Abstract
In this article, an approach to toughen epoxy thermosets with hyperbranched epoxy resin is presented. First, three tetramethyl biphenyl backboned hyperbranched epoxy resins (BPHBEs) were synthesized through a simple one-pot A2 + B3 polycondensation reaction. Then, they were incorporated into epoxy/anhydride and epoxy/jeffamine curing systems, respectively. The curing behavior was investigated by differential scanning calorimetry, which reveals that the adding of BPHBE to the formulation would not much affect the curing process. The influence of BPHBE on the mechanical and thermomechanical properties of both epoxy/anhydride and epoxy/jeffamine systems was studied. The results show that BPHBE can significantly toughen both two systems without much trade-offs in their strength, modulus and Tg. While the initial decomposition temperature of the cured thermosets slightly drops. Owing to the miscible backbone structure and terminal epoxy groups, no phase separation was observed in SEM.
Similar content being viewed by others
References
Mohan P (2013) A critical review: the modification, properties, and applications of epoxy resins. Polym Plast Technol Eng 52:107–125. https://doi.org/10.1080/03602559.2012.727057
Jin F-L, Li X, Park S-J (2015) Synthesis and application of epoxy resins: a review. J Ind Eng Chem 29:1–11. https://doi.org/10.1016/j.jiec.2015.03.026
Bagheri R, Marouf BT, Pearson RA (2009) Rubber-toughened epoxies: a critical review. Polym Rev 49:201–225. https://doi.org/10.1080/15583720903048227
Fei X, Wei W, Zhao F et al (2017) Efficient toughening of epoxy-anhydride thermosets with a biobased tannic acid derivative. ACS Sustain Chem Eng 5:596–603. https://doi.org/10.1021/acssuschemeng.6b01967
Ye W, Wei W, Fei X et al (2017) Six-arm star-shaped polymer with cyclophosphazene core and poly(ε-caprolactone) arms as modifier of epoxy thermosets. J Appl Polym Sci 134:1–9. https://doi.org/10.1002/app.44384
Chonkaew W, Sombatsompop N, Brostow W (2013) High impact strength and low wear of epoxy modified by a combination of liquid carboxyl terminated poly (butadiene-co-acrylonitrile) rubber and organoclay. Eur Polym J 49:1461–1470. https://doi.org/10.1016/j.eurpolymj.2013.03.022
Rico M, López J, Montero B, Bellas R (2012) Phase separation and morphology development in a thermoplastic-modified toughened epoxy. Eur Polym J 48:1660–1673. https://doi.org/10.1016/j.eurpolymj.2012.07.007
Jiang T, Kuila T, Kim NH, Lee JH (2014) Effects of surface-modified silica nanoparticles attached graphene oxide using isocyanate-terminated flexible polymer chains on the mechanical properties of epoxy composites. J Mater Chem A 2:10557. https://doi.org/10.1039/c4ta00584h
Fei X, Zhao F, Wei W et al (2016) Tannic acid as a bio-based modifier of epoxy/anhydride thermosets. Polymers (Basel) 8:314. https://doi.org/10.3390/polym8090314
Gui D, Miao X, Zeng G, Liu J (2013) Preparation and thermal stability of amine-terminated polyesterimide modified epoxy resin. J Mater Sci 24:4614–4620. https://doi.org/10.1007/s10854-013-1452-3
Li T, Qin H, Liu Y et al (2012) Hyperbranched polyester as additives in filled and unfilled epoxy-novolac systems. Polymer 53:5864–5872. https://doi.org/10.1016/j.polymer.2012.10.028
Li J, Xiang Y, Zheng S (2016) Hyperbranched block copolymer from AB2 macromonomer: synthesis and its reaction-induced microphase separation in epoxy thermosets. J Polym Sci Part A Polym Chem 54:368–380. https://doi.org/10.1002/pola.27784
Flores M, Fernández-Francos X, Ferrando F et al (2012) Efficient impact resistance improvement of epoxy/anhydride thermosets by adding hyperbranched polyesters partially modified with undecenoyl chains. Polymer 53:5232–5241. https://doi.org/10.1016/j.polymer.2012.09.031
Zhang D, Liang E, Li T et al (2013) The effect of molecular weight of hyperbranched epoxy resins with a silicone skeleton on performance. RSC Adv 3:9522–9529. https://doi.org/10.1039/c3ra00023k
Zou Z, Liu X, Wu Y et al (2016) Hyperbranched polyurethane as a highly efficient toughener in epoxy thermosets with reaction-induced microphase separation. RSC Adv 6:18060–18070. https://doi.org/10.1039/C5RA21168A
Jin Q, Misasi JM, Wiggins JS, Morgan SE (2015) Simultaneous reinforcement and toughness improvement in an aromatic epoxy network with an aliphatic hyperbranched epoxy modifier. Polymer 73:174–182. https://doi.org/10.1016/j.polymer.2015.07.031
Fernández-Francos X, Foix D, Serra À et al (2010) Novel thermosets based on DGEBA and hyperbranched polymers modified with vinyl and epoxy end groups. React Funct Polym 70:798–806. https://doi.org/10.1016/j.reactfunctpolym.2010.07.008
Luo L, Meng Y, Qiu T, Li X (2013) An epoxy-ended hyperbranched polymer as a new modifier for toughening and reinforcing in epoxy resin. J Appl Polym Sci 130:1064–1073. https://doi.org/10.1002/app.39257
Zhang D, Jia D (2006) Toughness and strength improvement of diglycidyl ether of bisphenol-A by low viscosity liquid hyperbranched epoxy resin. J Appl Polym Sci 101:2504–2511. https://doi.org/10.1002/app.23760
Miao X, Meng Y, Li X (2015) A novel all-purpose epoxy-terminated hyperbranched polyether sulphone toughener for an epoxy/amine system. Polymer 60:88–95. https://doi.org/10.1016/j.polymer.2015.01.034
Jiang H, Wang R, Farhan S, Zheng S (2015) Improved thermosets obtained from diglycidyl ether of bisphenol A/4,4′-diaminodiphenylsulfone based on a new epoxy-terminated hyperbranched polymer. Polym Int 64:1794–1800. https://doi.org/10.1002/pi.4982
Fu T, Zhang G, Zhong S et al (2007) Reaction kinetics, thermal properties of tetramethyl biphenyl epoxy resin cured with aromatic diamine. J Appl Polym Sci 105:2611–2620. https://doi.org/10.1002/app.26340
Su W-FA, Chuang C-M (2002) Effects of chemical structure changes on curing reactions and thermal properties of cyanate ester-cured rigid-rod epoxy resins. J Appl Polym Sci 85:2419–2422. https://doi.org/10.1002/app.10887
De B, Karak N (2015) Ultralow dielectric, high performing hyperbranched epoxy thermosets: synthesis, characterization and property evaluation. RSC Adv 5:35080–35088. https://doi.org/10.1039/C5RA04248H
Barua S, Dutta G, Karak N (2013) Glycerol based tough hyperbranched epoxy: synthesis, statistical optimization and property evaluation. Chem Eng Sci 95:138–147. https://doi.org/10.1016/j.ces.2013.03.026
De B, Karak N (2013) Novel high performance tough hyperbranched epoxy by an A2 + B3 polycondensation reaction. J Mater Chem A. https://doi.org/10.1039/c2ta00011c
Luo L, Meng Y, Qiu T et al (2013) Dielectric and mechanical properties of diglycidyl ether of bisphenol a modified by a new fluoro-terminated hyperbranched poly(phenylene oxide). Polym Compos 34:1051–1060. https://doi.org/10.1002/pc.22512
Pan L, Lu S, Xiao X et al (2015) Enhanced mechanical and thermal properties of epoxy with hyperbranched polyester grafted perylene diimide. RSC Adv 5:3177–3186. https://doi.org/10.1039/C4RA13609H
Liu T, Nie Y, Chen R et al (2015) Hyperbranched polyether as an all-purpose epoxy modifier: controlled synthesis and toughening mechanisms. J Mater Chem A 3:1188–1198. https://doi.org/10.1039/C4TA04841E
Miao X, Meng Y, Li X (2015) Epoxide-terminated hyperbranched polyether sulphone as triple enhancement modifier for DGEBA. J Appl Polym Sci. https://doi.org/10.1002/app.41910
Le QH, Kuan HC, Bin Dai J et al (2010) Structure-property relations of 55 nm particle-toughened epoxy. Polymer 51:4867–4879. https://doi.org/10.1016/j.polymer.2010.08.038
Luo X, Mather PT (2010) Triple-shape polymeric composites (TSPCs). Adv Funct Mater 20:2649–2656. https://doi.org/10.1002/adfm.201000052
Xie T, Rousseau IA (2009) Facile tailoring of thermal transition temperatures of epoxy shape memory polymers. Polymer 50:1852–1856. https://doi.org/10.1016/j.polymer.2009.02.035
Zheng N, Fang G, Cao Z et al (2015) High strain epoxy shape memory polymer. Polym Chem 6:3046–3053. https://doi.org/10.1039/C5PY00172B
Acknowledgements
We are grateful for the financial support from the Enterprise-University-Research Prospective Program, Jiangsu Province (BY2015019-08) and MOE & SAFEA for the 111 Project (B13025).
Author information
Authors and Affiliations
Contributions
The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript.
Corresponding author
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Fei, X., Tang, Y., Wei, W. et al. One-pot synthesis of tetramethyl biphenyl backboned hyperbranched epoxy resin as an efficient toughening modifier for two epoxy curing systems. Polym. Bull. 75, 4571–4586 (2018). https://doi.org/10.1007/s00289-018-2269-2
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00289-018-2269-2