Zinc oxide nanostructures grown by pulsed laser deposition

Abstract

We report the use of PLD to grow different ZnO nanostructures. Very different film morphologies have been observed using different laser wavelengths to ablate the target. The influence of substrate temperature and oxygen background pressure on the film morphology has been investigated too. Smooth and rough films, hexagonal pyramids and columns have been obtained by using a KrF excimer laser (248 nm) for the target ablation, while hexagonal hierarchical structures and pencils have been obtained by using ArF (193 nm). Photoluminescence and X-ray diffraction measurements revealed the good quality of the samples, in particular of those deposited using the ArF laser beam.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    Ü. Özgür, Ya.I. Alivov, C. Liu, A. Teke, M.A. Reshchikov, S. Doğan, V. Avrutin, S.-J. Cho, H. Morkoç, J. Appl. Phys. 98, 041301 (2005)

    Article  ADS  Google Scholar 

  2. 2.

    Z.L. Wang, Appl. Phys. A 88, 7 (2007)

    Article  ADS  Google Scholar 

  3. 3.

    Y.W. Heo, D.P. Norton, L.C. Tien, Y. Kwon, B.S. Kang, F. Ren, S.J. Pearton, J.R. LaRoche, Mater. Sci. Eng. R 47, 1 (2004)

    Article  Google Scholar 

  4. 4.

    K.-F. Lin, H.-M. Cheng, H.-C. Hsu, L.-J. Lin, W.-F. Hsieh, Chem. Phys. Lett. 409, 208 (2005)

    Article  ADS  Google Scholar 

  5. 5.

    M.H. Huang, Y. Wu, H. Feick, N. Tran, E. Weber, P. Yang, Adv. Mater. 13, 113 (2001)

    Article  Google Scholar 

  6. 6.

    Y. Sun, G.M. Fuge, M.N.R. Ashfold, Chem. Phys. Lett. 396, 21 (2004)

    Article  ADS  Google Scholar 

  7. 7.

    W.I. Park, G.-C. Yi, M. Kim, S.J. Pennycook, Adv. Mater. 14, 1841 (2002)

    Article  Google Scholar 

  8. 8.

    Y.H. Yang, B. Wang, G.W. Yang, Nanotechnology 17, 5556 (2006)

    Article  ADS  Google Scholar 

  9. 9.

    T. Okada, K. Kawashima, M. Ueda, Appl. Phys. A 81, 907 (2005)

    Article  ADS  Google Scholar 

  10. 10.

    I. Ozerov, D. Nelson, A.V. Bulgakov, W. Marine, M. Sentis, Appl. Surf. Sci. 212–213, 349 (2003)

    Article  Google Scholar 

  11. 11.

    L.E. Greene, B.D. Yuhas, M. Law, D. Zitoun, P. Yang, Inorg. Chem. 45, 7535 (2006)

    Article  Google Scholar 

  12. 12.

    C. Liu, H. Li, W. Jie, X. Zhang, D. Yu, Mater. Lett. 60, 1394 (2006)

    Article  Google Scholar 

  13. 13.

    M.H. Wong, A. Berenov, X. Qi, M.J. Kappers, Z.H. Barber, B. Illy, Z. Lockman, M.P. Ryan, J.L. MacManus-Driscoll, Nanotechnology 14, 968 (2003)

    Article  ADS  Google Scholar 

  14. 14.

    M.-T. Chen, J.-M. Ting, Thin Solid Films 494, 250 (2006)

    Article  ADS  Google Scholar 

  15. 15.

    Y.W. Heo, V. Varadarajan, M. Kaufman, K. Kim, D.P. Norton, F. Ren, P.H. Fleming, Appl. Phys. Lett. 81, 3046 (2002)

    Article  ADS  Google Scholar 

  16. 16.

    H.J. Fan, W. Lee, R. Scholz, A. Dadgar, A. Krost, K. Nielsch, M. Zacharias, Nanotechnology 16, 913 (2005)

    Article  ADS  Google Scholar 

  17. 17.

    P. Misra, L.M. Kukreja, Thin Solid Films 485, 42 (2005)

    Article  ADS  Google Scholar 

  18. 18.

    M. Lorenz, E.M. Kaidashev, A. Rahm, Th. Nobis, J. Lenzner, G. Wagner, D. Spemann, H. Hochmuth, M. Grundmann, Appl. Phys. Lett. 86, 143113 (2005)

    Article  ADS  Google Scholar 

  19. 19.

    J.-H. Park, I.-S. Hwang, Y.-J. Choi, J.-G. Park, J. Cryst. Growth 276, 171 (2005)

    Article  ADS  Google Scholar 

  20. 20.

    R. O’Haire, A. Meaney, E. McGlynn, M.O. Henry, J.-R. Duclère, J.-P. Mosnier, Superlattices Microstruct. 139, 153 (2006)

    Article  Google Scholar 

  21. 21.

    Y. Zhang, R.E. Russo, S.S. Mao, Appl. Phys. Lett. 87, 133115 (2005)

    Article  ADS  Google Scholar 

  22. 22.

    K. Vanheusden, C.H. Seager, W.L. Warren, D.R. Tallant, J.A. Voigt, Appl. Phys. Lett. 68, 403 (1996)

    Article  ADS  Google Scholar 

  23. 23.

    B. Cao, W. Cai, H. Zeng, Appl. Phys. Lett. 88, 161101 (2006)

    Article  ADS  Google Scholar 

  24. 24.

    X.L. Wu, G.G. Siu, C.L. Fu, H.C. Ong, Appl. Phys. Lett. 78, 2285 (2001)

    Article  ADS  Google Scholar 

  25. 25.

    P. Brix, G. Herzberg, J. Chem. Phys. 21, 2240 (1953)

    Article  ADS  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to D. Valerini.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Valerini, D., Caricato, A.P., Lomascolo, M. et al. Zinc oxide nanostructures grown by pulsed laser deposition. Appl. Phys. A 93, 729–733 (2008). https://doi.org/10.1007/s00339-008-4703-z

Download citation

PACS

  • 81.15.Fg
  • 81.07.-b
  • 68.55.J-