Abstract
Morphological, optical and transport properties of GaN and InN nanowires grown by molecular beam epitaxy (MBE) have been studied. The differences between the two materials in respect to growth parameters and optimization procedure was stressed. The nanowires crystalline quality has been investigated by means of their optical properties. A comparison of the transport characteristics was given. For each material a band schema was shown, which takes into account transport and optical features and is based on Fermi level pinning at the surface.
Similar content being viewed by others
References
R.S. Wagner, W.C. Ellis, Appl. Phys. Lett. 4, 89 (1964)
Y. Cui, Z. Zhong, D. Wang, W. Wang, C. Lieber, Nano Lett. 3, 149 (2003)
A. Greytak, L. Lauhon, M. Gudiksen, C. Lieber, Appl. Phys. Lett. 84, 4176 (2004)
J. Hahm, C. Lieber, Nano Lett. 4, 51 (2004)
Y. Huang, X. Duan, Y. Cui, C. Lieber, Nano Lett. 2, 101 (2002)
M. McAlpine, R. Friedman, S. Jin, K.H. Lin, W. Wang, C. Lieber, Nano Lett. 3, 1531 (2003)
Z. Zhong, F. Qian, D. Wang, C. Lieber, Nano Lett. 3, 343 (2003)
X. Duan, Y. Huang, R. Agarwal, C. Lieber, Nature 421, 241 (2003)
Z. Zhong, D. Wang, Y. Cui, M. Bockrath, C. Lieber, Science 302, 1377 (2003)
M.T. Bjoerk, B.J. Ohlsson, T. Sass, A.I. Persson, C. Thelander, M.H. Magnusson, K. Deppert, L.R. Wallenberg, L. Samuelson, Appl. Phys. Lett. 6, 1058 (2002)
M.T. Bjoerk, B.J. Ohlsson, C. Thelander, A.I. Persson, K. Deppert, L.R. Wallenberg, L. Samuelson, Appl. Phys. Lett. 81, 4458 (2002)
R. Calarco, M. Marso, T. Richter, A.I. Aykanat, R. Meijers, A. van der Hart, T. Stoica, H. Lüth, Nano Lett. 5, 981 (2005)
C. Thelander, H.A. Nilsson, L.E. Jensen, L. Samuelson, Nano Lett. 5, 635 (2005)
R. Calarco, M. Marso, R. Meijers, T. Richter, A. Aykanat, T. Stoica, H. Lüth, ASDAM 2004 – Conf. Proc., 5th Int. Conf. Semiconductor Devices and Microsystmes (2004), p. 9
E. Calleja, M.A. Sánchez-García, F. Sanchez, F. Calle, F. Naranjo, E. Munoz, U. Jahn, K. Ploog, Phys. Rev. B 62, 16826 (2000)
E. Calleja, M.A. Sánchez-García, F. Sanchez, F. Calle, F. Naranjo, E. Munoz, S. Molina, A. Sanchez, F. Pacheco, R. Garcia, J. Cryst. Growth 201–202, 296 (1999)
J. Sanchez-Páramo, J. Calleja, M.A. Sánchez-García, E. Calleja, U. Jahn, Physica E 13, 1070 (2002)
R. Meijers, T. Richter, R. Calarco, T. Stoica, H.-P. Bochem, M. Marso, H. Lüth, J. Cryst. Growth 289, 381 (2006)
J. Ristic, E. Calleja, M.A. Sánchez-García, J. Ulloa, J. Sanchez-Páramo, J. Calleja, U. Jahn, A. Trampert, K.H. Ploog, Phys. Rev. B 68, 125305 (2003)
J. Ristic, E. Calleja, A. Trampert, S. Fernandez-Garrido, C. Rivera, U. Jahn, K.H. Ploog, Phys. Rev. Lett. 94, 146102 (2005)
J. Ristic, M.A. Sánchez-García, E. Calleja, J. Sanchez-Páramo, J. Calleja, U. Jahn, K. Ploog, Phys. Stat. Solidi A 192, 60 (2002)
J. Ristic, M.A. Sánchez-García, J. Ulloa, E. Calleja, J. Sanchez-Páramo, J. Calleja, U. Jahn, A. Trampert, K. Ploog, Phys. Stat. Solidi B 234, 717 (2002)
F. Qian, Y. Li, S. Gradecak, D. Wang, C. Barrelet, C. Lieber, Nano Lett. 4, 1975 (2004)
O. Hayden, R. Agarwal, C.M. Lieber, Nature Mater. 5, 352356 (2006)
J.C. Johnson, H.-J. Choi, K.P. Knutsen, R.D. Schaller, P. Yang, R.J. Saykally, Nature Mater. 1, 106 (2002)
A.G. Bhuiyan, A. Hashimoto, A. Yamamoto, Appl. Phys. 94, 2779 (2003)
E. Dimakis, G. Konstantinidis, K. Tsagaraki, A. Adikimenakis, E. Iliopoulos, A. Georgakilas, Superlattices Microstruct. 36, 497 (2004)
J. Grandal, M.A. Sánchez-García, F. Calle, E. Calleja, Phys. Stat. Solidi C 2, 2289 (2005)
M.C. Johnson, C.J. Lee, E.D. Bourret-Courchesne, S.L. Konsek, S. Aloni, W.Q. Han, A. Zettl, Appl. Phys. Lett. 85, 5670 (2004)
C.H. Liang, L.C. Chen, J.S. Hwang, K.H. Chen, Y.T. Hung, Y.F. Chen, Appl. Phys. Lett. 81, 22 (2002)
C. Nörenberg, M.G. Martin, R.A. Oliver, M.R. Castell, G.A.D. Briggs, J. Phys. D Appl. Phys. 35, 615 (2002)
T. Tang, S. Han, W. Jin, X. Liu, C. Li, D. Zhang, C. Zhou, B. Chen, J. Han, M. Meyyapan, J. Mater. Res. 19, 423 (2004)
J. Zhang, B. Xu, F. Jiang, Y. Yang, J. Li, Phys. Lett. A 337, 121 (2005)
T. Stoica, R. Meijers, R. Calarco, T. Richter, H. Lüth, J. Cryst. Growth 290, 241 (2006)
E.I. Givargizov, J. Cryst. Growth 31, 20 (1975)
M. Shirai, K. Haraguchi, K. Hiruma, T. Katsuyama, Gold Bull. 32, 80 (1999)
R. Calarco, M. Marso, R. Meijers, T. Richter, A. Aykanat, T. Stoica, H. Lüth, Nano Lett. 6, 1548 (2006)
T. Stoica, R. Meijers, R. Calarco, T. Richter, E. Sutter, H. Läuth, Nano Lett. 6, 1541 (2006)
Author information
Authors and Affiliations
Corresponding author
Additional information
PACS
73.30.+y; 73.21.Hb; 73.22.-f
Rights and permissions
About this article
Cite this article
Calarco, R., Marso, M. GaN and InN nanowires grown by MBE: A comparison. Appl. Phys. A 87, 499–503 (2007). https://doi.org/10.1007/s00339-007-3871-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-007-3871-6