Synthesis and luminescent characteristics of one-dimensional europium doped Gd₂O₃ phosphors

Abstract

One-dimensional (1D) Gd₂O₃:Eu³⁺ nano-rods and micro-rods were prepared using a facile sol-gel precipitation method, without a template and with a post-growth heat treatment in air. Based on scanning electron microscopy (SEM) and X-ray diffraction (XRD) data, hexagonal Gd(OH)₃:Eu³⁺ micro-rods, 60∼90 nm in diameter and 700 nm to 1 μm in length, were synthesized and then transformed by calcining (800°C, 2 hr) to cubic Gd₂O₃:Eu³⁺ with the same morphology and dimensions. Nano-rods of Eu³⁺ doped Gd(OH)₃ and calcined Gd₂O₃, 60∼90 nm diameter and 150∼300 nm length, were prepared by adding polyethylene glycol (PEG) as a capping agent during the sol-gel synthesis. Photoluminescence (PL) spectra exhibited the ⁵D₀–⁷F₂ transitions of Eu³⁺ at 612 and 627 nm from excitation at 280 nm. Photoluminescence excitation (PLE) data showed that a small fraction of PL from Eu³⁺ resulted from direct excitation, but most PL resulted from the oxygen to europium charge-transfer band (CTB) between 250 and 280 nm.