Structural development of gel-spinning UHMWPE fibers through industrial hot-drawing process analyzed by small/wide-angle X-ray scattering

Polymer Bulletin volume 74, pages 721–736 (2017)Cite this article

Abstract

The ultrahigh molecular weight polyethylene (UHMWPE) fibers were obtained directly from the industrial production line. Two-step industrial hot-drawing-to-specific-drawing ratios were carried out at the temperature of 120 and 130 °C, respectively. Small-angle X-ray scattering (SAXS) measurements using synchrotron radiation were applied to study the evolution of kebab structure and the formation of shish structure. The slight increase of long period and the rapid decrease of lateral sizes indicated the destruction of original lamellae which was accomplished by chain slip resulted in the orientation of lamellae to form shish structure. The decrease of average shish length was explained that the formed new shish structure had shorter shish length than the original shish at the early stage with the high concentration of spinning solution. Wide-angle X-ray diffraction (WAXD) measurements were performed to explore the changes of the degree of orientation of the crystals. It was found that the elevated drawing temperature was benefited to the evolution of the orientational order. The DSC result confirmed the evolution of shish–kebab structure through the melting behavior.

This is a preview of subscription content, access via your institution.

Access options

Buy single article

Instant access to the full article PDF.

USD 39.95

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12

References

  1. Shen L, Peng M, Qiao F, JL Zhang (2008) Preparation of microporous ultra high molecular weight polyethylene (UHMWPE) by thermally induced phase separation of a UHMWPE/liquid paraffin mixture. Chin J Polym Sci 6:653–657

    Article  Google Scholar 

  2. Zwijnenburg A, Hutten PFV, Pennings AJ, Chanzy HD (1978) Longitudinal growth of polymer crystals from flowing solutions V.: structure and morphology of fibrillar polyethylene crystals. Colloid Polym Sci 256:729–740

    Article  CAS  Google Scholar 

  3. Hsieh YL, Hu XP (1997) Structural transformation of ultra-high modulus and molecular weight polyethylene fibers by high-temperature wide-angle X-ray diffraction. J Polym Sci, Part B: Polym Phys 35:623–630

    Article  CAS  Google Scholar 

  4. Smith P, Lemstra PJ (1980) Ultra-high-strength polyethylene filaments by solution spinning/drawing. J Mater Sci 15:505–514

    Article  CAS  Google Scholar 

  5. Smith P, Lemstra PJ, Pijpers JPL (1982) Tensile strength of highly oriented polyethylene. II. Effect of molecular weight distribution. J Polym Sci Polym Phys Edit 20:2229–2241

    Article  CAS  Google Scholar 

  6. Hearle JWS (2001) High-performance fibers. CRC Press, New York, p 62

    Book  Google Scholar 

  7. Peterlin A (1971) Molecular model of drawing polyethylene and polypropylene. J Mater Sci 6:490–508

    Article  CAS  Google Scholar 

  8. Gibson AG, Davies GR, Ward IM (1978) Dynamic mechanical-behavior and longitudinal crystal thickness measurements on ultrahigh modulus linear polyethylene—quantitative model for elastic-modulus. Polymer 19:683–693

    Article  CAS  Google Scholar 

  9. Steyaert I, Delplancke MP, Assche GV, Rahier H, Clerck KD (2013) Fast-scanning calorimetry of electrospun polyamide nanofibres: melting behaviour and crystal structure. Polymer 54:6809–6817

    Article  CAS  Google Scholar 

  10. Heeley EL, Gough T, Hughes DJ, Bras W, Rieger J, Ryan AJ (2013) Effect of processing parameters on the morphology development during extrusion of polyethylene tape: an in-line small-angle X-ray scattering (SAXS) study. Polymer 54:6580–6588

    Article  CAS  Google Scholar 

  11. Samon JM, Schultz JM, Hsiao BS, Seifert S, Stribeck N, Gurke I, Saw CC (1999) Structure development during the melt spinning of polyethylene and Poly(vinylidene fluoride) fibers by in situ synchrotron small- and wide-angle X-ray scattering techniques. Macromolecules 32:8121–8132

    Article  CAS  Google Scholar 

  12. Litvinov VM, Xu J, Melian C, Demco DE, Möller M, Simmelink J (2011) Morphology, chain dynamics, and domain sizes in highly drawn gel-spun ultrahigh molecular weight polyethylene fibers at the final stages of drawing by SAXS, WAXS, and 1H solid-state NMR. Macromolecules 44:9254–9266

    Article  CAS  Google Scholar 

  13. Krueger D, Yeh GSY (1972) Morphology of polyethylene microfibrils and “shish kebabs”. J Macromol Sci Part B Phys 6:431–450

    Article  CAS  Google Scholar 

  14. Ohta Y, Murase H, Hashimoto T (2010) Structural development of ultra-high strength polyethylene fibers: transformation from kebabs to shishs through hot-drawing process of gel-spun fibers. J Polym Sci Part B Polym Phys 48:1861–1872

    Article  CAS  Google Scholar 

  15. Perret R, Ruland W (1971) The evaluation of multiple X-ray small-angle scattering. J Appl Crystallogr 4:444–451

    Article  CAS  Google Scholar 

  16. Rathje J, Ruland W (1976) Density fluctuations in amorphous and semicrystalline polymers. Colloid Polym Sci 254:358–370

    Article  CAS  Google Scholar 

  17. Katayama K, Nakamura K, Amano T (1968) Structural formation during melt spinning process. Kolloid-Zeitschrift und Zeitschrift für Polymere 226:125–134

    Article  CAS  Google Scholar 

  18. Spruiell JE, White JL (2004) Structure development during polymer processing: studies of the melt spinning of polyethylene and polypropylene fibers. Polym Eng Sci 15:660–667

    Article  Google Scholar 

  19. Jing W, Schultz JM, Yeh F, Hsiao BS, Chu B (2000) In-situ simultaneous synchrotron small- and wide-angle X-ray scattering measurement of poly(vinylidene fluoride) fibers under deformation. Macromolecules 33:1765–1777

    Article  Google Scholar 

  20. Samon JM, Schultz JM, Hsiao BS (2000) Study of the cold drawing of nylon 6 fiber by in situ simultaneous small- and wide-angle X-ray scattering techniques. Polymer 41:2169–2182

    Article  CAS  Google Scholar 

  21. Zhang J, Hu S, Rieger J, Roth SV, Gehrke R, Men Y (2008) Effect of annealing on the deformation mechanism of a styrene/n-butyl acrylate copolymer latex film investigated by synchrotron small-angle X-ray scattering. Macromolecules 41:4353–4357

    Article  CAS  Google Scholar 

  22. Jiang Z et al (2007) Structural evolution of tensile-deformed high-density polyethylene during annealing: scanning synchrotron small-angle X-ray scattering study. Macromolecules 40:7263–7269

    Article  CAS  Google Scholar 

  23. Zhang J, Hu S, Rieger J, Roth SV, Gehrke R, Men Y (2009) In situ observation of tensile deformation processes of soft colloidal crystalline latex fibers. Macromolecules 42:4795–4800

    Article  CAS  Google Scholar 

  24. Jiang Z et al (2010) Two lamellar to fibrillar transitions in the tensile deformation of high-density polyethylene. Macromolecules 43:4727–4732

    Article  CAS  Google Scholar 

  25. Aerle NAJMV, Braam AWM (1988) A structural study on solid state drawing of solution-crystallized ultra-high molecular weight polyethylene. J Mater Sci 23:4429–4436

    Article  Google Scholar 

  26. Hoogsteen W, Pennings AJ, Tenbrinke G (1990) SAXS experiments on gel-spun polyethylene fibers. Colloid Polym Sci 268:245–255

    Article  CAS  Google Scholar 

  27. Tian F et al (2015) Small angle X-ray scattering beamline at SSRF. Nucl Sci Tech 26:1–6

    Google Scholar 

  28. Hammersley AP, Svensson SO, Thompson A (1994) Calibration and correction of spatial distortions in 2D detector systems. Nucl Instrum Methods Phys Res 346:312–321

    Article  CAS  Google Scholar 

  29. Hammersley AP (1997) FIT2D: an introduction and overview. Solid State Ferment Bioreact 8:1–34

    Google Scholar 

  30. Murthy NS, Grubb DT (2006) Tilted lamellae in an affinely deformed 3D macrolattice and elliptical features in small-angle scattering. J Polym Sci Part B Polym Phys 44:1277–1286

    Article  CAS  Google Scholar 

  31. Popli R, Glotin M, Mandelkern L, Benson RS (1984) Dynamic mechanical studies of α and β relaxations of polyethylenes. J Polym Sci Polym Phys Ed 22:407–448

    Article  CAS  Google Scholar 

  32. Keum JK, Feng Z, Hsiao BS (2008) Formation and stability of shear-induced shish-kebab structure in highly entangled melts of UHMWPE/HDPE blends. Macromolecules 41:4766–4776

    Article  CAS  Google Scholar 

  33. Ruland W (1969) Small-angle scattering studies on carbonized cellulose fibers & dagger. J Polym Sci Part C Polym Symp 28:143–151

    Article  Google Scholar 

  34. Polanyi M (1921) The X-ray fiber diagram. Z Angew Phys 7:149–180

    CAS  Google Scholar 

  35. Hermans PH, Kratky O, Platzek P (1939) Die Netzstruktur von gequollener Hydratzellulose. Kolloid-Zeitschrift 86:245–254

    Article  CAS  Google Scholar 

  36. Wang YZ, Hsieh KH, Chen LW, Tseng HC (1994) Effect of compatibility on specific volume of molten polyblends. J Appl Polym Sci 53:1191–1201

    Article  CAS  Google Scholar 

  37. Pennings AJ, Zwijnenburg A (1979) Longitudinal growth of polymer crystals from flowing solutions. VI. Melting behavior of continuous fibrillar polyethylene crystals. J Polym Sci Polym Phys Ed 17:1011–1032

    Article  CAS  Google Scholar 

Download references

Acknowledgments

This work was supported by the National Science Foundation of China (51273210). The project was supported by the Open Research Fund of State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, and Chinese Academy of Sciences. Sponsored by K. C. Wong Magna Fund in Ningbo University. We thank Shanghai Synchrotron Radiation Facility (SSRF) for supporting the WAXD and SAXS tests.

Author information

Authors and Affiliations

  1. Ningbo Key Laboratory of Specialty Polymers, Faculty of Materials Science and Chemical Engineering, Ningbo University, Ningbo, 315211, People’s Republic of China

    Haojun Xu, Minfang An, You Lv, Li Zhang & Zongbao Wang

Authors
  1. Haojun Xu
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Minfang An
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. You Lv
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Li Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Zongbao Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding authors

Correspondence to Li Zhang or Zongbao Wang.

Rights and permissions

Reprints and Permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Xu, H., An, M., Lv, Y. et al. Structural development of gel-spinning UHMWPE fibers through industrial hot-drawing process analyzed by small/wide-angle X-ray scattering. Polym. Bull. 74, 721–736 (2017). https://doi.org/10.1007/s00289-016-1742-z

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00289-016-1742-z

Keywords

search

Navigation