Picosecond laser ablation of SiO₂ layers on silicon substrates

Abstract

In this work, we report on laser ablation of thermally grown SiO₂ layers from silicon wafer substrates, employing an 8–9 ps laser, at 1064 (IR), 532 (VIS) and 355 nm (UV) wavelengths. High-intensity short-pulse laser radiation allows direct absorption in materials with bandgaps higher than the photon energy. However, our experiments show that in the intensity range of our laser pulses (peak intensities of <2×10¹² W/cm²) the removal of the SiO₂ layer from silicon wafers does not occur by direct absorption in the SiO₂ layer. Instead, we find that the layer is removed by a “lift off” mechanism, actuated by the melting and vaporisation of the absorbing silicon substrate. Furthermore, we find that exceeding the Si melting threshold is not sufficient to remove the SiO₂ layer. A second threshold exists for breaking of the layer caused by sufficient vapour pressure. For SiO₂ layer ablation, we determine layer thickness dependent minimum fluences of 0.7–1.2 J/cm² for IR, 0.1–0.35 J/cm² for VIS and 0.2–0.4 J/cm² for UV wavelength. After correcting the fluences by the reflected laser power, we show that, in contrast to the melting threshold, the threshold for breaking the layer depends on the SiO₂ thickness.