Abstract
The Pr1+xBa2-xCu3O7±δ solid solution was investigated by means of X-ray powder diffraction combined with Rietveld analysis. A Pr123 single phase could be synthesized under Pr-rich conditions by sintering at 950 °C in air. The solubility range of Pr1+xBa2-xCu3O7±δ solid solution is 0.08≤x≤0.80. The structure of Pr1+xBa2-xCu3O7±δ for 0.08≤x<0.30 is orthorhombic. The structure transforms into tetragonal for 0.30≤x≤0.80. To form the Pr123 single phase, the Ba sites in the Pr123 structure must have partial Pr ions, and the least amount is x=0.08. Ba ions cannot occupy the sites of Pr ions. In the Pr123 structure, Ca ions can replace Pr ions; the highest value is x=0.4 in the PrBa2-xCaxCu3O7±δ system under our experimental conditions. However, Ca ions cannot replace Ba ions. The ionic radius plays a more important role than the chemical properties in the substitution between Pr, Ba and Ca ions in the Pr123 structure.
Similar content being viewed by others
References
J.G. Bednorz, K.A. Muller: Z. Phys. B Cond. Mater. 64, 189 (1986)
G.W. Chu, P.H. Hor, R.L. Meng, L. Gao, Z.J. Huang: Science 235, 567 (1987)
Z.X. Zhao, L.Q. Chen, Q.S. Yang, Y.Z. Huang, G.H. Chen, R.M. Tang, G.R. Liu: Kexue Tongbao 32, 681 (1987)
D.G. Hinks, L. Soderholm, D.W. Caponell, J.D. Jorgense, I.K. Schuller, C.U. Segre, K. Zhang, J.D. Grace: Appl. Phys. Lett. 50, 1688 (1987)
K.G. Frase, D.M. DeLeeuw, C.A.H. Amutsaers, C. Langereis, H.C.A. Smooren-Burg, P.J. Roommers: Physica C 152, 39 (1988)
G.C. Che, J.K. Liang, W. Chen, Q.S. Yang, G.H. Chen, Y.M. Ni: J. Less Common Met. 138, 137 (1988)
K. Osamura, W. Zhang: Z. Metallkde. 82, 408 (1991)
C. Dong, J. K Liang, G.C. Che, S.S. Xie, Z.X. Zhao, Q.S. Yang, Y.M. Ni, G.R. Liu: Intern. J. Mod. Phys. B 1, 323 (1987)
G.C. Che, J.K. Liang, W. Chen, S.S. Xie, Y.D. Yu, Z.X. Zhao, Q.S. Yang, G.H. Chen: Kexue Tongbao 32, 1094 (1987)
J.K. Liang, X.L. Chen, X.T. Wang, W. Chen, Z. Chen, Z.Y. Qiao, Y.L. Zhang, S.S. Xie, Y.M. Ni: Solid State Commun. 76, 903 (1990)
S.A. Hodorowicz, J. Czerwonka, H.A. Eick: J. Solid State Chem. 88, 391 (1990)
S.J. Fu, S.S. Xie, J.K. Liang, G.C. Che, Z.X. Zhao: Mod. Phys. Lett. B 2, 1073 (1988)
J. Czerwonka, H.A. Eick: J. Solid State Chem. 90, 69 (1991)
Z.Y. Qiao, W.X. Yuan, X.R. Xing, S.K. Wei, X.R. Cheng, X.L. Chen, J.K. Liang: J. Rare Earths 11, 152 (1993)
S.A. Hodorowicz, A. Lasocha, W. Lasocha, H.A. Eick: J. Solid State Chem. 75, 270 (1988)
C.N. Pieczulewski, J.E. McAdams, T.O. Mason: J. Am. Ceram. Soc. 73, 3088 (1990)
J.K. Liang, X.T. Xu, G.H. Rao, S.S. Xie, X.Y. Shao, Z.G. Duan: J. Phys. D Appl. Phys. 20, 1324 (1987); J. Mod. Phys. 1, 337 (1987)
S.A. Hodorowicz, A. Chodorowicz-Bak, J. Czerwonka, E. Hodorowicz, W. Lasocha, H.A. Eick: J. Solid State Chem. 92, 480 (1991)
Y.L. Zhang, J.K. Liang, X.R. Cheng, G.H. Rao, H.B. Liu, Y.M. Ni, D.N. Zeng, S.S. Xie: J. Less Common Met. 146, 121 (1989)
E. Hodorowicz, S.A. Hodorowicz, W.K. Wong-Ng: J. Solid State Chem. 98, 181 (1992)
S.A. Hodorowicz, A. Chodorowicz-Bak, J. Czerwonka, E. Hodorowicz, W. Lasocha, H.A. Eick: Acta Phys. Pol. A 75, 121 (1989)
E. Hodorowic, S.A. Hodorowicz, H.A. Eick: Physica C 158, 395 (1989)
J.K. Liang, X.L. Chen, X.T. Wang, W. Chen, Z. Chen, Z.Y. Qiao, Y.L. Zhang, S.S. Xie: Solid State Commun. 74, 509 (1990)
K. Oka, T. Ito: Physica C 227, 77 (1994)
K. Oka, Z.G. Zou, T. Ito: Physica C 282–287, 479 (1997)
M. Tagami, M. Sumida, C. Krauns, Y. Yamada, T. Umeda, Y. Shiohara: Physica C 250, 240 (1995)
C. Bertrand, P. Galez, R.E. Gladyskerskii, J.L. Jorda: Physica C 321, 151 (1999)
M. Luszczek: Physica C 355, 15 (2001)
M. Park, M.J. Kramer, K.W. Dennis, R.W. McCallum: Physica C 259, 43 (1996)
C.H. Booth, F. Bridges, J.B. Boyce, T. Chaeson, Z.X. Zhao, P. Cervantes: Phys. Rev. B 49, 3432 (1994)
H.A. Blackstead, J.D. Dow: Solid State Commun. 115, 137 (2000)
B. Fisher, J. Genossar, L. Patlagan, G.M. Reisner, C.K. Subramanian, A.B. Kaiser: Phys. Rev. B 50, 4118 (1994)
C. Infante, M.K. El Mously, R. Dayal, M. Husain, S.A. Siddiqi, P. Ganguly: Physica C 1679, 640 (1990)
Z.P. Han, R. Dupree, D. McPaul, A.P. Howes, L.W.J. Caves: Physica C 181, 355 (1991)
C. Changkang, A.T. Boothroyd, Y. Hu, F.R. Wondre, B.M. Wanklyn, J.W. Hodby: Physica C 214, 231 (1993)
H.A. Blackstead, D.B. Chrisey, J.D. Dow, J.S. Horwitz, A.E. Klunzinger, D.B. Pulling: Phys. Lett. A 2, 109 (1995)
Z.X. Zhao, K.Q. Li, G.C. Che: Physica C 341–348, 331 (2000)
S.A. Hodorowicz, J. Czerwonka, H.A. Eick: J. Solid State Chem. 88, 391 (1990)
H.M. Rietveld: Acta Crystallog. 229, 151 (1967)
R.Y. Young, A. Sakthirel, T.S. Moss, C.O. Paiva-Santos: J. Appl. Crystallog. 28, 226 (1995)
I.D. Brown: Structure and Bonding in Crystals, Vol. 2, ed. by M. O’Keefe , A. Navrotsky (Academic Press, New York 1981)
Author information
Authors and Affiliations
Corresponding author
Additional information
PACS
61.50.Ah; 64.70.Kb; 61.72.Ff
Rights and permissions
About this article
Cite this article
Song , G., Liang , J., Yang , L. et al. Subsolidus phase relation and crystal structure in the Pr1+x-yBa2-x-zCay+zCu3O7±δ system. Appl Phys A 77, 915–921 (2003). https://doi.org/10.1007/s00339-002-2071-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-002-2071-7