Abstract
Poly(vinyl acetate-co-methyl methacrylate)/Cloisite 30B, P(VAc-co-MMA)/C30B nanocomposite have been prepared via emulsion polymerization method. In the nanocomposite latex preparation sodium lauryl sulfate, ammonium persulfate, and poly(vinyl alcohol) were as anionic emulsifier, conventional anionic initiator, and stabilizer, respectively. The resulting P(VAc-co-MMA)/C30B nanocomposites with various filler contents were characterized using elemental analysis, Fourier transform infrared spectroscopy, X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy (TEM), and atomic force microscopy. The effects of various C30B contents on the polymerization rate and monomer conversion of P(VAc-co-MMA)/C30B were studied. Thermal properties of the nanocomposite were studied by dynamic mechanical thermal analysis. The XRD and TEM results demonstrated that the synthesized polymer chains were aggregated into the C30B interlayer regions and consequently complete exfoliation was produced.
Similar content being viewed by others
References
Mohsen-Nia M, Mohammad douladi F (2011) Synthesis and characterization of poly vinyl acetate/montmorillonite nanocomposite by in situ emulsion polymerization technique. Polym Bull 66:1255–1265
Iji M, Morishita N, Kai H (2010) Self-assembling siloxane nanoparticles with three phases that increase tenacity of poly l-lactic acid. Polym J 43:101–107
Alvi F, Ram M, Gomez H, Joshi R, Kumar A (2010) Evaluating the chemio-physio properties of novel zinc oxide–polyaniline nanocomposite polymer films. Polym J 42:935–940
Mohsen-Nia M, Mohammad Doulabi F. PVAc microspheres via semicontinuous emulsion polymerization: synthesis, characterization, kinetic and surface morphology studies. J Adhesion (in press)
Araújo PH, Giudici R, Sayer C (2004) Butyl acrylate and vinyl acetate semicontinuous emulsion copolymerization: study of stabilization performance. Macromol Symp 206:179–190
Lazaridis N, Alexopoulos AH, Kiparissides C (2001) Semi-batch emulsion copolymerization of vinyl acetate and butyl acrylate using oligomeric nonionic surfactants. Macromol Chem Phys 202:2614–2619
Lee J, Hong C, Choe S, Shim S (2007) Synthesis of polystyrene/silica composite particles by soap-free emulsion polymerization using positively charged colloidal silica. J Colloid Interface Sci 310:112–120
Wang Y, Herron N (1992) Photoconductivity of CdS nanocluster-doped polymers. Chem Phys Lett 200:71–75
Sahoo PK, Samal R, Swain SK, Rana PK (2008) Synthesis of poly(butyl acrylate) sodium silicate nanocomposite filer retardant. Eur Polym J 44:3522–3528
Li Y, Liu L, Zhang W, Fang Y (2004) A new hybrid nanocomposite prepared by graft copolymerization of butyl acrylate onto chitosan in the presence of organophilic montmorillonite. Radiat Phys chem 69:467–472
Yildirim EH (2002) Vinyl acetate emulsion polymerization and copolymerization with acrylic monomers. CRC Press, Boca Raton
Hao L, Yunzhao Y, Yukun Y (2005) Synthesis of exfoliated polystyrene/montmorillonite nanocomposite by emulsion polymerization using zwitterions as the clay modifier. Eur Polym J 41:2016–2022
Shi Y, Peterson S, Sogah DY (2007) Surfactant-free method for the synthesis of poly(vinyl acetate) masterbatch nanocomposites as a route to ethylene vinyl acetate/silicate nanocomposites. Chem Mater 19:1552–1564
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Mohsen-Nia, M., Mohammad Doulabi, F.S. Preparation and characterization of exfoliated poly(vinyl acetate-co-methyl methacrylate)/Cloisite 30B nanocomposite. Polym. Bull. 68, 1663–1675 (2012). https://doi.org/10.1007/s00289-011-0665-y
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00289-011-0665-y