Abstract
High-density monoclinic β-Ga2O3 nanowires were synthesized by a vapor transport method with controlled ambient oxygen. The structures and morphology were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM) and high-resolution transmission electron microscopy (HR-TEM). X-ray diffraction and HR-TEM analysis indicate that the as-grown β-Ga2O3 nanowires are single crystals with monoclinic structure. Intense four-band emissions covering the range from ultraviolet (UV) to visible were observed in photoluminescence (PL) spectra at room temperature. The main emission bands of deep blue (3.04 eV) to green (2.37 eV) for β-Ga2O3 nanowires were adjusted by controlling the partial pressure of oxygen. This work demonstrates a low-cost and facile process for optoelectronics applications.
Similar content being viewed by others
References
M. Orita, H. Ohta, M. Hirano, H. Hosono, Appl. Phys. Lett. 77, 4166 (2000)
C. Baban, Y. Toyoda, M. Ogita, Thin Solid Films 484, 369 (2005)
J. Frank, M. Fleischer, H. Meixner, Sens. Actuators B 48, 318 (1998)
M. Passlack, E.F. Schubert, W.S. Hobson, M. Hong, N. Moriya, S.N.G. Chu, K. Konstadinidis, J.P. Mannaerts, M.L. Schnoes, G.J. Zydzik, J. Appl. Phys. 77, 686 (1998)
Y. Tomm, J.M. Ko, A. Yoshikawa, T. Fukuda, Sol. Energy Mater. Sol. Cells 66, 369 (2001)
Z.R. Dai, Z.W. Pan, Z.L. Wang, Adv. Funct. Mater. 13, 9 (2003)
H.Z. Zhang, Y.C. Kong, Y.Z. Wang, X. Du, Z.G. Bai, J.J. Wang, D.P. Yu, Y. Ding, Q.L. Hang, S.Q. Feng, Solid State Commun. 109, 677 (1999)
C.H. Liang, G.W. Meng, G.Z. Wang, Y.W. Wang, L.D. Zhang, S.Y. Zhang, Appl. Phys. Lett. 78, 3202 (2001)
Y.C. Choi, W.S. Kim, Y.S. Park, S.M. Lee, D.J. Bae, Y.H. Lee, G.S. Park, W.B. Choi, N.S. Lee, J.M. Kim, Adv. Mater. 12, 46 (2000)
J. Zhang, Z.G. Liu, C.K. Lin, J. Lin, J. Cryst. Growth 280, 99 (2005)
P.C. Chang, Z.Y. Fan, W.Y. Tseng, A. Rajagopal, J.G. Lu, Appl. Phys. Lett. 87, 222102 (2005)
K.W. Chang, J.J. Wu, Adv. Mater. 16, 545 (2004)
H. Zhou, M. Wissinger, J. Fallert, R. Hauschild, F. Stelzl, C. Klingshirn, H. Kalt, Appl. Phys. Lett. 91, 181112 (2007)
D.S. Yang, C.S. Lao, A.H. Zewail, Science 321, 1660 (2008)
M.H. Huang, S. Mao, H. Feick, H.Q. Yan, Y.Y. Wu, H. Kind, E. Weber, R. Russo, P.D. Yang, Science 292, 2001 (1897)
M.F. Yu, M.Z. Atashbar, X.L. Chen, IEEE Sens. J. 5, 20 (2005)
L.Y. Gao, M.J. Zheng, M. Zhong, M. Li, L. Ma, Appl. Phys. Lett. 91, 013101 (2007)
C.H. Hsieh, L.J. Chou, G.R. Lin, Y. Bando, D. Golberg, Nano Lett. 8, 3081 (2008)
L. Binet, D. Gourier, J. Phys. Chem. Solids 59, 1241 (1998)
T. Harwig, J. Schoonman, J. Solid State Chem. 23, 205 (1978)
V.I. Vasiltsiv, Y.M. Zakharko, Y.I. Rym, Ukr. Fiz. Zh. 33, 1320 (1988)
E.G. Villora, T. Atou, T. Sekiguchi, T. Sugawara, M. Kikuchi, T. Fukuda, Solid State Commun. 120, 455 (2001)
Y.P. Song, H.Z. Zhang, C. Lin, Y.W. Zhu, G.H. Li, F.H. Yang, D.P. Yu, Phys. Rev. B 69, 075304 (2004)
E. Nogales, J.A. Garcia, B. Mendez, J. Piqueras, J. Appl. Phys. 101, 033517 (2007)
G. Sinha, A. Patra, Chem. Phys. Lett. 473, 151 (2009)
R.S. Wagner, W.C. Ellis, Appl. Phys. Lett. 4, 89 (1964)
X.T. Zhou, F. Heigl, J.Y.P. Ko, M.W. Murphy, J.G. Zhou, T. Regier, R.I.R. Blyth, T.K. Sham, Phys. Rev. B 75, 125303 (2007)
C.H. Ho, C.Y. Tseng, L.C. Tien, Opt. Express 18, 16360 (2010)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Tien, L.C., Ho, C.H., Yao, X.T. et al. Synthesis of β-Ga2O3 nanowires as a broadband emitter. Appl. Phys. A 102, 105–108 (2011). https://doi.org/10.1007/s00339-010-6094-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-010-6094-1