The fine emulsion polymerizations of styrene initiated by a redox system ammonium peroxodisulfate/sodium thiosulfite stabilized by a non-ionic emulsifier were kinetically investigated. The dependence of the rate of polymerization on conversion or the emulsifier concentration was described by a curve with maximum at medium conversion. The maximum rate of polymerization is proportional to the − 0.45th and 1.5th power of initiator and emulsifier concentration, the number of particles to the 0.32nd and 1.3rd power of initiator and emulsifier concentration and the molecular weight to the − 0.62th and −0.97th power of initiator and emulsifier concentration, respectively. The results show a strong decrease in turbidity at around 20% conversion when emulsion turns into translucent latex. Deviation from the micellar nucleation model was attributed to the solubility of emulsifier in monomer, high level of nonmicellar aggregates, thick interfacial layer and transfer emulsion to microemulsion. The strong decrease of molecular weight with increasing emulsifier concentration is attributed to chain transfer events promoted by the high level of emulsifier at the reaction loci.
Similar content being viewed by others
Author information
Authors and Affiliations
Additional information
Received: 16 November 1998/Revised version: 25 May, 10 October 1999/Accepted: 10 October 1999
Rights and permissions
About this article
Cite this article
Capek, I., Chudej, J. On the fine emulsion polymerization of styrene with non-ionic emulsifier. Polymer Bulletin 43, 417–424 (1999). https://doi.org/10.1007/s002890050630
Issue Date:
DOI: https://doi.org/10.1007/s002890050630