
H. Liu, Y. Shi, Y. Ding, B. Lu, Investigation of growth properties of patterned and aligned carbon nanotubes for field emitter. Microelectron. Eng. 86, 2236–2240 (2009)
A. Pandey, A. Prasad, J. Moscatello, B. Ulmen, Y.K. Yap, Enhanced field emission stability and density produced by conical bundles of catalyst-free carbon nanotubes. Carbon 48, 287–292 (2010)
A. Pandey, A. Prasad, J.P. Moscatello, Y.K. Yap, Stable electron field emission from PMMA–CNT matrices. ACS Nano 4, 6760–6766 (2010)
S. Sridhar, L. Ge, C.S. Tiwary, A.C. Hart, S. Ozden, K. Kalaga et al., Enhanced field emission properties from CNT arrays synthesized on inconel superalloy. ACS Appl. Mater. Interfaces 6, 1986–1991 (2014)
G. Chen, S. Neupane, W. Li, L. Chen, J. Zhang, An increase in the field emission from vertically aligned multiwalled carbon nanotubes caused by NH3 plasma treatment. Carbon 52, 468–475 (2013)
M. Sreekanth, S. Ghosh, R. Patra, P. Srivastava, Highly enhanced and temporally stable field emission from MWCNTs grown on aluminum coated silicon substrate. AIP Adv. 5, 067173 (2015)
M. Sreekanth, S. Ghosh, P. Biswas, S. Kumar, P. Srivastava, Improved field emission from indium decorated multi-walled carbon nanotubes. Appl. Surf. Sci. 383, 84–89 (2016)
T. Jawhari, A. Roid, J. Casado, Raman spectroscopic characterization of some commercially available carbon black materials. Carbon 33, 1561–1565 (1995)
Y.C. Choi, K.-I. Min, M.S. Jeong, Novel method of evaluating the purity of multiwall carbon nanotubes using Raman spectroscopy. J. Nanomater. 2013, 1–6 (2013)
S.L.H. Rebelo, A. Guedes, M.E. Szefczyk, A.M. Pereira, J.P. Araújo, C. Freire, Progress in the Raman spectra analysis of covalently functionalized multiwalled carbon nanotubes: unraveling disorder in graphitic materials. Phys. Chem. Chem. Phys. 18, 12784–12796 (2016)
R.H. Fowler, L. Nordheim, Electron emission in intense electric fields. Proc. R. Soc. Lond. A 119, 173–181 (1928)
W. Melitz, J. Shen, A.C. Kummel, S. Lee, Kelvin probe force microscopy and its application. Surf. Sci. Rep. 66, 1–27 (2011)
S. Gupta, Y. Batra, B.R. Mehta, V.R. Satsangi, Study of charge separation and interface formation in a single nanorod CdS-CuxS heterojunction solar cell using kelvin probe force microscopy. Nanotechnology 24, 255703 (2013)
R.T.K. Baker, M.A. Barber, P.S. Harris, F.S. Feates, R.J. Waite, Nucleation and growth of carbon deposits from the nickel catalyzed decomposition of acetylene. J. Catal. 26, 51–62 (1972)
M. Xu, D.N. Futaba, M. Yumura, K. Hata, Alignment control of carbon nanotube forest from random to nearly perfectly aligned by utilizing the crowding effect. ACS Nano 6, 5837–5844 (2012)
Acknowledgements
Authors thank Prof. Vikram Kumar, Prof. V. D. Vankar, Dr. Ravi Kumar Bommali, Dr. Debalaya Sarker and Ms. Sana Azim for their help and discussions. The financial assistantship from CSIR, FIST (Raman facilities), NRF, and IIT Delhi is greatly acknowledged.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Sreekanth, M., Ghosh, S. & Srivastava, P. Tuning vertical alignment and field emission properties of multi-walled carbon nanotube bundles. Appl. Phys. A 124, 52 (2018). https://doi.org/10.1007/s00339-017-1471-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s00339-017-1471-7